Annealing effects on microstructure and laser-induced damage threshold of quasi-rugate filters.

Ta2O5/SiO2 quasi-rugate filters with high damage thresholds were deposited by ion-beam sputtering and then annealed at temperature of 200-800°C. The relations between microstructure, optical properties, chemical composition, weak absorption, and laser-induced damage threshold (LIDT) were studied. It was found that the transmittance spectra shifted to short wavelength as the annealing temperature increased. Three evolution courses of the films in the annealing process were analyzed by Atomic Force microscopy (AFM), Zygo interferometer measurement and Focused Ion Beam microscope (FIB). The decreased weak absorption during annealing process was found with significant effect on the LIDT. As the annealing temperature increased to 600°C, the weak absorption of films decreased from 39.99 to 7.2 ppm and the 50%-LIDTs increased from 59.32 to 158.87J/cm2. Distinct damage micrographs of the films annealed at different temperature were obtained. A combination of substoichiometric defect and structural defect dominant description was used to illustrate the aggravation of laser-induced damage.

[1]  A. Amassian,et al.  Stability and effect of annealing on the optical properties of plasma-deposited Ta2O5 and Nb2O5 films , 2006 .

[2]  M. Jupé,et al.  Morphology investigations of laser induced damage , 2007, SPIE Laser Damage.

[3]  H. Angus Macleod,et al.  Structure‐related optical properties of thin films , 1986 .

[4]  William H. Southwell,et al.  Spectral response calculations of rugate filters using coupled-wave theory , 1988 .

[5]  Z. Fan,et al.  Investigation of annealing effects on the laser-induced damage threshold of amorphous Ta2O5 films , 2009 .

[6]  Y. Jin,et al.  Effect of Rapid Thermal Annealing on the Structure and the Electrical Properties of Atomic-Layer-Deposited Ta$_2$O$_5$ Films , 2000 .

[7]  Z. Fan,et al.  High temperature annealing effect on structure, optical property and laser-induced damage threshold of Ta 2 O 5 films , 2008 .

[8]  P. Baumeister,et al.  Simulation of a rugate filter via a stepped-index dielectric multilayer. , 1986, Applied optics.

[9]  Jianda Shao,et al.  Annealing effects on structure and laser-induced damage threshold of Ta2O5/SiO2 dielectric mirrors , 2003 .

[10]  Yoshifumi Kawamoto,et al.  Promising storage capacitor structures with thin Ta/sub 2/O/sub 5/ film for low-power high-density DRAMs , 1990 .

[11]  Ping Ma,et al.  Characterization of 1064nm nanosecond laser-induced damage on antireflection coatings grown by atomic layer deposition. , 2012, Optics express.

[12]  Marc D. Fontana,et al.  Amorphous to crystalline transformation in Ta2O5 studied by Raman spectroscopy , 2012 .

[14]  Xiaomin Li,et al.  Effects of the post-annealing ambience on the microstructure and optical properties of tantalum oxide films prepared by pulsed laser deposition , 2009 .

[15]  S. Sorge,et al.  High quality r.f. sputtered metal oxides (Ta2O5, HfO2) and their properties after annealing , 2003 .