In vivo behaviour of hydroxyapatite coatings on titanium implants: a quantitative study in the rabbit.

The aim of this study was to evaluate quantitatively the behaviour of in vivo hydroxyapatite coated implants (HA) in the rabbit over time, and to compare the results with observations made on titanium plasma spray implants (TPS). Results were analysed according to the percentage of bone contact. Eighteen HA cylindrical implants (3.25 x 8 mm) and 6 TPS cylindrical implants from Steri-Oss were placed in the epiphysis of the femur in 24 white rabbits. Each rabbit received one implant. Three rabbits with one HA implant (n = 3) and 1 rabbit with one TPS implant (n = 1) were sacrificed after implantation periods of 2, 4, 6, 8, 10 and 12 months. Implants were cut along the long axis and prepared for histological and histomorphometrical evaluations. Measurements of coating thickness and percentage of bone contact were performed with scanning electron microscopy analysis on the sides of the implant, in 3 different types of bone, namely cortical, trabecular and marrow. In cortical bone, dense bone was apposed to the HA implants: from 92.3 +/- 5.5% at 2 months to 89.6 +/- 6.5% at 1 year, with no significant regression of HA thickness (P = 0.37). TPS coating showed less bone contact, but thickness was stable (P = 0.46). In trabecular zone, where bone contact was less pronounced, a significant regression of HA coatings thickness (P < 0.05) was observed. Nevertheless TPS coatings were stable (P = 0.81). Histomorphometrical results demonstrated that a highly significant regression (P < 0.0001) of HA thickness was observed in the marrow area, where the bone-to-implant contact never exceeded 7.6% from 2 to 12 months. TPS coating did not reveal any sign of resorption (P = 0.88), despite a rare bone contact. Histological analysis revealed inflammatory and giant cells, principally in the marrow area in contact with HA coating, but always in restrictive numbers. We conclude that bone contact protected the HA coating from resorption.

[1]  C. Bünger,et al.  Resorption of hydroxyapatite and fluorapatite coatings in man , 1997 .

[2]  Golec Ts,et al.  Long-term retrospective studies on hydroxyapatite coated endosteal and subperiosteal implants. , 1992 .

[3]  P. Trisi,et al.  Light and confocal laser scanning microscopic evaluation of hydroxyapatite resorption patterns in medullary and cortical bone. , 1993, The International journal of oral & maxillofacial implants.

[4]  C. Bünger,et al.  Hydroxyapatite coating converts fibrous tissue to bone around loaded implants. , 1993, The Journal of bone and joint surgery. British volume.

[5]  A. Biesbrock,et al.  Evaluation of the clinical predictability of hydroxyapatite-coated endosseous dental implants: a review of the literature. , 1995, The International journal of oral & maxillofacial implants.

[6]  J. Ong,et al.  Properties of calcium phosphate coatings before and after exposure to simulated biological fluid. , 1997, Biomaterials.

[7]  G. Daculsi,et al.  Polymyxin B inhibits biphasic calcium phosphate degradation induced by lipopolysaccharide-activated human monocytes/macrophages. , 1998, Journal of biomedical materials research.

[8]  D Buser,et al.  Influence of surface characteristics on bone integration of titanium implants. A histomorphometric study in miniature pigs. , 1991, Journal of biomedical materials research.

[9]  C. Blitterswijk,et al.  Osteoblast and Osteoclast Responses to Calcium Phosphates , 1994 .

[10]  G. Daculsi,et al.  Macroporous biphasic calcium phosphate ceramics: influence of macropore diameter and macroporosity percentage on bone ingrowth. , 1998, Biomaterials.

[11]  O. Gan,et al.  Biodegradation of synthetic biphasic calcium phosphate by human monocytes in vitro: a morphological study. , 1996, Biomaterials.

[12]  J. Jansen,et al.  A histological evaluation of TiO2-gritblasted and Ca-P magnetron sputter coated implants placed into the trabecular bone of the goat: Part 2. , 2000, Clinical oral implants research.

[13]  G. Daculsi,et al.  Apatite precipitation after incubation of biphasic calcium-phosphate ceramic in various solutions: influence of seed species and proteins. , 1998, Journal of biomedical materials research.

[14]  K. Donath,et al.  Interface between bone tissue and implants of solid hydroxyapatite or hydroxyapatite-coated titanium implants. , 1989, Biomaterials.

[15]  P. Trisi,et al.  Histochemical and laser scanning microscopy characterization of the hydroxyapatite-bone interface: an experimental study in rabbits. , 1994, The International journal of oral & maxillofacial implants.

[16]  U. Aebi,et al.  Severe osteolysis after third-body wear due to hydroxyapatite particles from acetabular cup coating. , 1998, The Journal of bone and joint surgery. British volume.

[17]  G. Daculsi,et al.  Ultrastructural study of degradation of calcium phosphate ceramic by human monocytes and modulation of this activity by HILDA/LIF cytokine. , 1996, The journal of histochemistry and cytochemistry : official journal of the Histochemistry Society.

[18]  G. Daculsi,et al.  Osteoclastic resorption of calcium phosphate ceramics with different hydroxyapatite/beta-tricalcium phosphate ratios. , 1997, Biomaterials.

[19]  C. Klein,et al.  Bonding of bone to apatite-coated implants. , 1988, The Journal of bone and joint surgery. British volume.

[20]  C. Klein,et al.  Plasma sprayed coatings of hydroxylapatite. , 1987, Journal of biomedical materials research.

[21]  T. Albrektsson,et al.  Histomorphometric studies of hydroxylapatite-coated and uncoated CP titanium threaded implants in bone. , 1991, The International journal of oral & maxillofacial implants.

[22]  Olivier Gauthier,et al.  Macroporous biphasic calcium phosphate ceramics , 1997 .

[23]  I. Hvid,et al.  Fixation of titanium and hydroxyapatite-coated implants in arthritic osteopenic bone. , 1991, The Journal of arthroplasty.

[24]  C. Berndt,et al.  Variability of hydroxyapatite-coated dental implants. , 1998, The International journal of oral & maxillofacial implants.

[25]  S D Cook,et al.  Interface mechanics and histology of titanium and hydroxylapatite-coated titanium for dental implant applications. , 1987, The International journal of oral & maxillofacial implants.

[26]  S. Radin,et al.  Effect of serum proteins and osteoblasts on the surface transformation of a calcium phosphate coating: a physicochemical and ultrastructural study. , 1998, Journal of biomedical materials research.

[27]  G. Daculsi,et al.  Growth hormone stimulatory effects on osteoclastic resorption are partly mediated by insulin-like growth factor I: an in vitro study. , 1998, Bone.

[28]  I. Rossen,et al.  Investigation of the surface texture of hydroxylapatite-coated dental implants by means of SEM. , 1989 .

[29]  J. Ong,et al.  Effect of transforming growth factor-beta on osteoblast cells cultured on 3 different hydroxyapatite surfaces. , 1999, The International journal of oral & maxillofacial implants.

[30]  T. Albrektsson,et al.  A histomorphometric study of unthreaded hydroxyapatite-coated and titanium-coated implants in rabbit bone. , 1992, The International journal of oral & maxillofacial implants.