Mix design of concrete with high content of mineral additions: Optimisation to improve early age strength

The concrete industry is an important source of CO2 gas emissions. The cement used in the design of concrete is the result of a chemical process linked to the decarbonation of limestone conducted at high temperature and results in a significant release of carbon dioxide. Under the project EcoBeton (Green concrete) funded by the French National Research Agency (ANR), concrete mixtures have been designed with a low cement quantity, by replacing cement by mineral additions i.e., blast-furnace slag, fly ash or limestone fillers. Replacement of cement by other materials at high percentages generally lowers the early age strength of the resulting concrete. To cope with this problem, an optimisation method for mix design of concrete using Bolomey's law has been used. Following the encouraging results obtained from mortar, a series of tests on concretes with various substitution percentages were carried out to validate the optimisation method.

[1]  Michael D.A. Thomas,et al.  The effect of fly ash composition on the expansion of concrete due to alkali-silica reaction , 2000 .

[2]  J. Bijen.  Benefits of slag and fly ash , 1996 .

[3]  C. Poon,et al.  Degree of hydration and gel/space ratio of high-volume fly ash/cement systems , 2000 .

[4]  M. Lachemi,et al.  LONG-TERM PERFORMANCE OF SILICA FUME CONCRETES , 1998 .

[5]  P. Taylor,et al.  Sulfate Resistance of Concrete Using Blended Cements or Supplementary Cementitious Materials , 2006 .

[6]  Ahmed Loukili,et al.  A performance based approach for durability of concrete exposed to carbonation , 2009 .

[7]  Dongxu Li,et al.  The influence of alkalinity on activation and microstructure of fly ash , 2000 .

[8]  Luc Taerwe,et al.  Influence of limestone powder used as filler in SCC on hydration and microstructure of cement pastes , 2007 .

[9]  Xiaozhong Wu,et al.  Influence of fly ash and its mean particle size on certain engineering properties of cement composite mortars , 2005 .

[10]  V M Malhotra,et al.  High-volume fly ash system : The concrete solution for sustainable development , 2000 .

[11]  Konstantin Sobolev,et al.  The development of a new method for the proportioning of high-performance concrete mixtures , 2004 .

[12]  T. L. Brownyard,et al.  Studies of the Physical Properties of Hardened Portland Cement Paste , 1946 .

[13]  Norbert J. Delatte,et al.  Effect of supplementary cementitious materials on the compressive strength and durability of short-term cured concrete , 2004 .

[14]  Thierry Sedran,et al.  Mixture-proportioning of high-performance concrete , 2002 .

[15]  V. Malhotra.  Fly Ash, Slag, Silica Fume, and Rice Husk Ash in Concrete: A Review , 1993 .

[16]  Wei Chen,et al.  Hydration of slag cement: theory, modeling and application , 2006 .

[17]  Steve Millard,et al.  Strength development of mortars containing ground granulated blast-furnace slag: Effect of curing temperature and determination of apparent activation energies , 2006 .

[19]  R. Dhir,et al.  Development of high volume fly ash cements for use in concrete construction , 2005 .

[20]  Xinghua Fu,et al.  Studies on high-strength slag and fly ash compound cement , 2000 .

[21]  F de Larrard,et al.  A METHOD FOR PROPORTIONING HIGH-STRENGTH CONCRETE MIXTURES , 1990 .

[22]  Konstantin Sobolev,et al.  Mechano-chemical modification of cement with high volumes of blast furnace slag , 2005 .

[23]  Dubravka Bjegović,et al.  Role of mineral additions in reducing CO2 emission , 2005 .

[24]  C. Poon,et al.  A study on high strength concrete prepared with large volumes of low calcium fly ash , 2000 .

[25]  Peter Fritzson,et al.  Modeling and Applications , 2004 .