Quantitative analysis of the grain morphology in self-assembled hexagonal lattices.

We present a methodology for the analysis of the grain morphology of self-ordered hexagonal lattices and for the quantitative comparison of the quality of their grain ordering based on the distances between nearest neighbors and their angular order. Two approaches to grain identification and evaluation are introduced: (i) color coding the relative angular orientation of hexagons containing a central entity and its six nearest neighbors, and (ii) incorporating triangles comprising three nearest neighbors into grains or repelling them from grains based on deviations of the side lengths and the internal angles of the triangles from those of an ideal equilateral triangle. A spreading algorithm with tolerance parameters allows single grains to be identified, which can thus be ranked according to their size. Hence, grain size distributions are accessible. For the practical evaluation of micrographs displaying self-ordered structures, we suggest using the size of the largest identified grain as a quality measure. Quantitative analyses of grain morphologies are key to the systematic and rational optimization of the fabrication of self-assembled materials.

[1]  Kornelius Nielsch,et al.  Fast fabrication of long-range ordered porous alumina membranes by hard anodization , 2006, Nature materials.

[2]  Hideki Masuda,et al.  Self-Ordering of Cell Configuration of Anodic Porous Alumina with Large-Size Pores in Phosphoric Acid Solution , 1998 .

[3]  S. Shingubara,et al.  Self-Organization of a Porous Alumina Nanohole Array Using a Sulfuric/Oxalic Acid Mixture as Electrolyte , 2004 .

[4]  Christopher B. Murray,et al.  Synthesis and Characterization of Monodisperse Nanocrystals and Close-Packed Nanocrystal Assemblies , 2000 .

[5]  Kornelius Nielsch,et al.  Hexagonal pore arrays with a 50-420 nm interpore distance formed by self-organization in anodic alumina , 1998 .

[6]  Robert M. Metzger,et al.  On the Growth of Highly Ordered Pores in Anodized Aluminum Oxide , 1998 .

[7]  Kenji Fukuda,et al.  Ordered Metal Nanohole Arrays Made by a Two-Step Replication of Honeycomb Structures of Anodic Alumina , 1995, Science.

[8]  Meihua Lu,et al.  Preparation of porous materials with ordered hole structure. , 2006, Advances in colloid and interface science.

[9]  I. Hamley,et al.  Morphologies of block copolymer melts , 2004 .

[10]  Dong Ha Kim,et al.  Ordered arrays of <100>-oriented silicon nanorods by CMOS-compatible block copolymer lithography. , 2007, Nano letters.

[11]  Sachiko Ono,et al.  Self‐Ordering of Cell Arrangement of Anodic Porous Alumina Formed in Sulfuric Acid Solution. , 1997 .

[12]  G. Fredrickson,et al.  Block copolymer thermodynamics: theory and experiment. , 1990, Annual review of physical chemistry.

[13]  V. Abetz,et al.  Phase behaviour and morphologies of block copolymers , 2005 .

[14]  Reinald Hillebrand,et al.  Self-ordered anodic aluminum oxide formed by H2SO4 hard anodization. , 2008, ACS nano.

[15]  K. Wada,et al.  Fabrication of Ideally Ordered Nanoporous Alumina Films and Integrated Alumina Nanotubule Arrays by High‐Field Anodization , 2005 .

[16]  Cherie R. Kagan,et al.  Self-Organization of CdSe Nanocrystallites into Three-Dimensional Quantum Dot Superlattices , 1995, Science.

[17]  L. N. Pfeiffer,et al.  Preparation of Photonic Crystals Made of Air Spheres in Titania , 1998 .

[18]  Stefan Mátéfi-Tempfli,et al.  Characterization of nanopores ordering in anodic alumina , 2008 .