Face/core debond fatigue crack growth characterization using the sandwich mixed mode bending specimen

Abstract Face/core fatigue crack growth in foam-cored sandwich composites is examined using the mixed mode bending (MMB) test method. The mixed mode loading at the debond crack tip is controlled by changing the load application point in the MMB test fixture. Sandwich specimens were manufactured using H45 and H100 PVC foam cores and E-glass/polyester face sheets. All specimens were pre-cracked in order to define a sharp crack front. The static debond fracture toughness for each material configuration was measured at different mode-mixity phase angles. Fatigue tests were performed at 80% of the static critical load, at load ratios of R  = 0.1 and 0.2. The crack length was determined during fatigue testing using the analytical compliance expression and verified by visual measurements. Fatigue crack growth results revealed higher crack growth rates for mode I dominated loading. For specimens with H45 core, the crack grew just below the face/core interface on the core side for all mode-mixities, whereas for specimens with H100 core, the crack propagated in the core or in the face laminate depending on the mode-mixity at the debond crack tip.

[1]  Bo Cerup Simonsen,et al.  Experimental and Numerical Study of Interface Crack Propagation in Foam-cored Sandwich Beams , 2007 .

[2]  Brian Hayman,et al.  Approaches to Damage Assessment and Damage Tolerance for FRP Sandwich Structures , 2007 .

[3]  Christian Berggreen,et al.  Face/core interface fracture characterization of mixed mode bending sandwich specimens , 2011 .

[4]  Christian Berggreen,et al.  Tailoring Sandwich Face/Core Interfaces for Improved Damage Tolerance—Part I: Finite Element Analysis , 2010 .

[5]  B. Shafiq,et al.  Fatigue characteristics of foam core sandwich composites , 2006 .

[6]  John W. Hutchinson,et al.  Decohesion of a cut prestressed film on a substrate , 1990 .

[7]  Leif A. Carlsson,et al.  Crack path in foam cored DCB sandwich fracture specimens , 2005 .

[8]  Leif A. Carlsson,et al.  Analysis of the sandwich DCB specimen for debond characterization , 2008 .

[9]  Christian Berggreen,et al.  Design Analysis of the Mixed Mode Bending Sandwich Specimen , 2010 .

[10]  George A. Kardomateas,et al.  Structural and Failure Mechanics of Sandwich Composites , 2011 .

[11]  D. Zenkert,et al.  Fatigue of Closed Cell Foams , 2006 .

[12]  Christian Berggreen,et al.  Tailoring Sandwich Face/Core Interfaces for Improved Damage Tolerance—Part II: Experiments , 2010 .

[13]  Z. Suo,et al.  Mixed mode cracking in layered materials , 1991 .

[14]  P. E. Irving,et al.  Comments on: “A correlation for fatigue crack growth rate” , 1977 .

[15]  B. Hayman,et al.  Materials Challenges in Present and Future Wind Energy , 2008 .

[16]  Shipsha,et al.  Interfacial fatigue crack growth in foam core sandwich structures , 1999 .

[17]  Christian Berggreen,et al.  On the analysis of a mixed mode bending sandwich specimen for debond fracture characterization , 2009 .

[18]  P. C. Paris,et al.  A Critical Analysis of Crack Propagation Laws , 1963 .

[19]  John H. Crews,et al.  The mixed-mode bending method for delamination testing , 1989 .

[20]  Ole Thybo Thomsen,et al.  Determination of mechanical properties of PVC foam using a modified Arcan fixture , 2012 .

[21]  Jr. J. Crews,et al.  Mixed-Mode Bending Method for Delamination Testing , 1990 .

[22]  Leif A. Carlsson,et al.  Characterization of Face Sheet/Core Shear Fracture of Composite Sandwich Beams , 1991 .