Characterization of chemical bath deposited CdS thin films at different deposition temperature

Abstract CdS thin films were deposited onto glass substrates by the chemical bath deposition (CBD). The influence of the deposition temperature varied from 55 °C to 85 °C in a step of 5 °C on the crystallographic structure, morphology as well as optical and electrical properties was investigated in detail. Increasing deposition temperature can promote phase transformation from cubic to hexagonal and improvement of crystallinity in CdS films. CdS film deposited at 75 °C shows compact and smooth surface, and excellent transmission in visible light range. The band gaps are found to decrease from 2.56 eV to 2.38 eV with the increase of deposition temperature, and the sub-band gap of about 2.32 eV is noticed at low deposition temperature of 55–70 °C. All CdS films are of n-type conductivity and the carrier concentration is in the order of 10 12 –10 13  cm −3 . The lowest resistivity and highest mobility obtained are in the case of 85 °C.

[1]  T. Coutts.  High efficiency solar cells with CdS window layers , 1982 .

[2]  I. Repins,et al.  19·9%‐efficient ZnO/CdS/CuInGaSe2 solar cell with 81·2% fill factor , 2008 .

[3]  K. Ramaiah,et al.  The effect of sulfur concentration on the properties of chemical bath deposited CdS thin films , 2000 .

[4]  F. D. Auret,et al.  Microstructures of electrodeposited CdS layers , 2003 .

[5]  Zhou Zhibin,et al.  Influence of growth process on the structural, optical and electrical properties of CBD-CdS films , 2005 .

[6]  Rommel Noufi,et al.  Optimization of CBD CdS process in high-efficiency Cu(In, Ga)Se2-based solar cells , 2002 .

[7]  J. Dongre,et al.  Synthesis of flower-like CdS nanostructured films and their application in photoelectrochemical solar cells , 2009 .

[8]  N. Browning,et al.  SIMS and XPS characterization of CdS/CdTe heterostructures grown by MBE , 2000 .

[9]  A. Oliva,et al.  Effect of indium tin oxide substrate roughness on the morphology, structural and optical properties of CdS thin films , 2000 .

[10]  J. Herrero,et al.  Chemical Bath Deposition of CdS Thin Films: An Approach to the Chemical Mechanism Through Study of the Film Microstructure , 1997 .

[11]  P. O’Brien,et al.  Developing an understanding of the processes controlling the chemical bath deposition of ZnS and CdS , 1998 .

[12]  W. Jaegermann,et al.  Band alignment of differently treated TCO/CdS interface , 2009 .

[13]  Lu,et al.  Zinc-blende-wurtzite polytypism in semiconductors. , 1992, Physical review. B, Condensed matter.

[14]  Ramphal Sharma,et al.  Growth, structural and optical properties of Cd1−xZnxS alloy thin films grown by solution growth technique (SGT) , 2007 .

[15]  J. J. Alvarado-Gil,et al.  Influence of thermal annealings in different atmospheres on the band‐gap shift and resistivity of CdS thin films , 1995 .

[16]  O. Zelaya-Ángel,et al.  Modification of the properties of chemically deposited CdS thin films grown under magnetic field and variable growing parameters , 2001 .

[17]  O. Vigil-Galan,et al.  CdTe solar cell degradation studies with the use of CdS as the window material , 2009 .

[18]  Isaiah O. Oladeji,et al.  Characterization of CdS thin films grown by chemical bath deposition using four different cadmium sources , 2008 .

[19]  G. Contreras-Puente,et al.  Physical properties of chemical bath deposited CdS thin films , 2004 .

[20]  Xuanzhi Wu,et al.  High-efficiency polycrystalline CdTe thin-film solar cells , 2004 .

[21]  O. Zelaya-Ángel,et al.  Sphalerite-wurtzite phase transformation in CdS , 2000 .

[22]  D. Hariskos,et al.  Buffer layers in Cu(In,Ga)Se2 solar cells and modules , 2005 .

[23]  I. Oladeji,et al.  Optimization of chemical bath deposited CdS thin films using nitrilotriacetic acid as a complexing agent , 2008 .

[24]  Jae-Hyeong Lee,et al.  Comparative studies of the properties of CdS films deposited on different substrates by R.F. sputtering , 2006 .

[25]  F. Yakuphanoglu,et al.  The effects of substrate temperature on refractive index dispersion and optical constants of CdZn(S0.8Se0.2)2 alloy thin films , 2009 .

[26]  G. Sasikala,et al.  Modification in the chemical bath deposition apparatus, growth and characterization of CdS semiconducting thin films for photovoltaic applications , 2000 .

[27]  Vincent Barrioz,et al.  Towards ultra-thin CdTe solar cells using MOCVD , 2009 .

[28]  P. S. Reddy,et al.  Synthesis and dc magnetic susceptibility of the diluted magnetic semiconducting Cd1−xMnxS nanocrystalline films , 2008 .

[29]  A. Morales-Acevedo,et al.  Properties of CdS thin films chemically deposited in the presence of a magnetic field , 1998 .

[30]  M. Saglam,et al.  Effects of thermal annealing on electrical characteristics of Cd/CdS/n-Si/Au―Sb sandwich structure , 2009 .

[31]  K. Ramaiah,et al.  Structural and optical investigations on CdS thin films grown by chemical bath technique , 2001 .

[32]  N. Kohara,et al.  Chemical bath deposition of Cds buffer layer for GIGS solar cells , 1998 .

[33]  P. Ramasamy,et al.  Influence of ultrsonification in CdS thin film deposition in PCD technique , 2005 .

[34]  C. Lokhande,et al.  Chemical deposition method for metal chalcogenide thin films , 2000 .

[35]  N. Huang,et al.  Study on electrical properties of CdS films prepared by chemical pyrolysis deposition , 2004 .

[36]  Jae-Hyeong Lee.  Influence of substrates on the structural and optical properties of chemically deposited CdS films , 2007 .

[37]  Sa. K. Narayandass,et al.  Structural and optical properties of CdS thin films , 2001 .