A phase inversion/sintering process to fabricate nickel/yttria-stabilized zirconia hollow fibers as the anode support for micro-tubular solid oxide fuel cells

Abstract NiO/YSZ hollow fibers were fabricated via a combined phase inversion and sintering technique, where polyethersulfone (PESf) was employed as the polymeric binder, N-methyl-2-pyrrolidone (NMP) as the solvent and polyvinylpyrrolidone (PVP) as the additive, respectively. After reduction with hydrogen at 750 °C for 5 h, the porous Ni/YSZ hollow fibers with an asymmetric structure comprising of a microporous layer integrated with a finger-like porous layer were obtained, which can be served as the anode support of micro-tubular solid oxide fuel cells (SOFCs). As the sintering temperature was increased from 1200 to 1400 °C, the mechanical strength and the electrical conductivity of the Ni/YSZ hollow fibers increased from 35 to 178 MPa and from 30 to 772 S cm−1, respectively but the porosity decreased from 64.2% to 37.0%. The optimum sintering temperature was found to be between 1350 and 1400 °C for Ni/YSZ hollow fibers applied as the anode support for micro-tubular SOFCs.

[1]  X. Tan,et al.  Preparation and characterization of inorganic hollow fiber membranes , 2001 .

[2]  T. Young,et al.  Pore formation mechanism of membranes from phase inversion process , 1995 .

[3]  N. Sammes,et al.  Design and fabrication of a 100 W anode supported micro-tubular SOFC stack , 2005 .

[4]  M. Mori,et al.  Fabrication and characterization of micro-tubular cathode-supported SOFC for intermediate temperature operation , 2007 .

[5]  Alois Kessler,et al.  Stationary fuel cells—Results of 2 years of operation at EnBW , 2006 .

[6]  P. Schaetzel,et al.  Formation and morphology studies of different polysulfones-based membranes made by wet phase inversion process , 2006 .

[7]  E. Traversa,et al.  Electrical properties of YSZ/NiO composites prepared by a liquid mixture technique , 2005 .

[8]  D. Dong,et al.  Fabrication of tubular NiO/YSZ anode-support of solid oxide fuel cell by gelcasting , 2007 .

[9]  N. Sammes,et al.  Fabrication and properties of anode-supported tubular solid oxide fuel cells , 2004 .

[10]  T. Matsuura,et al.  Study on the effect of spinning conditions and surface treatment on the geometry and performance of polymeric hollow-fibre membranes , 1995 .

[11]  Yoshinobu Fujishiro,et al.  Fabrication and characterization of components for cube shaped micro tubular SOFC bundle , 2007 .

[12]  G. J. Saunders,et al.  Reactions of hydrocarbons in small tubular SOFCs , 2002 .

[13]  Toshiaki Yamaguchi,et al.  Fabrication and characterization of micro tubular SOFCs for advanced ceramic reactors , 2008 .

[14]  X. Tan,et al.  Theoretical analysis of ion permeation through mixed conducting membranes and its application to dehydrogenation reactions , 2000 .

[15]  S. Linderoth,et al.  Interaction of NiO with yttria-stabilized zirconia , 1997 .

[16]  Toshio Suzuki,et al.  Fabrication and evaluation of cathode-supported small scale SOFCs , 2008 .

[17]  Toshiaki Yamaguchi,et al.  Fabrication and characterization of micro tubular SOFCs for operation in the intermediate temperature , 2006 .

[18]  Toshiaki Yamaguchi,et al.  Anode-supported micro tubular SOFCs for advanced ceramic reactor system , 2007 .

[19]  J. P. Strakey,et al.  U.S. DOE fossil energy fuel cells program , 2006 .

[20]  Zi Gu,et al.  Catalytic perovskite hollow fibre membrane reactors for methane oxidative coupling , 2007 .

[21]  Nigel M. Sammes,et al.  Fracture strength of micro-tubular solid oxide fuel cell anode in redox cycling experiments , 2007 .

[22]  Toshiaki Yamaguchi,et al.  Current collecting efficiency of micro tubular SOFCs , 2007 .