Erosion of thermal barrier coatings

Abstract Thermal barrier coatings have been used within gas turbines for over 30 years to extend the life of hot section components. Thermally sprayed ceramics were the first to be introduced and are widely used to coat combustor cans, ductwork, platforms and more recently turbine aerofoils of large industrial engines. The alternative technology, electron beam physical vapour deposition,(EB-PVD) has a more strain-tolerant columnar microstructure and is the only process that can offer satisfactory levels of spall resistance, erosion resistance and surface finish retention for aero-derivative engines. Whatever technology is used, the thermal barrier must remain intact throughout the turbine life. Erosion may lead to progressive loss of TBC thickness during operation, raising the metal surface temperatures and thus shortening component life. Ballistic damage can lead to total TBC removal. This paper reviews the erosion behaviour of both thermally sprayed and EB-PVD TBCs relating the observed behaviour to the coating microstructure. A model for the erosion of EB-PVD ceramics is presented that permits the prediction of erosion rates. The model has been validated using a high velocity erosion gas gun rig, both on test coupons and samples removed from coated components. The implications of erosion on component life are discussed in the light of experimental results and the model predictions.

[1]  J. Fackrell.  Aerodynamic effects on PFBC erosion target experiments , 1989 .

[2]  J. Nicholls,et al.  Erosion of EB-PVD thermal barrier coatings , 1998 .

[3]  Robert A. Miller,et al.  Current status of thermal barrier coatings — An overview , 1987 .

[4]  T. Cosack,et al.  Thermal Barrier Coatings on Turbine Blades by Plasma Spraying With Improved Cooling , 1992 .

[5]  J. Nicholls,et al.  Erosion and Foreign Object Damage of Thermal Barrier Coatings , 1997 .

[6]  J. Nicholls,et al.  Modelling the influence of surface oxidation on high temperature erosion , 1995 .

[7]  R. Handschuh.  High-temperature erosion of plasma-sprayed, yttria-stabilized zirconia in a simulated turbine environment , 1985 .

[8]  A. Levy,et al.  EROSION OF CERAMIC THERMAL BARRIER COATINGS , 1986 .

[9]  S. K. Gupta,et al.  Flight service evaluation of thermal barrier coatings by physical vapor deposition at 5200 H , 1989 .

[10]  J. Nicholls,et al.  A Mechanism for the Erosion of EB PVD TBCS , 2001 .

[11]  R. C. Novak,et al.  Particulate erosion of plasma-sprayed porous ceramic , 1987 .

[12]  M. Dorfman,et al.  Advanced thermal barrier coating systems , 1987 .

[13]  D. K. Gupta,et al.  The Evolution of Thermal Barrier Coatings in Gas Turbine Engine Applications , 1992 .

[14]  D. Stephenson,et al.  High temperature erosion of coated superalloys for gas turbines , 1987 .

[15]  J. Nicholls,et al.  Some observations on erosion mechanisms of EB PVD tbcs , 2000 .

[16]  T. A. Cruse,et al.  Thermal Barrier Coating Life Prediction Model Development , 1988 .

[17]  T. Rhys-Jones,et al.  Thermal barrier coatings for turbine applications in aero engines , 1989 .

[18]  J. Nicholls.  Laboratory studies of erosion-corrosion processes under oxidising and oxidising/sulphidising conditions , 1997 .

[19]  P. J. Slikkerveer.  Mechanical etching of glass by powder blasting , 1999 .

[20]  F. Soechting.  A design perspective on thermal barrier coatings , 1999 .

[21]  A. Evans,et al.  A model for crack initiation in elastic/plastic indentation fields , 1977 .

[22]  B. Beacher,et al.  Investigation of gas particle flow in an erosion wind tunnel , 1983 .

[23]  Robert Michael Orenstein,et al.  TBC experience in land- based gas turbines , 1997 .

[24]  W. Tabakoff.  Investigation of coatings at high temperature for use in turbomachinery , 1989 .

[25]  Widen Tabakoff,et al.  Dynamic Behavior of Solid Particles Suspended by Polluted Flow in a Turbine Stage , 1973 .