La2O3 Doped Y2O3 Stabilized ZrO2 TBC Prepared by EB-PVD

Effect of La2O3 addition on thermal conductivity and high temperature stability of YSZ coating produced by EB-PVD was investigated. La2O3 was selected as an additive because it had a significant effect on suppressing densification of YSZ. The developed coating showed extremely low thermal conductivity as well as high resistance to sintering. Microstructural observation revealed that the coating had fine feather-like subcolumns and nanopores, which contributed to limit thermal transport. These nanostructures were thought to be formed by suppressing densification during deposition.

N. Yamaguchi | H. Matsubara | M. Matsumoto

[1] C. Leyens,et al. Aspects on Sintering of EB‐PVD TBCs , 2007 .

[2] Y. Sugita,et al. Thermal conductivity and phase stability of plasma sprayed ZrO2–Y2O3–La2O3 coatings , 2005 .

[3] N. Yamaguchi,et al. Phase Stability and Thermal Cycle Life of ZrO2-Y2O3-La2O3 Coatings Produced by EB-PYD , 2005 .

[4] F. Tietz,et al. Thermal Stability of Lanthanum Zirconate Plasma‐Sprayed Coating , 2004 .

[5] N. Yamaguchi,et al. Low thermal conductivity and high temperature stability of ZrO2–Y2O3–La2O3 coatings produced by electron beam PVD , 2004 .

[6] K. Lawson,et al. Methods to reduce the thermal conductivity of EB-PVD TBCs , 2002 .

[7] Tian Jian Lu,et al. Distributed Porosity as a Control Parameter for Oxide Thermal Barriers Made by Physical Vapor Deposition , 2001 .

[8] Haydn N. G. Wadley,et al. Low thermal conductivity vapor deposited zirconia microstructures , 2001 .

[9] Components for Engines,et al. Ceramic materials and components for engines , 2001 .

[10] U. Schulz,et al. Microstructure of ZrO2 Thermal Barrier Coatings Applied by EB-PVD , 2000 .