Thin films of vanadium oxide grown on vanadium metal: oxidation conditions to produce V2O5 films for Li‐intercalation applications and characterisation by XPS, AFM, RBS/NRA

Thin films of vanadium oxide were grown on vanadium metal surfaces (i) in air at ambient conditions, (ii) in 5 mM H2SO4 (aq), pH 3, (iii) by thermal oxidation at low oxygen pressure (10−5 mbar) at temperatures between 350 and 550 °C and (iv) at near‐atmospheric oxygen pressure (750 mbar) at 500 °C. The oxide films were investigated by atomic force microscopy (AFM), X‐ray photoelectron spectroscopy (XPS), X‐Ray diffraction (XRD) and Rutherford backscattering spectrometry (RBS) and nuclear reaction analysis (NRA). The lithium intercalation properties were studied by cyclic voltammetry (CV). The results show that the oxide films formed in air at room temperature (RT), in acidic aqueous solution, and at low oxygen pressure at elevated temperatures are composed of V2O3. In air and in aqueous solution at RT, the oxide films are ultra‐thin and hydroxylated. At 500 °C, nearly atmospheric oxygen pressure is required to form crystalline V2O5 films. The oxide films grown at pO2 = 750 mbar for 5 min are about 260‐nm thick, and consist of a 115‐nm outer layer of crystalline V2O5. The inner oxide is mainly composed of VO2. For all high temperature oxidations, the oxygen diffusion from the oxide film into the metal matrix was considerable. The oxygen saturation of the metal at 450 °C was found, by XPS, to be 27 at.% at the oxide/metal interface. The well‐crystallized V2O5 film, formed by oxidation for 5 min at 500 °C and 750 mbar O2, was shown to have good lithium intercalation properties and is a promising candidate as electrode material in lithium batteries. Copyright © 2005 John Wiley & Sons, Ltd.

[1]  K. Hiraga,et al.  Local Ordering of Oxygen in Vanadium-Oxygen Alloys Studied by Electron Microscopy and Diffraction , 1980 .

[2]  Alexander Pergament,et al.  Phase composition of anodic oxide films on transition metals: a thermodynamic approach , 1998 .

[3]  M. Misono,et al.  EXAFS analysis of vanadium oxide thin overlayers on silica prepared by chemical vapour deposition , 1992 .

[4]  C. Blaauw,et al.  VO2における金属‐非金属転移: X線光電子放出および抵抗の測定 , 1975 .

[5]  C. Delmas,et al.  The LixV2O5 system: An overview of the structure modifications induced by the lithium intercalation , 1994 .

[6]  L. Doolittle.  A semiautomatic algorithm for rutherford backscattering analysis , 1986 .

[7]  Laura E. Depero,et al.  Vanadyl Precursors Used to Modify the Properties of Vanadium Oxide Thin Films Obtained by Chemical Vapor Deposition , 1999 .

[8]  J. B. Bates,et al.  RECHARGEABLE THIN-FILM LITHIUM MICROBATTERIES , 1993 .

[9]  G. Pistoia,et al.  Lithium batteries : new materials, developments, and perspectives , 1994 .

[10]  D. Lincot,et al.  Electrochemical Study of Phase Transition Processes in Lithium Insertion in V 2 O 5 Electrodes , 2003 .

[11]  J. Pereira‐Ramos,et al.  Sol-gel chromium–vanadium mixed oxides as lithium insertion compounds , 2000 .

[12]  D. Murphy,et al.  Solid State Electrodes for High Energy Batteries , 1979, Science.

[13]  H. Groult,et al.  Preparation of Li–Mn–O thin films by r.f.-sputtering method and its application to rechargeable batteries , 2000 .

[14]  M. Broussely,et al.  Crystal chemistry of electrochemically inserted LixV2O5 , 1991 .

[15]  J. S. Anderson,et al.  Phase equilibria in the vanadium-oxygen system , 1970 .

[16]  A. Manthiram,et al.  Synthesis of Nanocrystalline VO 2 and Its Electrochemical Behavior in Lithium Batteries , 1997 .

[17]  Y. Barbaux,et al.  XPS studies of V2O5, V6O13, VO2 and V2O3 , 1995 .

[18]  E. A. Gulbransen,et al.  The Kinetics of the Reactions of Vanadium with Oxygen and Nitrogen , 1950 .

[19]  E. Andrukaitis.  Lithium intercalation in electrodeposited vanadium oxide bronzes , 2003 .

[20]  V. Kruchinin,et al.  Spectral dependence of the complex refractive index shift across the semiconductor-metal transition in thermally-oxidized vanadium , 1998 .

[21]  A. V. Drigo,et al.  Intercomparison of absolute standards for RBS studies , 1983 .

[22]  G. Dräger,et al.  X‐ray and X‐ray photoelectron spectra of vanadium oxides , 1981 .

[23]  J. Siejka,et al.  Precision absolute thin film standard reference targets for nuclear reaction microanalysis of oxygen isotopes: Part II: 18O and 17O standards , 1978 .

[24]  G. Kiss,et al.  The influence of surface effects on the hydrogen absorption investigated on the V–H model system , 2001 .

[25]  M. Billy,et al.  Oxydation du vanadium , 1981 .

[26]  G. Eriksson.  An algorithm for the computation of aqueous multi-component, multiphase equilibria , 1979 .

[27]  T. Nakajima,et al.  Structural changes of Nb2O5 and V2O5 as rechargeable cathodes for lithium battery , 1983 .

[28]  W. Reichelt,et al.  Mixed-valence vanadium oxides studied by XPS , 2000 .

[29]  George A. Sawatzky,et al.  The metal-non-metal transition in VO2: X-ray photoemission and resistivity measurements , 1975 .

[30]  C. Julien.  Lithium intercalated compounds: Charge transfer and related properties , 2003 .

[31]  S. Deki,et al.  Novel wet process for preparation of vanadium oxide thin film , 1996 .

[32]  D. Guyomard,et al.  e-V2O5: Relationships between synthesis conditions, material characteristics and lithium intercalation behavior , 1999 .

[33]  J. Siejka,et al.  Precision absolute thin film standard reference targets for nuclear reaction microanalysis of oxygen isotopes , 1978 .

[34]  D. Smith.  Solubility of oxygen in vanadium , 1973 .

[35]  I. Hevesi,et al.  Structural characterization of amorphous vanadium pentoxide thin films prepared by chemical vapour deposition /CVD/ , 1980 .

[36]  D. Murphy,et al.  Vanadium Oxide Cathode Materials for Secondary Lithium Cells , 1979 .

[37]  S. Andersson.  ESCA investigation of V2O5+TiO2 catalysts for the vapour phase oxidation of alkylpyridines , 1979 .

[38]  S. Pyun,et al.  Electrochemical lithium intercalation reaction of anodic vanadium oxide film , 1995 .

[39]  A. Mukherjee,et al.  Kinetics of the oxidation of vanadium in the temperature range 350–950°C , 1983 .

[40]  F. Gan,et al.  Preparation and optical properties of phase-change VO2 thin films , 1993, Journal of Materials Science.

[41]  A. C. Wismayer,et al.  TEM and IBA study of the thermal oxidation of V following high dose He implantation , 1997 .

[42]  R. McCune,et al.  The vanadium-oxygen system: Phase relations in the vanadium-rich region below 1200 °C , 1970 .

[43]  G. Sawatzky,et al.  X-ray photoelectron and Auger spectroscopy study of some vanadium oxides , 1979 .

[44]  M. S. Hegde,et al.  Study of transition metal oxides by photoelectron spectroscopy , 1979, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[45]  T. Gustafsson,et al.  Direct XRD observation of oxidation-state changes on Li-ion insertion into transition-metal oxide hosts , 1999 .

[46]  I. Barin,et al.  Thermochemical properties of inorganic substances , 1973 .

[47]  Ji‐Guang Zhang,et al.  Charging Capacity and Cycling Stability of VO[sub x] Films Prepared by Pulsed Laser Deposition , 1997 .