A universal relation for edge chipping from sharp contacts in brittle materials: A simple means of toughness evaluation

An analysis of chipping fracture in brittle solids is presented. Cracks are introduced into the edges of selected materials, including soda-lime glass and fine-grain ceramics, using a Vickers indenter in monotonic loading. The ensuing chip morphology is examined and shown to exhibit a certain geometrical similarity, independent of material properties. A simple universal relation is derived for the critical chipping load in terms of indent location and material toughness. It is suggested that the method could be used as a simple and quick means for evaluating toughness values for glasses and fine-grain brittle materials.

[1]  R. Morrell,et al.  Edge chipping of hard materials , 2001 .

[2]  Brian R. Lawn,et al.  A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I , 1981 .

[3]  Brian Cotterell,et al.  The essential mechanics of conchoidal flaking , 1985 .

[4]  A. Evans,et al.  Fracture Mechanics of Ceramics , 1986 .

[5]  J. Quinn,et al.  “EDGE TOUGHNESS” AND MATERIAL PROPERTIES RELATED TO THE MACHINING OF DENTAL CERAMICS , 2000 .

[6]  M. D. Thouless,et al.  An analysis of Chipping in Brittle Materials , 1998 .

[7]  F. Guiberteau.  Indentation fatigue : a simple cyclic Hertzian test for measuring damage accumulation in polycrystalline ceramics , 1993 .

[8]  A. Evans,et al.  Elastic/Plastic Indentation Damage in Ceramics: The Median/Radial Crack System , 1980 .

[9]  B. Lawn,et al.  Hardness, Toughness, and Brittleness: An Indentation Analysis , 1979 .

[10]  Michael V. Swain,et al.  Microfracture beneath point indentations in brittle solids , 1975 .

[11]  N. McCormick,et al.  Constant-geometry edge-flaking of brittle materials , 1986, Nature.

[12]  Brian R. Lawn,et al.  Residual stress effects in sharp contact cracking , 1979 .

[13]  B. Lawn,et al.  A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: II, Strength Method , 1981 .

[14]  M. D. Thouless,et al.  The edge cracking and spalling of brittle plates , 1987 .

[15]  S. Jahanmir.  TRIBOLOGY ISSUES IN MACHINING , 1998 .

[16]  J. E. Ritter,et al.  Behavior of indentation cracks near free surfaces and interfaces , 1990 .

[17]  R. Morrell.  Edge Flaking - Similarity between Quasistatic Indentation and Impact Mechanisms for Brittle Materials , 2005 .

[18]  E. Fuller,et al.  Equilibrium penny-like cracks in indentation fracture , 1975 .

[19]  J. Varner,et al.  Fractography of Glasses and Ceramics II , 1991 .

[20]  Y. Mai,et al.  Crack‐Interface Grain Bridging as a Fracture Resistance I, Mechanism in Ceramics: I, Experimental Study on Alumina , 1987 .

[21]  G. Gogotsi.  Fracture toughness testing of materials by the EF method , 2006 .

[22]  S. Wiederhorn,et al.  Stress Corrosion and Static Fatigue of Glass , 1970 .

[23]  Brian R. Lawn,et al.  Failuer of fused silica fibers with subthreshold flaws , 1988 .

[24]  S. Scieszka.  Edge failure as a means of concurrently estimating the abrasion and edge fracture resistance of hard-metals , 2005 .