Comparative investigation of tungsten inert gas and friction stir welding characteristics of Al–Mg–Sc alloy plates

Abstract Al–Mg–Sc alloy plates were welded by FSW and TIG welding. The effect of welding processes on mechanical properties of Al–Mg–Sc welded joints was analyzed based on optical microscopy, transmission electron microscopy, tensile testing and Vickers microhardness measurements. The results show that the mechanical properties of FSW welded joint are much better than those of TIG welded joint; the strength coefficient of FSW joint is up to 94%. Moreover, tensile strength and yield strength of FSW joint are 19% and 31% higher than those of TIG joint, respectively, which are attributed to the preservation of cold working microstructures in the process of FSW. Due to the low welding temperature during FSW process and the excellent thermal stability of Al 3 (Sc, Zr) particles, the cold working microstructures can be well preserved. In addition, the FSW joint have asymmetric microstructures and mechanical properties, which are not observed in TIG welded joint.

[1]  Kuai-she Wang,et al.  Comparison of fatigue property between friction stir and TIG welds , 2008 .

[2]  E. Kaluç,et al.  Comparison between microstructure characteristics and joint performance of 5086-H32 aluminium alloy welded by MIG, TIG and friction stir welding processes , 2007 .

[3]  E. Taban,et al.  Microstructural and mechanical properties of double-sided MIG, TIG and friction stir welded 5083-H321 aluminium alloy , 2006 .

[4]  Hiroyuki Kokawa,et al.  Effect of microstructure on properties of friction stir welded Inconel Alloy 600 , 2008 .

[5]  M. N. James,et al.  Friction stir weld process evaluation by multi-axial transducer , 2008 .

[6]  Mats Ericsson,et al.  Influence of welding speed on the fatigue of friction stir welds, and comparison with MIG and TIG , 2003 .

[7]  W. Thomas,et al.  Friction stir welding for the transportation industries , 1997 .

[8]  Radovan Kovacevic,et al.  Finite element modeling of friction stir welding—thermal and thermomechanical analysis , 2003 .

[9]  Timotius Pasang,et al.  Shear flow and formation of Nugget zone during friction stir welding of aluminium alloy 5083-O , 2008 .

[10]  Xinqi Yang,et al.  Investigation of Microstructures and Fatigue Properties of Friction Stir Welded Al-Mg Alloy , 2006 .

[11]  Z. Ma,et al.  Microstructural evolution and mechanical properties of friction stir welded Mg–Zn–Y–Zr alloy , 2007 .

[12]  P.M.S.T. de Castro,et al.  Fatigue behaviour of FSW and MIG weldments for two aluminium alloys , 2007 .

[13]  A. Squillace,et al.  A comparison between FSW and TIG welding techniques: modifications of microstructure and pitting corrosion resistance in AA 2024-T3 butt joints , 2004 .

[14]  G. Odette,et al.  The microstructure and strength properties of MA957 nanostructured ferritic alloy joints produced by friction stir and electro-spark deposition welding , 2007 .

[15]  V. Balasubramanian,et al.  Influences of tool pin profile and tool shoulder diameter on the formation of friction stir processing zone in AA6061 aluminium alloy , 2008 .

[16]  Yuang-Cherng Chiou,et al.  Experimental study on temperature distributions within the workpiece during friction stir welding of aluminum alloys , 2008 .

[17]  V. Balasubramanian,et al.  Influences of post-weld heat treatment on tensile properties of friction stir-welded AA6061 aluminum alloy joints , 2008 .

[18]  Surendar Marya,et al.  Comparison of TIG welded and friction stir welded Al–4.5Mg–0.26Sc alloy , 2008 .

[19]  Hongwu Zhang,et al.  Numerical studies on controlling of process parameters in friction stir welding , 2009 .