Cellulose-Derived Highly Porous Three-Dimensional Activated Carbons for Supercapacitors

A novel “selective surface dissolution” (SSD) method was successfully utilized in previous research to prepare “all-polymer composites” aiming to structural applications. In the current study, this simple, cost-effective, and environmentally friendly method was employed for the first time to synthesize cellulose-derived highly porous three-dimensional (3D) activated carbon materials to assemble superior electrodes for supercapacitors. ZnCl2 aqueous solution was used to partially dissolve the surface of cellulose fibers. The partially dissolved cellulose I crystalline phase at the fiber surface can be consolidated into fibrillar cellulose polymorphs (e.g., cellulose II) which connects remaining fibers together. By a carefully controlled SSD method, a highly porous 3D cellulosic skeleton with interconnected bridge-like fibrillar linkages and hierarchical pore structures can be created. After carbonization, the 3D fiber construct with interconnected fibrillar linkages and hierarchical pore structures remains and highly porous activated carbons were obtained. The effects of various processing parameters (e.g., solvent concentration, immersion time, etc.) on the morphology of the as-formed activated porous carbons and their electrochemical performance as electrodes in supercapacitors were systematically investigated and discussed. It was concluded that the SSD method is a promising chemical approach to produce large-scale cellulose-derived activated porous carbons in an environmentally friendly manner.

[1]  T. Peijs,et al.  Effects of surface‐dissolution process multivariables on the morphology, mechanical properties, and crystallization of all‐aramid composites , 2018 .

[2]  T. Peijs,et al.  All‐aramid composites by partial fiber dissolution in mixed solvents , 2018 .

[3]  E. Liu,et al.  A high performance nitrogen-doped porous activated carbon for supercapacitor derived from pueraria , 2018 .

[4]  Bao-hang Han,et al.  Biomass-derived flexible porous carbon materials and their applications in supercapacitor and gas adsorption , 2017 .

[5]  R. Sun,et al.  Effects of Various Surfactants on Alkali Lignin Electrospinning Ability and Spun Fibers , 2017 .

[6]  Guoqing Zhang,et al.  Activated Carbon Fibers with Hierarchical Nanostructure Derived from Waste Cotton Gloves as High-Performance Electrodes for Supercapacitors , 2017, Nanoscale Research Letters.

[7]  R. Sun,et al.  Waste to wealth: A sustainable and flexible supercapacitor based on office waste paper electrodes , 2017 .

[8]  Carlos Alemán,et al.  Powering the future: application of cellulose-based materials for supercapacitors , 2016 .

[9]  Xinwen Peng,et al.  Sustainable hierarchical porous carbon aerogel from cellulose for high-performance supercapacitor and CO2 capture , 2016 .

[10]  Tong Lin,et al.  High-performance supercapacitor electrode from cellulose-derived, inter-bonded carbon nanofibers , 2016 .

[11]  A. Arof,et al.  Activated carbon from coconut leaves for electrical double-layer capacitor , 2016, Ionics.

[12]  S. Han,et al.  Natural Cellulose Materials for Supercapacitors , 2016 .

[13]  Yanfang Gao,et al.  Biomass-Swelling Assisted Synthesis of Hierarchical Porous Carbon Fibers for Supercapacitor Electrodes. , 2016, ACS applied materials & interfaces.

[14]  T. Peijs,et al.  High-performance liquid-crystalline polymer films for monolithic “composites” , 2016 .

[15]  B. Duchemin,et al.  All-cellulose composites based on microfibrillated cellulose and filter paper via a NaOH-urea solvent system , 2016, Cellulose.

[16]  Zhiguo Wang,et al.  Self-Reinforced Grease-Resistant Sheets Produced by Paper Treatment with Zinc Chloride Solution , 2015 .

[17]  Wei Zhao,et al.  Preparation of activated carbon hollow fibers from ramie at low temperature for electric double-layer capacitor applications. , 2013, Bioresource technology.

[18]  Satishchandra Ogale,et al.  From dead leaves to high energy density supercapacitors , 2013 .

[19]  K. Oksman,et al.  Self-reinforced nanocomposite by partial dissolution of cellulose microfibrils in ionic liquid , 2012 .

[20]  T. Peijs,et al.  Self-reinforced poly(ethylene terephthalate) composites by hot consolidation of Bi-component PET yarns , 2010 .

[21]  T. Peijs,et al.  All-aramid composites by partial fiber dissolution. , 2010, ACS applied materials & interfaces.

[22]  T. Peijs,et al.  All-poly(ethylene terephthalate) composites by film stacking of oriented tapes , 2009 .

[23]  Y. Gogotsi,et al.  Materials for electrochemical capacitors. , 2008, Nature materials.

[24]  T. Peijs,et al.  All-cellulose composites by surface selective dissolution of aligned ligno-cellulosic fibres , 2008 .

[25]  T. Nishino,et al.  All-cellulose composite prepared by selective dissolving of fiber surface. , 2007, Biomacromolecules.

[26]  Ki Chul Park,et al.  Preparation and characterization of bamboo-based activated carbons as electrode materials for electric double layer capacitors , 2006 .

[27]  Ton Peijs,et al.  Processing of all-polypropylene composites for ultimate recyclability , 2004 .

[28]  I. Ward,et al.  The science and technology of hot compaction , 2004 .

[29]  Ton Peijs,et al.  Composites for recyclability , 2003 .

[30]  N. Capiati,et al.  The concept of one polymer composites modelled with high density polyethylene , 1975 .

[31]  B. Alcock,et al.  Technology and Development of Self-Reinforced Polymer Composites , 2011 .

[32]  I. Ward,et al.  The hot compaction of high modulus melt-spun polyethylene fibres , 1993 .