Nano-AlN functionalization by silane modification for the preparation of covalent-integrated epoxy/poly(ether imide) nanocomposites

Aluminum nitride nanoparticle (nano-AlN) organically modified with the silane-containing epoxide groups (3-glycidoxypropyltrimethoxy silane, GPTMS) was incorporated into a mixture of poly(ether imide) (PEI), and methyl hexahydrophthalic anhydride-cured bisphenol A diglycidyl ether grafted by GPTMS was prepared for nanocomposite. Scanning electron microscopy, transmission electron microscopy, and atomic force microscopy were used to investigate the microscopic structures of nanocomposites. According to experimental results, it was shown that addition of nano-AlN and PEI into the modified epoxy could lead to the improvement of the impact and bend strengths. When the concentrations of nano-AlN and PEI were 20 and 10 pbw, respectively, the toughness/stiffness balance could be achieved. Dynamic mechanical analysis (DMA) results displayed that two glass transition temperatures (Tg) found in the nanocomposites were assigned to the modified epoxy phase and PEI phase, respectively. As nano-AlN concentration increased, Tg value of epoxy phase had gradually increased, and the storage modulus of the nanocomposite at the ambient temperature displayed an increasing tendency. Additionally, thermal stability of the nanocomposite was apparently improved. The macroscopic properties of nanocomposites were found to be strongly dependent on their components, concentrations, dispersion, and resulted morphological structures. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010

[1]  M. Razzaq,et al.  Thermomechanical studies of aluminum nitride filled shape memory polymer composites , 2007 .

[2]  Ji-Ming Hu,et al.  Improving the corrosion performance of epoxy coatings by chemical modification with silane monomers , 2007 .

[3]  Enrico Boccaleri,et al.  Synthetic, layered nanoparticles for polymeric nanocomposites (PNCs) , 2007 .

[4]  A. Ershad-Langroudi,et al.  Synthesis and characterization of hydrophilic nanocomposite coating on glass substrate , 2006 .

[5]  Adriaan S. Luyt,et al.  Thermal, mechanical and electrical properties of copper powder filled low-density and linear low-density polyethylene composites , 2006 .

[6]  W. Shi,et al.  Effects of hyperbranched poly(ester-silane) as a coupling agent on the mechanical behavior of glass bead filled epoxy resin , 2005 .

[7]  R. Vaia,et al.  Generating Triaxial Reinforced Epoxy/Montmorillonite Nanocomposites with Uniaxial Magnetic Fields , 2005 .

[8]  U. Sundararaj,et al.  Big returns from small fibers: A review of polymer/carbon nanotube composites , 2004 .

[9]  J. Pascault,et al.  Effect of Reinforcing Glass Fibers on Morphology and Properties of Thermoplastic Modified Epoxy-Aromatic Diamine Matrix , 2004 .

[10]  Yingfeng Yu,et al.  Viscoelastic effects on the phase separation in thermoplastics modified cyanate ester resin , 2004 .

[11]  R. Vaia,et al.  Tuning Polymer Nanocomposite Morphology: AC Electric Field Manipulation of Epoxy–Montmorillonite (Clay) Suspensions , 2004 .

[12]  I. Mondragon,et al.  AFM approach toward understanding morphologies in toughened thermosetting matrices , 2003 .

[13]  Yingfeng Yu,et al.  Viscoelastic Effects on the Phase Separation in Thermoplastics-Modified Epoxy Resin , 2003 .

[14]  R. Mülhaupt,et al.  Toughened Epoxy Hybrid Nanocomposites Containing Both an Organophilic Layered Silicate Filler and a Compatibilized Liquid Rubber , 2003 .

[15]  D. Lou,et al.  Simple thermal model for online laser curing of thermoset composites in filament winding , 2003 .

[16]  Donald R Paul,et al.  Effect of glass fiber surface chemistry on the mechanical properties of glass fiber reinforced, rubber-toughened nylon 6 , 2002 .

[17]  G. Simon,et al.  Morphology, thermal relaxations and mechanical properties of layered silicate nanocomposites based upon high-functionality epoxy resins , 2002 .

[18]  Alan J. Lesser,et al.  Intercalated clay nanocomposites: Morphology, mechanics, and fracture behavior , 2001 .

[19]  A. Terauchi,et al.  Phase structure and mechanical and adhesion properties of epoxy/silica hybrids , 2001 .

[20]  Junkyung Kim,et al.  Effect of molecular weight between crosslinks on the fracture behavior of rubber-toughened epoxy adhesives , 2001 .

[21]  P. Hing,et al.  Dynamic mechanical properties of polystyrene–aluminum nitride composite , 2000 .

[22]  Otto Zhou,et al.  Deformation of carbon nanotubes in nanotube–polymer composites , 1999 .

[23]  P. Heiden,et al.  Investigation of readily processable thermoplastic-toughened thermosets. V. Epoxy resin toughened with hyperbranched polyester , 1999 .

[24]  P. Heiden,et al.  Investigation of readily processable thermoplastic-toughened thermosets. III. Toughening BMIs and epoxy with a comb-shaped imide oligomer , 1998 .

[25]  Gu Xu,et al.  Thermally conductive polymer composites for electronic packaging , 1997 .

[26]  Yuan Hu,et al.  Miscibility, morphology and fracture toughness of epoxy resin/poly(vinyl acetate) blends , 1996 .

[27]  J. W. Park,et al.  Phase separation during synthesis of polyetherimide/epoxy semi-IPNs , 1996 .

[28]  H. Hamada,et al.  Degradation behavior of mechanically fastened joints of glass‐reinforced crosslinked polyester immersed in hot water , 1995 .

[29]  Tatsuya Ohsako,et al.  Morphologies and tensile properties of elastomer-modified epoxy and polycarbonate blended systems , 1993 .

[30]  Z. Stachurski,et al.  Reaction mechanisms, microstructure, and fracture properties of thermoplastic polysulfone‐modified epoxy resin , 1993 .

[31]  S. D. Jenkins,et al.  A dielectric, mechanical, rheological and electron microscopy study of cure and properties of a thermoplastic-modified epoxy resin , 1992 .

[32]  Peter G. Pape,et al.  Methods for improving the performance of silane coupling agents , 1991 .

[33]  C. Bucknall,et al.  Toughening tetrafunctional epoxy resins using polyetherimide , 1989 .