Effects of the Quenching Rate on the Microstructure, Mechanical Properties and Paint Bake-Hardening Response of Al–Mg–Si Automotive Sheets

The quenching rate of Al–Mg–Si alloys during solution treatment is an important parameter for the automotive industry. In this work, the effect of the different quenching rates on the microstructures, mechanical properties, and paint bake-hardening response of Al–Mg–Si sheets was studied. Large dimples form on the fracture surface of a sample at a quenching rate of 0.01 °C/s. When the quenching rate increased to 58.9 °C/s, the dimples became smaller. The recrystallized grains and textures were slightly affected by quenching rates beyond 1.9 °C/s. Thus, higher r values of the samples were achieved with slower quenching rates. Furthermore, only the Al(FeMn)SiCr insoluble phases were observed in samples with a rapid quenching rate. Sufficient solute atoms and vacancies resulted in the improvement of the precipitation kinetics and paint bake-hardening capacity for Al–Mg–Si sheets at rapid rates. With a decrease in the quenching rate, the formation of the rod-like coarse β′ phases consumed many solute atoms and vacancies, leading to the deterioration of the paint bake-hardening capacity. This study provides a critical reference on quenching rates for industrial practices, so that good mechanical properties can be achieved using precision control of the quenching process.

[1]  N. Parson,et al.  Effects of Mn addition and related Mn-containing dispersoids on the hot deformation behavior of 6082 aluminum alloys , 2019, Materials Science and Engineering: A.

[2]  G. Renou,et al.  Correlation between quenching rate, mechanical properties and microstructure in thick sections of Al Mg Si( Cu) alloys , 2019, Materials Science and Engineering: A.

[3]  E. Lavernia,et al.  Influence of aging pathways on the evolution of heterogeneous solute-rich features in peak-aged Al-Mg-Si-Cu alloy with a high Mg/Si ratio , 2019, Philosophical Magazine Letters.

[4]  Guoqun Zhao,et al.  Investigation of dynamic recrystallization and modeling of microstructure evolution of an Al-Mg-Si aluminum alloy during high-temperature deformation , 2019, Journal of Alloys and Compounds.

[5]  Shang Zhu,et al.  Effects of Zn addition on the age hardening behavior and precipitation evolution of an Al-Mg-Si-Cu alloy , 2018, Materials Characterization.

[6]  Bin-hao Hu,et al.  Analyzing the microstructural evolution and hardening response of an Al-Si-Mg casting alloy with Cr addition , 2018, Materials Characterization.

[7]  Z. Fan,et al.  Influence of quenching rate and aging on bendability of AA6016 sheet , 2018, Materials Science and Engineering: A.

[8]  Hui Li,et al.  Bake hardening behavior and precipitation kinetic of a novel Al-Mg-Si-Cu aluminum alloy for lightweight automotive body , 2018, Materials Science and Engineering: A.

[9]  Yufeng Zheng,et al.  Grain growth and recrystallization behaviors of an ultrafine grained Al-0.6 wt%Mg-0.4 wt%Si-5vol.%SiC nanocomposite during heat treatment and extrusion , 2018 .

[10]  T. Zhai,et al.  Precipitation strengthening mechanisms during natural ageing and subsequent artificial aging in an Al-Mg-Si-Cu alloy , 2018 .

[11]  R. Misra,et al.  Influence of different solution methods on microstructure, precipitation behavior and mechanical properties of Al–Mg–Si alloy , 2018 .

[12]  Q. Liu,et al.  The structural and compositional evolution of precipitates in Al-Mg-Si-Cu alloy , 2018 .

[13]  S. Qiu,et al.  Intergranular crack during fatigue in Al-Mg-Si aluminum alloy thin extrusions , 2017 .

[14]  Yu Ye,et al.  Effects of various Mg/Si ratios on microstructure and performance property of Al-Mg-Si alloy cables , 2016 .

[15]  Talita A. Vida,et al.  Cellular/dendritic arrays and intermetallic phases affecting corrosion and mechanical resistances of an Al-Mg-Si alloy , 2016 .

[16]  L. Zhuang,et al.  The dependence of microstructure, texture evolution and mechanical properties of Al–Mg–Si–Cu alloy sheet on final cold rolling deformation , 2016 .

[17]  N. Provatas,et al.  Cluster evolution mechanisms during aging in Al–Mg–Si alloys , 2016 .

[18]  Qing Liu,et al.  Optimization of the pre-aging treatment for an AA6022 alloy at various temperatures and holding times , 2015 .

[19]  Chunhui Liu,et al.  The influence of Mg/Si ratio on the negative natural aging effect in Al–Mg–Si–Cu alloys , 2015 .

[20]  L. Zhuang,et al.  Enhanced bake-hardening response of an Al–Mg–Si–Cu alloy with Zn addition , 2015 .

[21]  Tatsuo Sato,et al.  Formation and reversion of clusters during natural aging and subsequent artificial aging in an Al–Mg–Si alloy , 2015 .

[22]  L. Zhuang,et al.  Effect of heating rate on mechanical property, microstructure and texture evolution of Al–Mg–Si–Cu alloy during solution treatment , 2015 .

[23]  Jia-quan Zhang,et al.  The effect of Zn on the age hardening response in an Al–Mg–Si alloy , 2015 .

[24]  P. Uggowitzer,et al.  Property Criteria for Automotive Al-Mg-Si Sheet Alloys , 2014, Materials.

[25]  J. Hirsch,et al.  Superior light metals by texture engineering: Optimized aluminum and magnesium alloys for automotive applications , 2013 .

[26]  P. Uggowitzer,et al.  Mechanisms controlling the artificial aging of Al-Mg-Si Alloys , 2011 .

[27]  Qian Zhang,et al.  The diffraction patterns from β″ precipitates in 12 orientations in Al–Mg–Si alloy , 2010 .

[28]  Tatsuo Sato,et al.  Three-Dimensional Atom Probe Characterization of Nanoclusters Responsible for Multistep Aging Behavior of an Al-Mg-Si Alloy , 2008 .

[29]  H. Zandbergen,et al.  The structural relation between precipitates in Al-Mg-Si alloys, the Al-matrix and diamond silicon, with emphasis on the trigonal phase U1-MgAl2Si2 , 2007 .

[30]  M. Karlík,et al.  The interaction of natural ageing with straining in a twin-roll cast AlMgSi automotive sheet , 2006 .

[31]  Xiang Wang,et al.  The sequence of precipitation in the Al-Mg-Si-Cu alloy AA6111 , 2006 .

[32]  M. V. van Huis,et al.  Atomic Pillar-Based Nanoprecipitates Strengthen AlMgSi Alloys , 2006, Science.

[33]  R. Holmestad,et al.  Post-β″ phases and their influence on microstructure and hardness in 6xxx Al-Mg-Si alloys , 2006 .

[34]  Y. Birol Pre-straining to improve the bake hardening response of a twin-roll cast Al¿Mg¿Si alloy , 2005 .

[35]  Y. Birol Pre-aging to improve bake hardening in a twin-roll cast Al–Mg–Si alloy , 2005 .

[36]  Olaf Engler,et al.  Texture control by thermomechanical processing of AA6xxx Al–Mg–Si sheet alloys for automotive applications—a review , 2002 .

[37]  W. S. Miller,et al.  Recent development in aluminium alloys for the automotive industry , 2000 .

[38]  M. Takeda,et al.  Stability of metastable phases and microstructures in the ageing process of Al–Mg–Si ternary alloys , 1998 .

[39]  H. Zandbergen,et al.  The crystal structure of the ? phase in AlMgSi alloys , 1998 .

[40]  H. W. Zandbergen,et al.  Structure Determination of Mg5Si6 Particles in Al by Dynamic Electron Diffraction Studies , 1997 .

[41]  H. Ko,et al.  Texture and plastic anisotropy of Al-Mg-0.3Cu-1.0Zn alloys , 1997 .