An improved basis for characterizing the suitability of fly ash as a cement replacement agent

Fly ash is a critical material for partial replacement of ordinary portland cement (OPC) in the binder fraction of a concrete mixture. However, significant compositional variability currently limits fly ash use. For example, the performance of OPC-fly ash blends cannot be estimated a priori using current characterization standards (e.g., ASTM C618). In this study, fly ashes spanning a wide compositional range are characterized in terms of glassy and crystalline phases using a combination of X-ray fluorescence (XRF), X-ray diffraction (XRD), and scanning electron microscopy with X-ray energy dispersive spectroscopy (SEM-EDS) techniques. The compositional data are distilled to a unitless parameter, the network ratio (Nr), which represents the network behavior of atoms that form alkali/alkaline earth-aluminosilicate glasses that make up fly ashes. Nr is correlated to known composition-dependent features, including the glass transition temperature and amorphous XRD peak (“hump”) position. Analysis of heat release data and compressive strengths are used to evaluate the impact of fly ash compositions on reaction kinetics and on the engineering properties of cement-fly ash blends. It is shown that fly ashes hosting glasses with a high network ratio (i.e., having a less stable glass structure) are more reactive than others. This article is protected by copyright. All rights reserved.

[1]  Vojtech Janousek,et al.  TECHNICAL NOTE Interpretation of Whole-rock Geochemical Data in Igneous Geochemistry: Introducing Geochemical Data Toolkit (GCDkit) , 2006 .

[2]  Yubin Jun,et al.  The importance of the network-modifying element content in fly ash as a simple measure to predict its strength potential for alkali-activation , 2015 .

[3]  Sidney Diamond,et al.  On the glass present in low-calcium and in high-calcium flyashes , 1983 .

[4]  J. Biernacki,et al.  Kinetics of carbon oxidation from fly ash , 2010 .

[5]  D. Fowler,et al.  Comprehensive Phase Characterization of Crystalline and Amorphous Phases of a Class F Fly Ash , 2010 .

[6]  C. Poon,et al.  Degree of hydration and gel/space ratio of high-volume fly ash/cement systems , 2000 .

[7]  M. Daimon,et al.  Hydration of fly ash cement , 2005 .

[8]  G. Sant,et al.  Topological Control on Silicates' Dissolution Kinetics. , 2015, Langmuir : the ACS journal of surfaces and colloids.

[9]  Michael D.A. Thomas,et al.  Use of ternary blends containing silica fume and fly ash to suppress expansion due to alkali-silica reaction in concrete , 2002 .

[10]  E. E. Berry,et al.  Mechanisms of hydration reactions in high volume fly ash pastes and mortars , 1990 .

[11]  V. Papadakis Effect of fly ash on Portland cement systems. Part II. High-calcium fly ash , 1999 .

[12]  Sidney Diamond The utilization of flyash , 1984 .

[13]  R. Snellings Surface Chemistry of Calcium Aluminosilicate Glasses , 2015 .

[14]  D. Fowler,et al.  An examination of the reactivity of fly ash in cementitious pore solutions , 2013 .

[15]  P. K. Mehta Influence of fly ash characteristics on the strength of portland-fly ash mixtures , 1985 .

[16]  Vagelis G. Papadakis,et al.  Effect of fly ash on Portland cement systems , 1999 .

[17]  J. Ideker,et al.  Advances in alternative cementitious binders , 2011 .

[18]  Della M. Roy,et al.  Characterization of Fly Ash and its Reactions in Concrete , 1984 .

[19]  D. Neuville,et al.  Al speciation and Ca environment in calcium aluminosilicate glasses and crystals by Al and Ca K-edge X-ray absorption spectroscopy. , 2004 .

[20]  D. Neuville,et al.  Relationship Between Structure and Glass Transition Temperature in Low-silica Calcium Aluminosilicate Glasses: the Origin of the Anomaly at Low Silica Content. , 2005 .

[21]  Jeffrey W. Bullard,et al.  The Filler Effect: The Influence of Filler Content and Surface Area on Cementitious Reaction Rates , 2013 .

[22]  Robert H. Hurt,et al.  Size distribution of unburned carbon in coal fly ash and its implications , 2004 .

[23]  Carl-Eric Hagentoft,et al.  Determination of specific heat capacity by transient plane source , 2012 .

[24]  P. Termkhajornkit,et al.  Microstructurally-designed cement pastes: A mimic strategy to determine the relationships between microstructure and properties at any hydration degree , 2015 .

[25]  Ryan S. Winburn,et al.  Rietveld quantitative X-ray diffraction analysis of NIST fly ash standard reference materials , 2000, Powder Diffraction.

[26]  G. Sant,et al.  Simple methods to estimate the influence of limestone fillers on reaction and property evolution in cementitious materials , 2013 .

[27]  G. Saoût,et al.  Application of the Rietveld method to the analysis of anhydrous cement , 2011 .

[28]  I. Avramov,et al.  The glass transition temperature of silicate and borate glasses , 2005 .

[29]  David A. Landgrebe,et al.  MultiSpec: a tool for multispectral--hyperspectral image data analysis , 2002 .

[30]  I. Avramov,et al.  Effect of chemical composition on viscosity of oxide glasses , 2003 .

[31]  C. Dunant,et al.  A new quantification method based on SEM-EDS to assess fly ash composition and study the reaction of its individual components in hydrating cement paste , 2015 .

[32]  D. Bentz,et al.  Rheology and setting of high volume fly ash mixtures , 2010 .

[33]  Y. Yue Characteristic temperatures of enthalpy relaxation in glass , 2008 .

[34]  L. Price,et al.  CARBON DIOXIDE EMISSIONS FROM THE GLOBAL CEMENT INDUSTRY , 2001 .

[35]  S. Diamond Particle morphologies in fly ash , 1986 .

[36]  E. E. Berry,et al.  On the Glass in Coal Fly Ashes: Recent Advances , 1987 .