论文信息 - Ba doping and rapid cooling effects on coercivity of Bi‐Dy‐Al‐Fe garnet films for magneto‐optical recording prepared by pyrolysis

Ba doping and rapid cooling effects on coercivity of Bi‐Dy‐Al‐Fe garnet films for magneto‐optical recording prepared by pyrolysis

Al‐doped Bi‐Dy iron garnet films have been fabricated by the pyrolysis method on glass substrates, and the effects of Ba doping and rapid cooling on the coercivity (Hc) were investigated. Films were quenched from 660 °C to room temperature within about 120 s. Rapid cooling causes a rise of Hc, and a small amount of Ba doping enhances this effect. Hc values near 4200 Oe at room temperature were obtained in rapidly cooled films with the composition Bi1Dy1.96Ba0.04Fe4.4Al0.6O12.

Mark H. Kryder | Akiyoshi Itoh | M. Kryder | A. Itoh

[1] Akiyoshi Itoh,et al. Bi-substituted DyIG thin films prepared by thermal decomposition method for magneto-optic recording medium. , 1986 .

[2] Manabu Gomi,et al. Improvement in optical and magnetic properties of Bi‐substituted garnet sputtered films for magneto‐optical recording , 1988 .

[3] M. Abe,et al. RF-Sputtering of Highly Bi-Substituted Garnet Films on Glass Substrates for Magneto-Optic Memory , 1985, IEEE Translation Journal on Magnetics in Japan.

[4] W. W. Malinofsky,et al. Chemically Deposited Thin Ferrite Films , 1963 .

[5] Nagaaki Koshino,et al. Microstructure of sputtered garnet films for magneto‐optical recording media , 1988 .

[6] J. Nielsen,et al. Dependence of the Magnetic Properties of Y3Fe5−xGaxO12 and Y3Fe5−xAlxO12 on Thermal History , 1966 .

[7] S. Geller. Magnetic Interactions and Distribution of Ions in the Garnets , 1960 .