The relation between the defect hardening resulting from the deviation of composition and the exclusive substitutional solution hardening in the intermetallic compound Ni3Al is investigated by comparing the variation of lattice parameter and shear modulus with the change of compressive yield stress. In either case, the hardening rates are expressed by Fleischer's parameter in consideration of both effects, namely the elastic interaction between dislocations and solute atoms. Consequently, it is concluded that the defect hardening in Ni3Al is to be regarded as a sort of a substitutional solution hardening, and both hardening effects are controlled by the same mechanism.
Die Beziehung zwischen der Storstellenverfestigung, die durch die Abweichung der Zusammensetzung herruhrt, und der Substitutionsloslichkeits-Verfestigung, wird in der intermetallischen Verbindung Ni3Al durch Vergleich der Anderung der Gitterparameter und des Schermoduls mit der Kompressionsstreckgrenze untersucht. In jedem Fall werden die Verfestigungsgeschwindigkeiten durch Fleischers Parameter unter Berucksichtigung beider Effekte, der elastischen Wechselwirkung zwischen Versetzungen und gelosten Atomen, ausgedruckt. Es wird angenommen, das die Storstellenverfestigung in Ni3Al als eine Art von Substitutionsloslichkeits-Verfestigung angesehen werden mus und das beide Verfestigungseffekte durch den gleichen Mechanismus gesteuert werden.
[1]
O. Izumi,et al.
Defect Structures and Long‐Range‐Order Parameters in Off‐Stoichiometric Ni3Al
,
1975
.
[2]
O. Izumi,et al.
Influence of Substitutional Solute Elements on the Strength of Intermetallic Compound Ni 3 Al at Elevated Temperature
,
1975
.
[3]
D. Koss,et al.
Solid solution hardening of the ternary system: Nb--Hf--W. Technical progress report, 1 January 1973--1 July 1974
,
1974
.
[4]
R. T. Pascoe,et al.
The Tensile Deformation of Solute-Strengthened Copper Polycrystals
,
1972
.
[5]
J. A. López,et al.
The effects of non-stoichiometry and titanium additions on the mechanical behaviour of Ni3Al (γ′)
,
1970
.
[6]
E. Teghtsoonian,et al.
Tensile deformation of polycrystalline beta prime-AuZn
,
1970
.
[7]
R. Fleischer,et al.
Substitutional solution hardening
,
1963
.
[8]
J. H. Westbeook.
Temperature Dependence of Hardness of the Equi‐Atomic Iron Group Aluminides
,
1956
.