Foaming of PS/wood fiber composites using moisture as a blowing agent

This paper presents an experimental study on foam processing of polystyrene (PS) and high-impact polystyrene HIPS/wood-fiber composites in extrusion using moisture as a blowing agent. Wood-fiber inherently contains moisture that can potentially be used as a blowing agent. Undried wood-fiber was processed together with PS and HIPS materials in extrusion and wood-fiber composite foams were produced. The cellular morphology and volume expansion ratios of the foamed composites were characterized. Because of the high stiffness of styrenic materials, moisture condensation during cooling after expansion at high temperature did not cause much contraction of the foamed composite and a high volume expansion ratio up to 20 was successfully obtained. The experimental results showed that the expansion ratio could be controlled by varying the processing temperature and the moisture content in the wood fiber. The effects of a small amount of a chemical blowing agent and mineral oil on the cell morphologies of plastic/wood-fiber composite foams were also investigated.

[1]  Chul B. Park,et al.  Cell morphology and property relationships of microcellular foamed pvc/wood‐fiber composites , 1998 .

[2]  R. D. Venter,et al.  Low density microcellular foam processing in extrusion using CO2 , 1998 .

[3]  Chul B. Park,et al.  Influence of interfacial interactions on the properties of PVC/cellulosic fiber composites , 1998 .

[4]  Chul B. Park,et al.  Effect of surface properties on the adhesion between PVC and wood veneer laminates , 1998 .

[5]  Chul B. Park,et al.  Microcellular sheet extrusion system process design models for shaping and cell growth control , 1998 .

[6]  R. D. Venter,et al.  Challenge to the production of low-density, fine-cell HDPE foams using CO2 , 1998 .

[7]  Chul B. Park,et al.  The effect of low levels of plasticizer on the rheological and mechanical properties of polyvinyl chloride/newsprint‐fiber composites , 1997 .

[8]  Chul B. Park,et al.  Processing and cell morphology relationships for microcellular foamed PVC/wood-fiber composites , 1997 .

[9]  J. Balatinecz,et al.  Effects of Wood Fiber Surface Chemistry on the Mechanical Properties of Wood Fiber-Polypropylene Composites , 1997 .

[10]  R. D. Venter,et al.  Extrusion of polypropylene foams with hydrocerol and isopentane , 1996 .

[11]  G. Campbell,et al.  The heterogeneous nucleation of microcellular foams assisted by the survival of microvoids in polymers containing low glass transition particles. Part II: Experimental results and discussion , 1994 .

[12]  John J. Balatinecz,et al.  Wood-Plastic Composites: Doing More with Less , 1993 .

[13]  R. Geimer,et al.  Density Range of Compression-Molded Polypropylene-Wood Composites , 1993 .

[14]  Alan A. Marra,et al.  Technology of Wood Bonding : Principles in Practice , 1992 .

[15]  B. Kokta,et al.  Studies on mechanical properties of polyethylene–organic fiber composites. I. Nut shell flour , 1992 .

[16]  B. Riedl,et al.  Reinforcement of Recycled Polyolefins with Wood Fibers , 1992 .

[17]  C. A. Coberly,et al.  Wood Flour/Polypropylene Composites: Influence of Maleated Polypropylene and Process and Composition Variables on Mechanical Properties , 1991 .

[18]  B. Kokta,et al.  Composites of polyvinyl chloride–wood fibers. III: Effect of silane as coupling agent , 1990 .

[19]  B. Kokta,et al.  Composites of polyvinyl chloride—wood fibers: IV. Effect of the nature of fibers , 1989 .

[20]  G. Thomas,et al.  Wood fibers as reinforcing fillers for polyolefins , 1984 .