Micromechanisms of crack growth in ceramics and glasses in corrosive environments

AbstractAt normal temperatures and pressures water is known to have a strong influence on the strength of ceramics and glasses. Behaving as a stress corrosion agent, water causes these materials to fail prematurely as a consequence of subcritical crack growth. A basic premise of this paper is that stress corrosion cracking of ceramics is a chemical process which involves a stress-enhanced chemical reaction between the water and the highly stressed ceramic near the crack tip. Plastic deformation is believed to play no role in this fracture process. After a brief survey of chemical reaction rate theory, the basic rate equation from this theory is modified to reflect physical and chemical processes which occur at crack tips. Modification of the rate equation is based on the assumption thatl the crack tip can be modelled as an elastic continuum, an assumption that is supported by a simple atomistic model of crack growth. When tested against experimental data collected on glass the theory was found to be consi...

[1]  S. Rice,et al.  High Pressure Physics and Chemistry , 1964 .

[2]  S. Freiman,et al.  Crack propagation in alkaline‐earth fluorides , 1978 .

[3]  Sheldon M. Wiederhorn,et al.  A Chemical Interpretation of Static Fatigue , 1972 .

[4]  B. Lawn,et al.  Electron microscopy of microcracking about indentations in aluminium oxide and silicon carbide , 1975 .

[5]  Brian R. Lawn,et al.  An atomistic model of kinetic crack growth in brittle solids , 1975 .

[6]  Anthony G. Evans,et al.  Application of Fracture Mechanics to Space‐Shuttle Windows , 1974 .

[7]  R. J. Jaccodine,et al.  Surface Energy of Germanium and Silicon , 1963 .

[8]  Dependence of Ultimate Strength of Glass Under Constant Load on Temperature, Ambient Atmosphere, and Time , 1953 .

[9]  C. Eckert.  High Pressure Kinetics in Solution , 1972 .

[10]  Sheldon M. Wiederhorn,et al.  Fracture Surface Energy of Glass , 1969 .

[11]  E. Fuller,et al.  Theory of chemically assisted fracture , 1980 .

[12]  M. Ladd.  Structure and Bonding in Solid State Chemistry , 1979 .

[13]  S. Wiederhorn.  Moisture assisted crack growth in ceramics , 1968 .

[14]  Effect of Alcohols on Crack Propagation in Glass , 1974 .

[15]  M. Born.  Volumen und Hydratationswärme der Ionen , 1920 .

[16]  Sheldon M. Wiederhorn,et al.  Influence of Water Vapor on Crack Propagation in Soda‐Lime Glass , 1967 .

[17]  Sheldon M. Wiederhorn,et al.  Subcritical Crack Growth in Ceramics , 1974 .

[18]  R. W. Douglas,et al.  Reactions of Glasses with Aqueous Solutions , 1967 .

[19]  M. G. Evans,et al.  Some applications of the transition state method to the calculation of reaction velocities, especially in solution , 1935 .

[20]  B. Stevens,et al.  Progress in reaction kinetics , 1961 .

[21]  H. Johnson,et al.  Fracture of Glass in Vacuum , 1974 .

[22]  D. Hubbard,et al.  Studies of the chemical durability of glass by an interferometer method , 1941 .

[23]  S. Wiederhorn,et al.  Crack Healing in Glass , 1970 .

[24]  S. Wiederhorn,et al.  Stress Corrosion and Static Fatigue of Glass , 1970 .

[25]  A. Adamson.  Physical chemistry of surfaces , 1960 .

[26]  B. A. Proctor,et al.  The strength of fused silica , 1967, Proceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences.

[27]  Theory of chemically assisted fracture , 1980 .