Effects of Bismuth on Wide-Depletion-Width GaInNAs Solar Cells

GaInNAs solar cells could be useful in next-generation multijunction solar cells if issues surrounding low photocurrents and photovoltages are surmounted. Wide-depletion-width devices generate significant photocurrent using a p-i-n structure grown by molecular beam epitaxy, but these depletion widths are only realized in a region of parameter space that leads to rough surface morphologies. Here, bismuth is explored as a surfactant for the growth of GaInNAs solar cells. Very low fluxes of Bi are effective at maintaining smooth surfaces, even at high growth temperatures and In contents. However, Bi also increases the net donor concentration in these materials, manifested in our n-on-p device structures as a pn-junction that moves deeper into the base layer with increasing Bi fluxes. Quantum efficiency modeling and scanning kelvin probe microscopy measurements confirm the type conversion of the base layer from p type to n type. Bi incorporation in GaAsBi samples shows signs of surface segregation, leading to...

[1]  James S. Harris,et al.  Dilute nitride GaInNAs and GaInNAsSb solar cells by molecular beam epitaxy , 2007 .

[2]  Daryl R. Myers,et al.  Projected performance of three- and four-junction devices using GaAs and GaInP , 1997, Conference Record of the Twenty Sixth IEEE Photovoltaic Specialists Conference - 1997.

[3]  Z. R. Wasilewski,et al.  Molecular beam epitaxy growth of 1.55 μm GaInNAs(Sb) double quantum wells with bright and narrow photoluminescence , 2006 .

[4]  Eric Daniel Jones,et al.  Minority carrier diffusion, defects, and localization in InGaAsN with 2% nitrogen , 2000 .

[5]  Daniel J. Friedman,et al.  Effects of temperature, nitrogen ions, and antimony on wide depletion width GaInNAs , 2007 .

[6]  T. Tiedje,et al.  Bismuth surfactant growth of the dilute nitride GaNxAs1−x , 2005 .

[7]  Daniel J. Friedman,et al.  Photocurrent of 1 eV GaInNAs lattice-matched to GaAs , 1998 .

[8]  I. Batyrev,et al.  5-7-5 line defects on As ∕ Si ( 100 ) : A general stress-relief mechanism for V/IV surfaces , 2006 .

[9]  Xiaodong Yang,et al.  Molecular beam epitaxial growth of InGaAsN:Sb/GaAs quantum wells for long-wavelength semiconductor lasers , 1999 .

[10]  S. Ho,et al.  Growth of InxGa1−xAs/GaAs heterostructures using Bi as a surfactant , 2000 .

[11]  S. Kurtz,et al.  Low-acceptor-concentration GaInNAs grown by molecular-beam epitaxy for high-current p-i-n solar cell applications , 2005 .

[12]  Erin C. Young,et al.  Surfactant enhanced growth of GaNAs and InGaNAs using bismuth , 2003 .

[13]  Enhanced-depletion-width GaInNAs solar cells grown by molecular-beam epitaxy , 2005, Conference Record of the Thirty-first IEEE Photovoltaic Specialists Conference, 2005..

[14]  K. Evans,et al.  Surface chemistry evolution during molecular beam epitaxy growth of InGaAs , 1995 .

[15]  D. G. Thomas,et al.  LUMINESCENCE DUE TO THE ISOELECTRONIC SUBSTITUTION OF BISMUTH FOR PHOSPHORUS IN GALLIUM PHOSPHIDE , 1966 .

[16]  J. Harris,et al.  Molecular-beam epitaxy growth of low-threshold cw GaInNAsSb lasers at 1.5 μm , 2005 .

[17]  Xiaodong Yang,et al.  InGaAsNSb/GaAs quantum wells for 1.55 μm lasers grown by molecular-beam epitaxy , 2001 .

[18]  D. Friedman,et al.  Measurement of built-in electrical potential in III–V solar cells by scanning Kelvin probe microscopy , 2003 .

[19]  D. Friedman,et al.  Distribution of built-in electrical potential in GaInP2/GaAs tandem-junction solar cells , 2003 .

[20]  Sumio Hosaka,et al.  Silicon pn junction imaging and characterizations using sensitivity enhanced Kelvin probe force microscopy , 1995 .