论文信息 - Evaluation of hydrogen embrittlement susceptibility of temper embrittled 2.25Cr–1Mo steel by SSRT method - 字舞流文

Evaluation of hydrogen embrittlement susceptibility of temper embrittled 2.25Cr–1Mo steel by SSRT method

Yan Sun | Hong Xu | Li Hua | Y. Dai | Xiang-ming Xia

[1] Y. Shindo,et al. Evaluation of hydrogen embrittlement and temper embrittlement by key curve method in instrumented Charpy test , 2010 .

[2] J. Tartaglia,et al. A Comparison of Mechanical Properties and Hydrogen Embrittlement Resistance of Austempered vs Quenched and Tempered 4340 Steel , 2008 .

[3] M. Islam. Grain Boundary Segregation Behavior in 2.25Cr-1Mo Steel During Reversible Temper Embrittlement , 2007, Journal of materials engineering and performance (Print).

[4] Qiong-qi Wang,et al. Experimental study of temper embrittlement of aged specimens removed from a hydrogenation reactor , 2006 .

[5] Li Li,et al. Temper embrittlement dynamics induced by non-equilibrium segregation of phosphorus in steel 12Cr1MoV , 2005 .

[6] Shuvra Das,et al. Practical numerical analysis of a crack near a weld subjected to primary loading and hydrogen embrittlement , 2006 .

[7] Noam Eliaz,et al. Characteristics of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels , 2002 .