Triblock copolymer syntheses of mesoporous silica with periodic 50 to 300 angstrom pores

Use of amphiphilic triblock copolymers to direct the organization of polymerizing silica species has resulted in the preparation of well-ordered hexagonal mesoporous silica structures (SBA-15) with uniform pore sizes up to approximately 300 angstroms. The SBA-15 materials are synthesized in acidic media to produce highly ordered, two-dimensional hexagonal (space group p6mm) silica-block copolymer mesophases. Calcination at 500 degrees C gives porous structures with unusually large interlattice d spacings of 74.5 to 320 angstroms between the (100) planes, pore sizes from 46 to 300 angstroms, pore volume fractions up to 0.85, and silica wall thicknesses of 31 to 64 angstroms. SBA-15 can be readily prepared over a wide range of uniform pore sizes and pore wall thicknesses at low temperature (35 degrees to 80 degrees C), using a variety of poly(alkylene oxide) triblock copolymers and by the addition of cosolvent organic molecules. The block copolymer species can be recovered for reuse by solvent extraction with ethanol or removed by heating at 140 degrees C for 3 hours, in both cases, yielding a product that is thermally stable in boiling water.

[1]  Bradley F. Chmelka,et al.  Magnetic Field Alignment of Ordered Silicate-Surfactant Composites and Mesoporous Silica , 1997 .

[2]  S. Tolbert,et al.  Magnetic-Field-Induced Orientational Ordering of Alkaline Lyotropic Silicate−Surfactant Liquid Crystals , 1997 .

[3]  I. Aksay,et al.  Formation of a Silicate L3 Phase with Continuously Adjustable Pore Sizes , 1997 .

[4]  Markus Antonietti,et al.  Superstructures of Functional Colloids: Chemistry on the Nanometer Scale , 1997 .

[5]  A. Stein,et al.  Synthesis and characterization of a reactive vinyl-functionalized MCM-41: Probing the internal pore structure by a bromination reaction , 1997 .

[6]  A. G. Oertli,et al.  Alkaline Lyotropic Silicate−Surfactant Liquid Crystals , 1997 .

[7]  F. Bates,et al.  SELF-ASSEMBLY AND POLYMERIZATION OF EPOXY RESIN-AMPHIPHILIC BLOCK COPOLYMER NANOCOMPOSITES , 1997 .

[8]  E. Prouzet,et al.  Assembly of Mesoporous Molecular Sieves Containing Wormhole Motifs by a Nonionic Surfactant Pathway: Control of Pore Size by Synthesis Temperature† , 1997 .

[9]  A. Sayari.  Catalysis by Crystalline Mesoporous Molecular Sieves , 1996 .

[10]  Q. Huo,et al.  Surfactant Control of Phases in the Synthesis of Mesoporous Silica-Based Materials , 1996 .

[11]  Jackie Y. Ying,et al.  Synthesis of a Stable Hexagonally Packed Mesoporous Niobium Oxide Molecular Sieve Through a Novel Ligand‐Assisted Templating Mechanism , 1996 .

[12]  George S. Attard,et al.  Liquid-crystalline phases as templates for the synthesis of mesoporous silica , 1995, Nature.

[13]  Stephen A. Bagshaw,et al.  Templating of Mesoporous Molecular Sieves by Nonionic Polyethylene Oxide Surfactants , 1995, Science.

[14]  M. Matsen.  Phase Behavior of Block Copolymer/Homopolymer Blends , 1995 .

[15]  Q. Huo,et al.  Mesostructure Design with Gemini Surfactants: Supercage Formation in a Three-Dimensional Hexagonal Array , 1995, Science.

[16]  D. Akporiaye,et al.  Pore Size Determination of MCM-51 Mesoporous Materials by means of 1H NMR Spectroscopy, N2 adsorption, and HREM. A Preliminary Study , 1995 .

[17]  P. Tanev,et al.  A Neutral Templating Route to Mesoporous Molecular Sieves , 1995, Science.

[18]  H. Hoffmann,et al.  Phase Diagrams and Aggregation Behavior of Poly(oxyethylene)-Poly(oxypropylene)-Poly(oxyethylene) Triblock Copolymers in Aqueous Solutions , 1994 .

[19]  Pierre M. Petroff,et al.  Generalized synthesis of periodic surfactant/inorganic composite materials , 1994, Nature.

[20]  K. Sing,et al.  Physisorption of argon, nitrogen and oxygen by MCM-41, a model mesoporous adsorbent , 1994 .

[21]  J. B. Higgins,et al.  A new family of mesoporous molecular sieves prepared with liquid crystal templates , 1992 .

[22]  L. McCusker,et al.  A synthetic gallophosphate molecular sieve with a 20-tetrahedral-atom pore opening , 1991, Nature.