In situ surface modification of TiO2 by CaTiO3 to improve the UV stability and power conversion efficiency of perovskite solar cells

The usage of TiO2 in perovskite solar cells is always faced with the risk of device decomposition due to its high photocatalysis activity. To deal with this problem, here in this work, a strategy of in situ surface passivation was proposed and performed on TiO2. After spin-coating Ca(OH)2 solution on a TiO2 mesoporous scaffold and annealing, the surface layer of the scaffold was converted into CaTiO3, as confirmed by X-ray photoemission spectroscopy and X-ray diffraction studies. The modified TiO2 scaffold was then used as an electron-transport-material in perovskite solar cells. It was observed that after moderate modification, the short-circuit current density increased from 22.32 (±0.25) to 23.19 (±0.28) mA/cm2, the open-circuit voltage rose from 1.042 (±0.009) to 1.080 (±0.011) V, and the fill factor increased from 63.89 (±1.95)% to 71.37 (±0.43)%, leading to an improvement from 14.92 (±0.36)% to 17.88 (±0.37)% of the power conversion efficiency. Transient photocurrent/photovoltage decay curves and impedance spectroscopy tests showed that moderate modification accelerated charge extraction while it retarded charge recombination. Besides, the in situ CaTiO3 layer prolonged the device stability. After being stored in the dark for 46 days (relative humidity of 30%), 92.6% of the initial efficiency was reserved, compared to that of 68.4% for the control devices. Designated UV irradiation showed that the surface passivation retarded the photocatalysis activity of TiO2, which contributed to the prolonged device stability.The usage of TiO2 in perovskite solar cells is always faced with the risk of device decomposition due to its high photocatalysis activity. To deal with this problem, here in this work, a strategy of in situ surface passivation was proposed and performed on TiO2. After spin-coating Ca(OH)2 solution on a TiO2 mesoporous scaffold and annealing, the surface layer of the scaffold was converted into CaTiO3, as confirmed by X-ray photoemission spectroscopy and X-ray diffraction studies. The modified TiO2 scaffold was then used as an electron-transport-material in perovskite solar cells. It was observed that after moderate modification, the short-circuit current density increased from 22.32 (±0.25) to 23.19 (±0.28) mA/cm2, the open-circuit voltage rose from 1.042 (±0.009) to 1.080 (±0.011) V, and the fill factor increased from 63.89 (±1.95)% to 71.37 (±0.43)%, leading to an improvement from 14.92 (±0.36)% to 17.88 (±0.37)% of the power conversion efficiency. Transient photocurrent/photovoltage decay curves and im...

[1]  H. Tao,et al.  Performance enhancement of perovskite solar cells with Mg-doped TiO2 compact film as the hole-blocking layer , 2015 .

[2]  Yoshikazu Suzuki,et al.  Mesoporous BaTiO3/TiO2 Double Layer for Electron Transport in Perovskite Solar Cells , 2016 .

[3]  Yongli Gao,et al.  Accelerated electron extraction and improved UV stability of TiO2 based perovskite solar cells by SnO2 based surface passivation , 2018, Organic Electronics.

[4]  Z. Yin,et al.  Enhanced electron extraction using SnO2 for high-efficiency planar-structure HC(NH2)2PbI3-based perovskite solar cells , 2016, Nature Energy.

[5]  Thomas Riedl,et al.  Inverted Organic Solar Cells with Sol–Gel Processed High Work‐Function Vanadium Oxide Hole‐Extraction Layers , 2011 .

[6]  Sandeep Kumar Pathak,et al.  Enhanced Efficiency and Stability of Perovskite Solar Cells Through Nd‐Doping of Mesostructured TiO2 , 2016 .

[7]  Seigo Ito,et al.  Effects of Surface Blocking Layer of Sb2S3 on Nanocrystalline TiO2 for CH3NH3PbI3 Perovskite Solar Cells , 2014 .

[8]  K. Yeung,et al.  EPR Study of the Surface Characteristics of Nanostructured TiO2 under UV Irradiation , 2001 .

[9]  Jing Li,et al.  Stacking n-type layers: Effective route towards stable, efficient and hysteresis-free planar perovskite solar cells , 2018 .

[10]  Yongli Gao,et al.  Dependence of power conversion properties of perovskite solar cells on operating temperature , 2018, Applied Physics Letters.

[11]  Henry J. Snaith,et al.  Enhanced UV-light stability of planar heterojunction perovskite solar cells with caesium bromide interface modification , 2016 .

[12]  Michael Grätzel,et al.  Porphyrin-Sensitized Solar Cells with Cobalt (II/III)–Based Redox Electrolyte Exceed 12 Percent Efficiency , 2011, Science.

[13]  P. Homola,et al.  Improving dielectric properties of plasma sprayed calcium titanate (CaTiO3) coatings by thermal annealing , 2014 .

[14]  N. Yuan,et al.  Enhanced UV-light stability of organometal halide perovskite solar cells with interface modification and a UV absorption layer , 2017 .

[15]  Yongli Gao,et al.  Stable monolithic hole-conductor-free perovskite solar cells using TiO2 nanoparticle binding carbon films , 2017 .

[16]  Young Chan Kim,et al.  Compositional engineering of perovskite materials for high-performance solar cells , 2015, Nature.

[17]  Min Liu,et al.  Hierarchical TiO2 spheres: facile fabrication and enhanced photocatalysis , 2011 .

[18]  G. Fang,et al.  Efficient and Stable Nonfullerene‐Graded Heterojunction Inverted Perovskite Solar Cells with Inorganic Ga2O3 Tunneling Protective Nanolayer , 2018, Advanced Functional Materials.

[19]  Ruixia Yang,et al.  Hysteresis‐Suppressed High‐Efficiency Flexible Perovskite Solar Cells Using Solid‐State Ionic‐Liquids for Effective Electron Transport , 2016, Advanced materials.

[20]  H. G. Kim,et al.  Photocatalytic Hydrogen Production in Water-Methanol Mixture over Iron-doped CaTiO3 , 2011 .

[21]  J. Liang,et al.  Dye-sensitized solar cells made from BaTiO3-coated TiO2 nanoporous electrodes , 2008 .

[22]  M. Grätzel,et al.  A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 films , 1991, Nature.

[23]  M. Maeda,et al.  CaTiO3 nanobricks prepared from anodized TiO2 nanotubes , 2012 .

[24]  Yongli Gao,et al.  Irreversible light-soaking effect of perovskite solar cells caused by light-induced oxygen vacancies in titanium oxide , 2017 .

[25]  Hyunwoong Park,et al.  Surface modification of TiO2 photocatalyst for environmental applications , 2013 .

[26]  F. Giordano,et al.  Enhanced electronic properties in mesoporous TiO2 via lithium doping for high-efficiency perovskite solar cells , 2016, Nature Communications.

[27]  Yongli Gao,et al.  Dependence of power conversion properties of hole-conductor-free mesoscopic perovskite solar cells on the loading of perovskite crystallites , 2018, Organic Electronics.

[28]  Yongli Gao,et al.  Dependence of power conversion properties of the hole-conductor-free mesoscopic perovskite solar cells on the thickness of carbon film , 2018, Organic Electronics.

[29]  Mohammad Khaja Nazeeruddin,et al.  Conversion of light to electricity by cis-X2bis(2,2'-bipyridyl-4,4'-dicarboxylate)ruthenium(II) charge-transfer sensitizers (X = Cl-, Br-, I-, CN-, and SCN-) on nanocrystalline titanium dioxide electrodes , 1993 .

[30]  Yoshikazu Suzuki,et al.  Perovskite-type SrTiO3, CaTiO3 and BaTiO3 porous film electrodes for dye-sensitized solar cells , 2014 .

[31]  Sandeep Kumar Pathak,et al.  Overcoming ultraviolet light instability of sensitized TiO2 with meso-superstructured organometal tri-halide perovskite solar cells , 2013, Nature Communications.

[32]  M. Grätzel,et al.  A hole-conductor–free, fully printable mesoscopic perovskite solar cell with high stability , 2014, Science.

[33]  B. Li,et al.  TiO2 surface modification and characterization with nanosized PbS in dye-sensitized solar cells. , 2006, The journal of physical chemistry. B.