Touching the properties of NbTi by carbon doped tapes with mechanically alloyed MgB2

Combining mechanical alloying and powder-in-tube processing is a promising way to obtain tapes with excellent properties. Taking advantage of the properties of nanocrystalline precursor powders, it was possible to obtain Jc values of 104A∕cm2 at 12.1T and 4.2K. Evidential substitution of carbon into the MgB2 changed the electron scattering and therefore raised the Bc2 up to 12T at 10K. Systematic investigation on the influence of the heat treatment showed that, although an interfering Fe2B reaction layer was formed, an excellent Jc of 104A∕cm2 at 14.3T and 4.2K was achieved.

[1] J. Nagamatsu,et al. Superconductivity at 39 K in magnesium diboride , 2001, Nature.

[2] Improved critical current densities in B4C doped MgB2 based wires , 2006, cond-mat/0607073.

[3] Improved superconducting properties in nanocrystalline bulk MgB2 , 2001, cond-mat/0111585.

[4] R. Penco,et al. Development of ex situ processed MgB2 wires and their applications to magnets , 2007 .

[5] H. Sosiati,et al. MgB2 films with very high critical current densities due to strong grain boundary pinning , 2004 .

[6] H. Kitaguchi,et al. Fabrication and properties of powder-in-tube-processed MgB2 tape conductors , 2007 .

[7] M. Herrmann,et al. Reactive nanostructured carbon as an effective doping agent for MgB2 , 2007 .

[8] Pierre Villars,et al. Pearson's handbook of crystallographic data for intermetallic phases , 1985 .

[9] G. Seifert,et al. Modification of carbon nanostructures by high energy ball-milling under argon and hydrogen atmosphere , 2005 .

[10] S. Dou,et al. Strong pinning and high critical current density in carbon nanotube doped MgB2 , 2004 .

[11] S. Dou,et al. Enhancement of Hc2 and Jc by carbon-based chemical doping , 2007 .

[12] D. Larbalestier,et al. Development of high critical current densities in niobium 46.5 wt% titanium , 1987 .

[13] M. Herrmann,et al. MgB2 bulk and tapes prepared by mechanical alloying: influence of the boron precursor powder , 2006 .