Fabrication of Metal Oxide Nanoparticles by Highly Exothermic Reactions

The development of two methods using highly exothermic oxidation reactions to synthesize nanostructured oxide particles is described. The first method uses solution combustion to produce a high temperature front that moves through the sample and produces the nanoparticles. For example, Bi 2 O 3 nanoparticles are produced using a solution of molten metal nitrates and glycine. The glycine (fuel) is completely combusted during the thermal decomposition of the (oxidizer) nitrates and generates a temperature front that propagates through the sample. The second method produces nanoparticles by a self-propagating high-temperature reaction from stoichiometric powder mixtures of metal oxides (or carbonates) and carbon. The exothermic oxidation of the carbon generates a propagating high-temperature front at a velocity in the range of 0.1-2.5 mm/s that converts the reactants to products. In both cases, the synthesis was completed within a few seconds. In both methods, a higher maximum combustion temperature and larger oxide particle size were obtained following an increase in the fuel concentration. The main advantages of these synthesis methods technologies are simplicity, short reaction time, low reactant costs, and no external energy consumption. The methods can be used to synthesize nanoparticles for various applications including nanoenergetic materials, catalysts and electronic components.

[1]  O. A. Shlyakhtin,et al.  Recent progress in cryochemical synthesis of oxide materials , 1999 .

[2]  Q. Pankhurst,et al.  Applications of magnetic nanoparticles in biomedicine , 2003 .

[3]  Z. J. Zhang,et al.  Magnetic Spinel Ferrite Nanoparticles from Microemulsions , 2004 .

[4]  Arvind Varma,et al.  Combustion Synthesis of Advanced Materials: Principles and Applications , 1998 .

[5]  A. Merzhanov,et al.  The chemistry of self-propagating high-temperature synthesis , 2004 .

[6]  C. Bárcena,et al.  APPLICATIONS OF MAGNETIC NANOPARTICLES IN BIOMEDICINE , 2003 .

[7]  M. Nersesyan,et al.  Phase Formation during Self-Propagating High-Temperature Synthesis of Ferrites , 2002 .

[8]  T. Alan Hatton,et al.  Nanoparticles: Synthesis, Stabilization, Passivation, and Functionalization , 2008 .

[9]  W. Skorupa,et al.  Ion beam synthesis of semiconductor nanoclusters for opto-and microelectronics applications , 1999 .

[10]  D. Litvinov,et al.  Carbon Combustion Synthesis and Magnetic Properties of Cobalt Ferrite Nanoparticles , 2007, IEEE Transactions on Magnetics.

[11]  P. Maggard,et al.  Hydrothermal Synthesis and Photocatalytic Activities of SrTiO3‐Coated Fe2O3 and BiFeO3 , 2006 .

[12]  D. Luss,et al.  Carbon Combustion Synthesis of Ferrites: Synthesis and Characterization , 2007 .

[13]  C. Brinker,et al.  Sol-Gel Science: The Physics and Chemistry of Sol-Gel Processing , 1990 .

[14]  D. Luss,et al.  Carbon combustion synthesis of complex oxides: Process demonstration and features , 2005 .

[15]  V. T. Liveri,et al.  Controlled Synthesis of Nanoparticles in Microheterogeneous Systems , 2006 .

[16]  R. M. Barrer,et al.  Hydrothermal Chemistry of Zeolites , 1982 .

[18]  A. M. Glass,et al.  Principles and Applications of Ferroelectrics and Related Materials , 1977 .

[19]  K. Suresh,et al.  A novel combustion synthesis of spinel ferrites, orthoferrites and garnets , 1991 .