Enhancement of Thermoelectric Performance of n‐Type PbSe by Cr Doping with Optimized Carrier Concentration

Ti, V, Cr, Nb, and Mo are found to be effective at increasing the Seebeck coefficient and power factor of n-type PbSe at temperatures below 600 K. It is found that the higher Seebeck coefficients and power factors are due to higher Hall mobility ≈1000 cm2 V−1s−1 at lower carrier concentration. A larger average ZT value (relevant for applications) can be obtained by an optimization of carrier concentration to ≈1018–1019 cm−3. Even though the highest room temperature power factor ≈3.3 × 10−3 W m−1 K−2 is found in 1 at% Mo-doped PbSe, the highest ZT is achieved in Cr-doped PbSe. Combined with the lower thermal conductivity, ZT is improved to ≈0.4 at room temperature and peak ZTs of ≈1.0 are observed at ≈573 K for Pb0.9925Cr0.0075Se and ≈673 K for Pb0.995Cr0.005Se. The calculated device efficiency of Pb0.995Cr0.005Se is as high as ≈12.5% with cold side 300 K and hot side 873 K, higher than those of all the n-type PbSe materials reported in the literature.

[1]  J. Heremans,et al.  Titanium forms a resonant level in the conduction band of PbTe , 2011 .

[2]  G. J. Snyder,et al.  Heavily Doped p‐Type PbSe with High Thermoelectric Performance: An Alternative for PbTe , 2011, Advanced materials.

[3]  Tiejun Zhu,et al.  Shifting up the optimum figure of merit of p -type bismuth telluride-based thermoelectric materials for power generation by suppressing intrinsic conduction , 2014 .

[4]  E. M. Levin,et al.  Chromium as resonant donor impurity in PbTe , 2012 .

[5]  M. Baleva,et al.  Optical absorption in PbTe doped with Cr , 1983 .

[6]  Heng Wang,et al.  Weak electron–phonon coupling contributing to high thermoelectric performance in n-type PbSe , 2012, Proceedings of the National Academy of Sciences.

[7]  Zhifeng Ren,et al.  Skutterudite Unicouple Characterization for Energy Harvesting Applications , 2013 .

[8]  M. Kanatzidis,et al.  High-temperature charge and thermal transport properties of the n-type thermoelectric material PbSe , 2011, 1108.2109.

[9]  B. Paul,et al.  Dramatic enhancement of thermoelectric power factor in PbTe:Cr co-doped with iodine , 2011 .

[10]  G. J. Snyder,et al.  Stabilizing the Optimal Carrier Concentration for High Thermoelectric Efficiency , 2011, Advanced materials.

[11]  M. Kanatzidis,et al.  Strained endotaxial nanostructures with high thermoelectric figure of merit. , 2011, Nature chemistry.

[12]  Gang Chen,et al.  Transmission electron microscopy study of Pb-depleted disks in PbTe-based alloys , 2011 .

[13]  Qian Zhang,et al.  Heavy doping and band engineering by potassium to improve the thermoelectric figure of merit in p-type PbTe, PbSe, and PbTe(1-y)Se(y). , 2012, Journal of the American Chemical Society.

[14]  W. S. Liu,et al.  Experimental studies on anisotropic thermoelectric properties and structures of n-type Bi2Te2.7Se0.3. , 2010, Nano letters.

[15]  Elias Kyriakides,et al.  Designing high efficiency segmented thermoelectric generators , 2013 .

[16]  G. J. Snyder,et al.  Towards high efficiency segmented thermoelectric unicouples , 2014 .

[17]  G. J. Snyder,et al.  Reevaluation of PbTe1−xIx as high performance n-type thermoelectric material , 2011 .

[18]  M. Dresselhaus,et al.  High-Thermoelectric Performance of Nanostructured Bismuth Antimony Telluride Bulk Alloys , 2008, Science.

[19]  G. J. Snyder,et al.  Combination of large nanostructures and complex band structure for high performance thermoelectric lead telluride , 2011 .

[20]  Heng Wang,et al.  Convergence of electronic bands for high performance bulk thermoelectrics , 2011, Nature.

[21]  G. J. Snyder,et al.  Enhancement of Thermoelectric Efficiency in PbTe by Distortion of the Electronic Density of States , 2008, Science.

[22]  Gang Chen,et al.  Studies on the Bi2Te3–Bi2Se3–Bi2S3 system for mid-temperature thermoelectric energy conversion , 2013 .

[23]  Gang Chen,et al.  Increased thermoelectric performance by Cl doping in nanostructured AgPb18SbSe20−xClx , 2013 .

[24]  Gang Chen,et al.  A review of cermet-based spectrally selective solar absorbers , 2014 .

[25]  G. J. Snyder,et al.  High thermoelectric figure of merit in heavy hole dominated PbTe , 2011 .

[26]  Ali Shakouri,et al.  Thermoelectric power generator module of 16×16 Bi2Te3 and 0.6% ErAs:(InGaAs)1−x(InAlAs)x segmented elements , 2009 .

[27]  K. Esfarjani,et al.  Enhancement of thermoelectric figure-of-merit by resonant states of aluminium doping in lead selenide , 2011 .

[28]  M. Kanatzidis,et al.  High ZT in p-type (PbTe)1-2x(PbSe)x(PbS)x thermoelectric materials. , 2014, Journal of the American Chemical Society.

[29]  Gang Chen,et al.  High-performance flat-panel solar thermoelectric generators with high thermal concentration. , 2011, Nature materials.

[30]  Gang Chen,et al.  Effect of silicon and sodium on thermoelectric properties of thallium-doped lead telluride-based materials. , 2012, Nano letters.

[31]  B. Paul,et al.  The effect of chromium impurity on the thermoelectric properties of PbTe in the temperature range 100–600 K , 2011 .

[32]  David J. Singh,et al.  Study of the thermoelectric properties of lead selenide doped with boron, gallium, indium, or thallium. , 2012, Journal of the American Chemical Society.

[33]  Eric S. Toberer,et al.  High Thermoelectric Performance in PbTe Due to Large Nanoscale Ag2Te Precipitates and La Doping , 2010 .

[34]  H. Goldsmid,et al.  Introduction to Thermoelectricity , 2016 .

[35]  Chan Park,et al.  Thermoelectric Properties of n-Type Bi2Te3/PbSe0.5Te0.5 Segmented Thermoelectric Material , 2014, Journal of Electronic Materials.

[36]  V. Slyn’ko,et al.  On the resonant level of chromium in the rhombohedral and cubic phases of Pb1 − x − yGexCryTe alloys , 2013 .