Geometrical characteristics and damage morphology of nodules grown from artificial seeds in multilayer coating.

Nodules have been planted in an HfO(2)/SiO(2) multilayer system with absorptive gold nanoparticle seeds located on the surface of a substrate. The topography of nodules was scanned by an atomic force microscope and imaged by a scanning electron microscope. The underlying characteristics of nodules were revealed by a focused ion beam. The cross-sectional profiles reveal that nodules grown from small seeds have a continuous boundary and better mechanical stability. A laser-induced damage test shows that nodules decrease the laser-induced damage threshold by up to 3 times. The damage pits are exclusively caused by nodular ejection and triggered by the absorptive seeds. The distribution of electric field and average temperature rise in the nodules were analyzed. Theoretical results met experimental results very well. The strong absorptive seed and microlens effect of the nodule play important roles in laser-induced damage of a planted nodule.

[1]  Donald R Uhlmann,et al.  Mechanism of Inclusion Damage in Laser Glass , 1970 .

[2]  Mark R. Kozlowski,et al.  Characterization of defect geometries in multilayer optical coatings , 1994 .

[3]  Mark R. Kozlowski,et al.  Comparison of nodular defect seed geometries from different deposition techniques , 1996, Laser Damage.

[4]  Christopher J Stolz,et al.  Laser intensification by spherical inclusions embedded within multilayer coatings. , 2006, Applied optics.

[5]  K. Yee Numerical solution of initial boundary value problems involving maxwell's equations in isotropic media , 1966 .

[6]  Pierre Garrec,et al.  1.06-μm laser irradiation on high-reflection coatings inside a scanning electron microscope , 1999, Laser Damage.

[7]  Herve Leplan,et al.  New approach for the critical size of nodular defects: the mechanical connection , 1999, Laser Damage.

[8]  S. Papernov,et al.  Using gold nanoparticles as artificial defects in thin films: What have we learned about laser-induced damage driven by localized absorbers? , 2006, SPIE Laser Damage.

[9]  Rick H. Sawicki,et al.  Failure characterization of nodular defects in multilayer dielectric coatings , 1995, Laser Damage.

[10]  C. Tranter,et al.  Heat flow in an infinite medium heated by a sphere , 1952 .

[11]  Mark R. Kozlowski,et al.  Role of defects in laser damage of multilayer coatings , 1993, Laser Damage.

[12]  Mark R. Kozlowski,et al.  In-situ atomic-force microscopy of laser-conditioned and laser-damaged HfO2/SiO2 dielectric mirror coatings , 1992, Laser Damage.

[13]  Jean Hue,et al.  Thermomechanical model of mirror laser damage at 1.06 μm: I. Nodule ejection , 1999, Laser Damage.

[14]  Francois Y. Genin,et al.  Morphologies of laser-induced damage in hafnia-silica multilayer mirror and polarizer coatings , 1996, Other Conferences.

[15]  B. Rafin,et al.  Generation of defects with diamond and silica particles inside high-reflection coatings: influence on the laser damage threshold , 1999, Optical Systems Design.

[16]  Jianda Shao,et al.  Characteristics of nodular defect in HfO2/SiO2 multilayer optical coatings , 2010 .

[17]  Mark R. Kozlowski,et al.  Modeling of electric-field enhancement at nodular defects in dielectric mirror coatings , 1993, Laser Damage.

[18]  Christopher J. Stolz,et al.  Effect of SiO2 overcoat thickness on laser damage morphology of HfO2/SiO2 Brewster's angle polarizers at 1064 nm , 1997, Laser Damage.