Glass Forming Ability of Bulk Amorphous Materials in Cu-Zr-Ag Ternary Alloy Systems

The glass forming ability (GFA) of the Cu-Zr-Ag alloy system was investigated on the basis of the thermal stability, and the structural, thermodynamic and kinetic properties of the material. We changed the concentration of the alloys, as we departed from the Cu58Zr42 composition and produced three different eutectic points in the Cu-Zr-Ag ternary system, in accordance with the results published in the respective literature. We produced various test pieces of Cu-Zr-Ag amorphous alloys with different Ag contents (0-70%), by casting the material into wedge-shaped copper moulds. In such ternary alloy system there is only a limited concentration range where amorphous materials can be produced: in the event that the Ag content of the material exceeds 35 at%, no amorphous material structure will develop. In our experiment the maximum temperature range of the supercooled liquid region (ΔTx) was 75 K. The calculated four GFA parameter values are not in perfect harmony and fail to point out the optimal composition available; however, based on γ and the reciprocal value of ω, the best compositions from the GFA aspect are Cu42.5Zr37.5Ag20 and Cu40Zr37.5Ag22.5. The decrease of the maximum thickness of the bulk metallic glasses is influenced more by the oxygen content than the composition changes within the Cu-Zr-Ag system.

[1]  I. Jung,et al.  Critical thermodynamic evaluation and optimization of the Ag–Zr, Cu–Zr and Ag–Cu–Zr systems and its applications to amorphous Cu–Zr–Ag alloys , 2010 .

[2]  A. Inoue,et al.  A new criterion for predicting the glass-forming ability of bulk metallic glasses , 2009 .

[3]  N. Hegman,et al.  CuZrAl amorphous alloys prepared by casting and milling , 2009 .

[4]  D. V. Louzguine-Luzgin,et al.  Cooling rate, structure, thermal stability and crystallization behaviour of Cu-based bulk glass-forming alloys , 2009 .

[5]  L. Schultz,et al.  Cap casting and enveloped casting techniques for Zr55Cu30Ni5Al10 glassy alloy rod with 32 mm in diameter , 2009 .

[6]  Wei Zhang,et al.  Formation of a phase separating bulk metallic glass in Cu40Zr40Al10Ag10 alloy , 2008 .

[7]  W. Johnson,et al.  Compositional dependence of thermal, elastic, and mechanical properties in Cu–Zr–Ag bulk metallic glasses , 2008 .

[8]  J. Eckert,et al.  Structural behavior of CuxZr100−x metallic glass (x = 35−70) , 2008 .

[9]  K. Vecchio,et al.  Prediction of glass-forming compositions using liquidus temperature calculations , 2007 .

[10]  Wei Zhang,et al.  Devitrification behavior and glass-forming ability of Cu–Zr–Ag alloys , 2007 .

[11]  Wei Zhang,et al.  Effects of additional Ag on the thermal stability and glass-forming ability of Cu–Zr binary glassy alloys , 2007 .

[12]  C. Dong,et al.  Cu–Zr–Ag bulk metallic glasses based on Cu8Zr5 icosahedron , 2007 .

[13]  H. S. Liu,et al.  Thermodynamic description of the Cu–Ag–Zr system , 2006 .

[14]  T. Abe,et al.  Glass formation and phase separation in the Ag–Cu–Zr system , 2006 .

[15]  W. Johnson,et al.  TEM study of structural evolution in a copper mold cast Cu46Zr54 bulk metallic glass , 2006 .

[16]  D. Kim,et al.  Parameter for glass forming ability of ternary alloy systems , 2005 .

[17]  C. Liu,et al.  A new glass-forming ability criterion for bulk metallic glasses , 2002 .

[18]  I. Kuti,et al.  Modelling of Microsegregation of Binary Solid Solutions , 2000 .

[19]  A. Inoue.  Stabilization of metallic supercooled liquid and bulk amorphous alloys , 2000 .

[20]  H. Shibata,et al.  Melting temperature, Transformation and Metastable phase diagram of rapidly solidified Ag-Cu alloys , 1998 .

[21]  M. Flemings,et al.  Measurements of Solute Redistribution in Dendritic Solidification , 1966 .