Optimization of the isolation of nanocrystals from microcrystalline cellulose by acid hydrolysis

The objective of this work was to find a rapid, high-yield process to obtain an aqueous stable colloid suspension of cellulose nanocrystals/whiskers. Large quantities are required since these whiskers are designed to be extruded into polymers in the production of nano-biocomposites. Microcrystalline cellulose (MCC), derived from Norway spruce (Picea abies), was used as the starting material. The processing parameters have been optimized by using response surface methodology. The factors that varied during the process were the concentration of MCC and sulfuric acid, the hydrolysis time and temperature, and the ultrasonic treatment time. Responses measured were the median size of the cellulose particles/whiskers and yield. The surface charge as calculated from conductometric titration, microscopic examinations (optical and transmission electron microscopy), and observation of birefringence were also investigated in order to determine the outcome (efficiency) of the process. With a sulfuric acid concentration of 63.5% (w/w), it was possible to obtain cellulose nanocrystals/whiskers with a length between 200 and 400 nm and a width less than 10 nm in approximately 2 h with a yield of 30% (of initial weight).

[1]  R. Herzog,et al.  Röntgenspektrographischer Vergleich von Tunicin und Lichenin mit Zellulose. , 1924 .

[2]  H. J. Woods,et al.  X-ray and electron microscope studies of the degradation of cellulose by sulphuric acid. , 1953, Biochimica et biophysica acta.

[3]  Takeshi Okano,et al.  Flow properties of microcrystalline cellulose suspension prepared by acid treatment of native cellulose , 1998 .

[4]  D G Gray,et al.  Helicoidal self-ordering of cellulose microfibrils in aqueous suspension. , 1992, International journal of biological macromolecules.

[5]  Alain Dufresne,et al.  Thermoplastic nanocomposites filled with wheat straw cellulose whiskers. Part I: Processing and mechanical behavior , 1996 .

[6]  A. Dufresne,et al.  Plasticized Starch/Tunicin Whiskers Nanocomposites. 1. Structural Analysis , 2000 .

[7]  F. Morehead,et al.  Some hydrodynamic properties of neutral suspensions of cellulose crystallites as related to size and shape , 1961 .

[8]  R. Beatson,et al.  The determination of strong and weak acidic groups in sulfite pulps , 1984 .

[9]  M. Roman,et al.  Effect of reaction conditions on the properties and behavior of wood cellulose nanocrystal suspensions. , 2005, Biomacromolecules.

[10]  F. Morehead,et al.  Liquid Crystal Systems from Fibrillar Polysaccharides , 1959, Nature.

[11]  Véronique Favier,et al.  Polymer Nanocomposites Reinforced by Cellulose Whiskers , 1995 .

[12]  Masamichi Kobayashi,et al.  THEORETICAL EVALUATION OF THREE-DIMENSIONAL ELASTIC CONSTANTS OF NATIVE AND REGENERATED CELLULOSES : ROLE OF HYDROGEN BONDS , 1991 .

[13]  D. Gray,et al.  Influence of dextran on the phase behavior of suspensions of cellulose nanocrystals , 2002 .

[14]  Takeshi Okano,et al.  Birefringent Glassy Phase of a Cellulose Microcrystal Suspension , 2000 .

[15]  William J. Orts,et al.  Enhanced Ordering of Liquid Crystalline Suspensions of Cellulose Microfibrils: A Small Angle Neutron Scattering Study , 1998 .

[16]  R. F. Nickerson,et al.  Cellulose Intercrystalline Structure , 1947 .

[17]  D. Gray,et al.  Effect of microcrystallite preparation conditions on the formation of colloid crystals of cellulose , 1998 .

[18]  S. Eichhorn,et al.  Elastic modulus and stress-transfer properties of tunicate cellulose whiskers. , 2005, Biomacromolecules.

[19]  Stephen J. Eichhorn,et al.  The Young's modulus of a microcrystalline cellulose , 2001 .