Bonding mechanism of electroless Ni-P film with AlN substrate and Cu foil

Electroless Ni (EN) plating method is employed to metallize Y2O3-doped AlN ceramic substrates with different surface morphologies, including the as-received, polished, and etched AlN. The EN-plated AlN substrate is bonded with the Cu foil to form a sandwich-like AlN-EN/Cu/EN-AlN assembly by hot pressing in vacuum with a pressure of 6.5 MPa for 30 min. The bonding strength of the joint is determined by the adhesive abilities of EN/AlN and EN/Cu interfaces. Bonding between the Cu foil and the EN film is achieved by the interdiffusion of Cu and Ni atoms to form a solid solution interlayer, while the EN film is adhered on the AlN substrate mainly by the mechanical interlocking through the rough interface, etched holes, and open pores. At the bonding temperatures lower than 400/spl deg/C, no reaction occurs between the Cu foil and the EN film. Increasing bonding temperature enhances the interdiffusion of Cu and Ni to form a strong bonded solid solution interlayer. However, the depletion of the element Ni in EN film results in the formation and enlargement of the pores at EN/AlN interface, which makes a poor adhesion between EN film and AlN substrate. An optimum bonding temperature is observed around 600 and 700/spl deg/C for various surface conditions of AM substrates. Theoretical calculations of the residual thermal stresses in AlN, EN, and Cu layers with respect to the bonding temperatures are related to the variation of the bonding strengths. The relations of the adhesion strengths, interfacial morphologies, elemental distribution, and calculated residual stresses is proposed.

[1]  P. Gudmundson,et al.  Mechanical Properties of Liquid‐Phase‐Bonded Copper‐Ceramic Substrates , 1982 .

[2]  S. Rhee.  Wetting of AlN and TiC by Liquid Ag and Liquid Cu , 1970 .

[3]  S. Rhee.  Wetting of Ceramics by Liquid Aluminum , 1970 .

[4]  C. Young,et al.  Indirect bonding of Ni-electroless plated AlN and Cu by hot pressing method , 1994 .

[5]  Glenn O. Mallory,et al.  Electroless plating : fundamentals and applications , 1990 .

[6]  C. Young,et al.  Thick film metallization of AlN substrate with Cu conductive pastes , 1992, 1992 Proceedings 42nd Electronic Components & Technology Conference.

[7]  K. Suganuma,et al.  Diffusion-reaction bonding of ceramics to ceramics and to metals under pressure , 1984 .

[8]  J. Gobrecht,et al.  Directly Bonded Copper Metallization of AℓN Substrates for Power Hybrids , 1984 .

[9]  C. Young,et al.  Adhesion strength and microstructural evaluation in electroless Ni-P metallized AlN substrate , 1997 .

[10]  W. D. Scott,et al.  Characterization of the AIN–W Interface in a Cofired Multilayer AIN Substrate , 1989 .

[11]  T. Osaka,et al.  Metalization of AlN Ceramics by Electroless Ni‐P Plating , 1986 .

[12]  W. Pamler,et al.  Grain boundary diffusion in Ni―Cu multilayer films , 1988 .

[13]  T. Osaka,et al.  Chemical Etching Properties of Highly Thermal Conductive AlN Ceramics for Electroless Ni‐P Metallization , 1988 .

[14]  A. Evans,et al.  Residual Stresses in Meta/Ceramic Bonded Strips , 1985 .

[15]  W. Zdaniewski,et al.  Characterization of Gold—Aluminum Nitride and Gold—Silicon Carbide Interfaces , 1989 .

[16]  Arthur H. Graham,et al.  The Structure and Mechanical Properties of Electroless Nickel , 1965 .

[17]  C. Young,et al.  Corrosion of aluminium nitride substrates in acid, alkaline solutions and water , 1995 .

[18]  A. Knudsen,et al.  Effect of Yttria on the Thermal Conductivity of Aluminum Nitride , 1993 .

[19]  D. Kolar,et al.  Wetting of Aluminum Nitride by Nickel Alloys , 1978 .

[20]  Hideo Takamizawa,et al.  A1N Substrates with High Thermal Conductivity , 1985 .

[21]  R. Lee.  Development of High Thermal Conductivity Aluminum Nitride Ceramic , 1991 .

[22]  Y. Iijima,et al.  Determination of Intrinsic Diffusion Coefficients in a Wide Concentration Range of a Cu–Ni Couple by the Multiple Markers Method , 1982 .