Surface Roughness and Residual Stresses on the Fatigue Life of Shot Peened Components: Theoretical Determination

The effects of the shot peening process on the fatigue damage are analysed and modelled. Surface roughness is modelled in a way that would increase the far-fi eld stress. Compressive residual stresses translated as closure stresses which tend to reduce the application of the far-fi eld stress by introducing this closure stress on the crack fl anks and thus the propagation of the crack is ex- pected to be somewhat reduced compared to the unpeened condition. Resumen Se analizaron y modelaron matematicamente los efectos del proceso de granallado que tienen en el dano por fatiga de mate- riales metalicos policristalinos. La rugosidad superfi cial se modelo de tal forma que incrementa el esfuerzo aplicado. Los esfuerzos residuales compresivos se convirtieron en esfuerzos de cerradura los cuales tienden a contrarrestar el esfuerzo aplicado dado que el esfuerzo de cerradura actua en las caras de la grieta reduciendo la velocidad de propagacion en comparacion con aquellos componentes sin la aplicacion del granallado.