Effect of mendable polymer stitch density on the toughening and healing of delamination cracks in Carbon-epoxy laminates

This paper presents an investigation into the effect of stitch density on the delamination toughening and self-healing properties of carbon–epoxy laminates. The stitches provide the laminate with the synergistic combination of high mode I interlaminar fracture toughness to resist delamination cracking and healing properties to repair delamination damage. The results show that the fracture toughness of the laminate increased with stitch density, due to higher traction (crack closure) loads exerted by the stitches bridging the delamination. During the healing process these bridging stitches first melt and then flow into the delamination, leading to self-healing with full restoration of the mode I fracture toughness. Furthermore, the stitches were capable of repairing delamination cracks many times larger than the original size of the stitches. The effect of stitch density on the healing process of delamination cracks and restoration of fracture toughness was found to remain approximately the same under multiple repair operations.

[1]  Simon A. Hayes,et al.  A self-healing thermosetting composite material , 2007 .

[2]  Chun H. Wang,et al.  Self-healing of delamination cracks in mendable epoxy matrix laminates using poly[ethylene-co-(methacrylic acid)] thermoplastic , 2012 .

[3]  F. Wudl,et al.  Towards Development of a Self-Healing Composite using a Mendable Polymer and Resistive Heating , 2008 .

[4]  S. Furman,et al.  Poly[ethylene-co-(methacrylic acid)] Healing Agents for Mendable Carbon Fiber Laminates , 2010 .

[5]  Fred Wudl,et al.  Synthesis and Characterization of a Single-Component Thermally Remendable Polymer Network: Staudinger and Stille Revisited , 2008 .

[6]  Scott A. Furman,et al.  Polyethylene-co-methacrylic acid healing agents for mendable epoxy resins , 2009 .

[7]  A. Mouritz,et al.  Self-healing of delamination fatigue cracks in carbon fibre–epoxy laminate using mendable thermoplastic , 2012, Journal of Materials Science.

[8]  A. Mouritz,et al.  A mechanistic approach to the properties of stitched laminates , 2000 .

[9]  Chun H. Wang,et al.  Healing of carbon fibre–epoxy composite T-joints using mendable polymer fibre stitching , 2013 .

[10]  J. Velasco,et al.  Influence of EMAA compatibilizer on the structure and properties of HDPE/hydrotalcite nanocomposites prepared by melt mixing , 2009 .

[11]  Chun H. Wang,et al.  Ultrasonic activation of mendable polymer for self-healing carbon–epoxy laminates , 2013 .

[12]  Russell J. Varley,et al.  Confirmation of the healing mechanism in a mendable EMAA–epoxy resin , 2012 .

[13]  A. Mouritz,et al.  A mechanistic interpretation of the comparative in-plane mechanical properties of 3D woven, stitched and pinned composites , 2010 .

[14]  Fred Wudl,et al.  The world of smart healable materials , 2010 .

[15]  D. Wu,et al.  FTIR study of bonding between a thermoplastic healing agent and a mendable epoxy resin , 2010 .

[16]  Ajit K. Mal,et al.  New Thermally Remendable Highly Cross-Linked Polymeric Materials , 2003 .

[17]  S. Zwaag,et al.  Development of a quasi-static test method to investigate the origin of self-healing in ionomers under ballistic conditions , 2008 .

[18]  D. Wu,et al.  Self-healing polymeric materials: A review of recent developments , 2008 .

[19]  Yiu-Wing Mai,et al.  Improving the delamination resistance of CFRP by stitching—a review , 1994 .

[20]  Tao Yang,et al.  Toughening and self-healing of epoxy matrix laminates using mendable polymer stitching , 2012 .