Calcium silicate ceramic scaffolds toughened with hydroxyapatite whiskers for bone tissue engineering

Abstract Calcium silicate possessed excellent biocompatibility, bioactivity and degradability, while the high brittleness limited its application in load-bearing sites. Hydroxyapatite whiskers ranging from 0 to 30 wt.% were incorporated into the calcium silicate matrix to improve the strength and fracture resistance. Porous scaffolds were fabricated by selective laser sintering. The effects of hydroxyapatite whiskers on the mechanical properties and toughening mechanisms were investigated. The results showed that the scaffolds had a uniform and continuous inner network with the pore size ranging between 0.5 mm and 0.8 mm. The mechanical properties were enhanced with increasing hydroxyapatite whiskers, reached a maximum at 20 wt.% (compressive strength: 27.28 MPa, compressive Young's modulus: 156.2 MPa, flexural strength: 15.64 MPa and fracture toughness: 1.43 MPa·m1/2) and then decreased by addition of more hydroxyapatite whiskers. The improvement of mechanical properties was due to whisker pull-out, crack deflection and crack bridging. Moreover, the degradation rate decreased with the increase of hydroxyapatite whisker content. A layer of bone-like apatite was formed on the scaffold surfaces after being soaked in simulated body fluid. Human osteoblast-like MG-63 cells spread well on the scaffolds and proliferated with increasing culture time. These findings suggested that the calcium silicate scaffolds reinforced with hydroxyapatite whiskers showed great potential for bone regeneration and tissue engineering applications.

[1]  S. Dorozhkin,et al.  Nanosized and nanocrystalline calcium orthophosphates. , 2010, Acta biomaterialia.

[2]  Fumio Watari,et al.  Biocomposites reinforced by fibers or tubes as scaffolds for tissue engineering or regenerative medicine. , 2014, Journal of biomedical materials research. Part A.

[3]  E. Bernardo,et al.  Wollastonite Foams From an Extruded Preceramic Polymer Mixed with CaCO3 Microparticles Assisted by Supercritical Carbon Dioxide , 2013 .

[4]  Shiqing Xu,et al.  Effects of Al2O3 addition on the sintering behavior and microwave dielectric properties of CaSiO3 ceramics , 2012 .

[5]  G. El-Bassyouni,et al.  Mechanical and microstructure of reinforced hydroxyapatite/calcium silicate nano-composites materials , 2013 .

[6]  Robert J. Kane,et al.  Effects of the reinforcement morphology on the fatigue properties of hydroxyapatite reinforced polymers. , 2008, Journal of the mechanical behavior of biomedical materials.

[7]  Chengtie Wu,et al.  Improvement of mechanical and biological properties of porous CaSiO3 scaffolds by poly(D,L-lactic acid) modification. , 2008, Acta biomaterialia.

[8]  Xiaohong Li,et al.  Degradation behaviors of electrospun fibrous composites of hydroxyapatite and chemically modified poly(dl-lactide) , 2011 .

[9]  F. Lin,et al.  Thermal decomposition and reconstitution of hydroxyapatite in air atmosphere. , 1999, Biomaterials.

[10]  Bin Duan,et al.  Three-dimensional nanocomposite scaffolds fabricated via selective laser sintering for bone tissue engineering. , 2010, Acta biomaterialia.

[11]  M. A. Fanovich,et al.  Influence of temperature and additives on the microstructure and sintering behaviour of hydroxyapatites with different Ca/P ratios , 1998, Journal of materials science. Materials in medicine.

[12]  J. Tanaka,et al.  Composition and structure of apatite formed on organic polymer in simulated body fluid with a high content of carbonate ion , 2000, Journal of materials science. Materials in medicine.

[13]  T Kitsugi,et al.  Ca,P-rich layer formed on high-strength bioactive glass-ceramic A-W. , 1990, Journal of biomedical materials research.

[14]  J Ciurana,et al.  The first systematic analysis of 3D rapid prototyped poly(ε-caprolactone) scaffolds manufactured through BioCell printing: the effect of pore size and geometry on compressive mechanical behaviour and in vitro hMSC viability , 2013, Biofabrication.

[15]  A. A. Zadpoor.  Relationship between in vitro apatite-forming ability measured using simulated body fluid and in vivo bioactivity of biomaterials. , 2014, Materials science & engineering. C, Materials for biological applications.

[16]  S. Ding,et al.  Bio-inspired calcium silicate–gelatin bone grafts for load-bearing applications , 2011 .

[17]  Ran Liu,et al.  In situ formation of nano-hydroxyapatite whisker reinfoced porous β-TCP scaffolds , 2012 .

[18]  S. Ushakov,et al.  Phase Transformations and Melt Structure of Calcium Metasilicate , 2002 .

[19]  Robert J. Kane,et al.  Effects of hydroxyapatite reinforcement on the architecture and mechanical properties of freeze-dried collagen scaffolds. , 2012, Journal of the mechanical behavior of biomedical materials.

[20]  N. A. Abu Osman,et al.  Mechanical and physical properties of calcium silicate/alumina composite for biomedical engineering applications. , 2014, Journal of the mechanical behavior of biomedical materials.

[21]  T. Guda,et al.  Influence of substrate curvature on osteoblast orientation and extracellular matrix deposition , 2013, Journal of biological engineering.

[22]  Jiang Chang,et al.  Preparation, mechanical properties and in vitro degradability of wollastonite/tricalcium phosphate macroporous scaffolds from nanocomposite powders , 2008, Journal of materials science. Materials in medicine.

[23]  Ryan B. Wicker,et al.  Fused deposition modeling of patient‐specific polymethylmethacrylate implants , 2010 .

[24]  M. Mehmood,et al.  Effect of CTAB Addition on Improvement of Properties of Al2O3(w)–Al2O3(n)–ZrO2(n) (3mole% Yttria Stabilized Tetragonal Zirconia) Nanocomposite , 2012 .

[25]  E. A. Charles,et al.  Fracture Toughness Determinations by Indentation , 1976 .

[26]  Zhou Fang,et al.  In-situ grown hydroxyapatite whiskers reinforced porous HA bioceramic , 2013 .

[27]  M. Kakihana,et al.  Hydroxyapatite/Hydroxyapatite‐Whisker Composites without Sintering Additives: Mechanical Properties and Microstructural Evolution , 1997 .

[28]  F. Müller,et al.  Whisker‐Reinforced Calcium Phosphate Cements , 2007 .

[29]  Jianqiang Wei,et al.  Microstructure and mechanical properties of CaCO3 whisker-reinforced cement , 2011 .

[30]  Si-yu Ni,et al.  A novel bioactive porous CaSiO3 scaffold for bone tissue engineering. , 2006, Journal of biomedical materials research. Part A.

[31]  Si-yu Ni,et al.  Comparison of osteoblast-like cell responses to calcium silicate and tricalcium phosphate ceramics in vitro. , 2007, Journal of biomedical materials research. Part B, Applied biomaterials.

[32]  M. Khorasani,et al.  Synthesis methods for nanosized hydroxyapatite with diverse structures. , 2013, Acta biomaterialia.

[33]  F. Oliveira,et al.  SiC whisker reinforced multi-carbides composites prepared from B4C and pyrolyzed rice husks via reactive infiltration , 2012 .

[34]  Hala Zreiqat,et al.  The incorporation of strontium and zinc into a calcium-silicon ceramic for bone tissue engineering. , 2010, Biomaterials.

[35]  V. Rangari,et al.  Carbon nanoparticles/whiskers reinforced composites and their tensile response , 2003 .

[36]  S. Teoh,et al.  In vitro degradation of novel bioactive polycaprolactone—20% tricalcium phosphate composite scaffolds for bone engineering , 2007 .

[37]  R. Roeder,et al.  Processing and tensile properties of hydroxyapatite-whisker-reinforced polyetheretherketone. , 2007, Biomaterials.

[38]  S. Kim,et al.  Observation of Toughness Improvement of the Hydroxyapatite Bioceramics Densified Using High-Frequency Induction Heat Sintering , 2007 .

[39]  M. Teshima,et al.  Tape-cast and sintered β-tricalcium phosphate laminates for biomedical applications: Effect of milled Al2O3 fiber additives on microstructural and mechanical properties. , 2012, Journal of biomedical materials research. Part B, Applied biomaterials.

[40]  C. Shuai,et al.  Optimization of TCP/HAP ratio for better properties of calcium phosphate scaffold via selective laser sintering , 2013 .

[41]  P. D. de Oliveira,et al.  Pore size regulates cell and tissue interactions with PLGA–CaP scaffolds used for bone engineering , 2012, Journal of tissue engineering and regenerative medicine.

[42]  A. Bandyopadhyay,et al.  Mesoporous calcium silicate for controlled release of bovine serum albumin protein. , 2009, Acta biomaterialia.

[43]  A. Sannino,et al.  Wollastonite/hydroxyapatite scaffolds with improved mechanical, bioactive and biodegradable properties for bone tissue engineering , 2013 .

[44]  Si-yu Ni,et al.  In vitro Degradation, Bioactivity, and Cytocompatibility of Calcium Silicate, Dimagnesium Silicate, and Tricalcium Phosphate Bioceramics , 2009, Journal of biomaterials applications.

[45]  B. Darvell,et al.  Synthesis and characterization of hydroxyapatite whiskers by hydrothermal homogeneous precipitation using acetamide. , 2010, Acta biomaterialia.

[46]  Jie Yuan,et al.  Effect of ZnO whisker content on sinterability and fracture behaviour of PZT peizoelectric composites , 2010 .

[47]  B. Darvell,et al.  Mechanical properties of hydroxyapatite whisker-reinforced bis-GMA-based resin composites. , 2012, Dental materials : official publication of the Academy of Dental Materials.

[48]  Jiang Chang,et al.  The calcium silicate/alginate composite: preparation and evaluation of its behavior as bioactive injectable hydrogels. , 2013, Acta biomaterialia.

[49]  K. Leong,et al.  Solid freeform fabrication of three-dimensional scaffolds for engineering replacement tissues and organs. , 2003, Biomaterials.

[50]  T. Furuzono,et al.  Hydroxylapatite nanoparticles: fabrication methods and medical applications , 2012, Science and technology of advanced materials.

[51]  Jisoo Shin,et al.  Preparation and characterization of bioactive calcium silicate and poly(epsilon-caprolactone) nanocomposite for bone tissue regeneration. , 2009, Journal of biomedical materials research. Part A.

[52]  Yinghong Zhou,et al.  3D-printing of highly uniform CaSiO3 ceramic scaffolds: preparation, characterization and in vivo osteogenesis , 2012 .

[53]  Jukka Seppälä,et al.  Biodegradable and bioactive porous scaffold structures prepared using fused deposition modeling. , 2013, Journal of biomedical materials research. Part B, Applied biomaterials.

[54]  D. Mantovani,et al.  Spontaneous and Biomimetic Apatite Formation on Pure Magnesium , 2007 .