University of Groningen Rough Electrode Creates Excess Capacitance in Thin-Film Capacitors

The parallel-plate capacitor equation is widely used in contemporary material research for nanoscale applications and nanoelectronics. To apply this equation, flat and smooth electrodes are assumed for a capacitor. This essential assumption is often violated for thin-film capacitors because the formation of nanoscale roughness at the electrode interface is very probable for thin films grown via common deposition methods. In this work, we experimentally and theoretically show that the electrical capacitance of thin-film capacitors with realistic interface roughness is significantly larger than the value predicted by the parallel-plate capacitor equation. The degree of the deviation depends on the strength of the roughness, which is described by three roughness parameters for a self-affine fractal surface. By applying an extended parallelplate capacitor equation that includes the roughness parameters of the electrode, we are able to calculate the excess capacitance of the electrode with weak roughness. Moreover, we introduce the roughness parameter limits for which the simple parallel-plate capacitor equation is sufficiently accurate for capacitors with one rough electrode. Our results imply that the interface roughness beyond the proposed limits cannot be dismissed unless the independence of the capacitance from the interface roughness is experimentally demonstrated. The practical protocols suggested in our work for the reliable use of the parallel-plate capacitor equation can be applied as general guidelines in various fields of interest.

[1]  Yang Shen,et al.  Polymer-Based Dielectrics with High Energy Storage Density , 2015 .

[2]  F. Cacialli,et al.  Low-Temperature Photoluminescence Spectroscopy of Solvent-Free PCBM Single-Crystals , 2015 .

[3]  G. Jafari,et al.  Surface coupling effects on the capacitance of thin insulating films , 2015, 1505.00751.

[4]  Jian Li,et al.  Smart sensing skin for detection and localization of fatigue cracks , 2015 .

[5]  J. Hummelen,et al.  Strategy for Enhancing the Dielectric Constant of Organic Semiconductors Without Sacrificing Charge Carrier Mobility and Solubility , 2015 .

[6]  Xinran Wang,et al.  Large [6,6]-phenyl C61 butyric acid methyl (PCBM) hexagonal crystals grown by solvent-vapor annealing , 2014 .

[7]  D. Carroll,et al.  Solution‐Processed Highly Efficient Alternating Current‐Driven Field‐Induced Polymer Electroluminescent Devices Employing High‐k Relaxor Ferroelectric Polymer Dielectric , 2014 .

[8]  M. Premaratne,et al.  On the validity of unintentional doping densities extracted using Mott–Schottky analysis for thin film organic devices , 2013 .

[9]  M. Loi,et al.  High Performance Ambipolar Field‐Effect Transistor of Random Network Carbon Nanotubes , 2012, Advanced materials.

[10]  Sean E. Shaheen,et al.  Pathways to a New Efficiency Regime for Organic Solar Cells , 2012 .

[11]  Todd A. Gisby,et al.  Multi-functional dielectric elastomer artificial muscles for soft and smart machines , 2012 .

[12]  Matteo Aureli,et al.  A physics-based model of the electrical impedance of ionic polymer metal composites , 2012 .

[13]  Thomas Kirchartz,et al.  Sensitivity of the Mott–Schottky Analysis in Organic Solar Cells , 2012 .

[14]  Q. Pei,et al.  Advances in dielectric elastomers for actuators and artificial muscles. , 2010, Macromolecular rapid communications.

[15]  Y. Shin,et al.  Interface roughness effect between gate oxide and metal gate on dielectric property , 2009 .

[16]  Matteo Aureli,et al.  On the capacitance-boost of ionic polymer metal composites due to electroless plating: Theory and experiments , 2009 .

[17]  Yong Wang,et al.  High field tunneling as a limiting factor of maximum energy density in dielectric energy storage capacitors , 2008 .

[18]  Barbara Stadlober,et al.  Low‐Voltage Organic Thin‐Film Transistors with High‐k Nanocomposite Gate Dielectrics for Flexible Electronics and Optothermal Sensors , 2007 .

[19]  Yi Jia,et al.  Design and characterization of a passive wireless strain sensor , 2006 .

[20]  Thierry Lebey,et al.  Impact of the surface roughness on the electrical capacitance , 2006, Microelectron. J..

[21]  O. Wunnicke.  Gate capacitance of back-gated nanowire field-effect transistors , 2006, cond-mat/0607379.

[22]  Ching-Ping Wong,et al.  Synthesis and dielectric properties of novel high-K polymer composites containing in-situ formed silver nanoparticles for embedded capacitor applications , 2006 .

[23]  G. Palasantzas.  Self-affine roughness influence on the pull-in voltage in capacitive electromechanical devices , 2005 .

[24]  S. Bauer,et al.  High-mobility pentacene organic field-effect transistors with a high-dielectric-constant fluorinated polymer film gate dielectric , 2005 .

[25]  Yang Yang,et al.  Organic thin-film transistors with nanocomposite dielectric gate insulator , 2004 .

[26]  Jack B. Howard,et al.  Size analysis of single fullerene molecules by electron microscopy , 2004 .

[27]  Jacob K. White,et al.  A stochastic integral equation method for modeling the rough surface effect on interconnect capacitance , 2004, IEEE/ACM International Conference on Computer Aided Design, 2004. ICCAD-2004..

[28]  E. J. Rymaszewski,et al.  Thin-film capacitors for packaged electronics , 2003 .

[29]  Xiangfeng Duan,et al.  High-performance thin-film transistors using semiconductor nanowires and nanoribbons , 2003, Nature.

[30]  W. Euler,et al.  Determination of the crystalline phases of poly(vinylidene fluoride) under different preparation conditions using differential scanning calorimetry and infrared spectroscopy , 2003 .

[31]  Mark S. Lundstrom,et al.  High-κ dielectrics for advanced carbon-nanotube transistors and logic gates , 2002 .

[32]  Rajendra Patrikar,et al.  Modelling interconnects with surface roughness , 2002 .

[33]  F. Xia,et al.  An all-organic composite actuator material with a high dielectric constant , 2002, Nature.

[34]  P. Kohl,et al.  Novel polymer–ceramic nanocomposite based on high dielectric constant epoxy formula for embedded capacitor application , 2002 .

[35]  G. Palasantzas,et al.  The effect of mound roughness on the electrical capacitance of a thin insulating film , 2001 .

[36]  Jon-Paul Maria,et al.  Alternative dielectrics to silicon dioxide for memory and logic devices , 2000, Nature.

[37]  Toh-Ming Lu,et al.  Surface-roughness effect on capacitance and leakage current of an insulating film , 1999 .

[38]  Zhang,et al.  Giant electrostriction and relaxor ferroelectric behavior in electron-irradiated poly(vinylidene fluoride-trifluoroethylene) copolymer , 1998, Science.

[39]  Pinnaduwa Kulatilake,et al.  Requirements for accurate quantification of self affine roughness using the roughness-length method , 1997 .

[40]  J. J. Krajewski,et al.  Enhancement of the dielectric constant of Ta2O5through substitution with TiO2 , 1995, Nature.

[41]  P. Meakin.  The growth of rough surfaces and interfaces , 1993 .

[42]  Palasantzas.  Roughness spectrum and surface width of self-affine fractal surfaces via the K-correlation model. , 1993, Physical review. B, Condensed matter.

[43]  H. Kumar Wickramasinghe,et al.  High‐resolution capacitance measurement and potentiometry by force microscopy , 1988 .

[44]  T. Furukawa,et al.  Investigation of Switching Characteristics of Vinylidene Fluoride/Trifluoroethylene Copolymers in Relation to Their Structures , 1987 .

[45]  A. J. Lovinger.  Ferroelectric Polymers , 1983, Science.

[46]  J. Fontanella,et al.  Accurate Determination of the Dielectric Constant by the Method of Substitution , 1970 .