Modeling Forced Flow Chemical Vapor Infiltration Fabrication of SiC-SiC Composites for Advanced Nuclear Reactors

Silicon carbide fiber/silicon carbide matrix (SiC-SiC) composites exhibit remarkable material properties, including high temperature strength and stability under irradiation. These qualities have made SiC-SiC composites extremely desirable for use in advanced nuclear reactor concepts, where higher operating temperatures and longer lives require performance improvements over conventional metal alloys. However, fabrication efficiency advances need to be achieved. SiC composites are typically produced using chemical vapor infiltration (CVI), where gas phase precursors flow into the fiber preform and react to form a solid SiC matrix. Forced flow CVI utilizes a pressure gradient to more effectively transport reactants into the composite, reducing fabrication time. The fabrication parameters must be well understood to ensure that the resulting composite has a high density and good performance. To help optimize this process, a computer model was developed. This model simulates the transport of the SiC precursors, the deposition of SiC matrix on the fiber surfaces, and the effects of byproducts on the process. Critical process parameters, such as the temperature and reactant concentration, were simulated to identify infiltration conditions which maximize composite density while minimizing the fabrication time.

[1]  R. Naslain Design, preparation and properties of non-oxide CMCs for application in engines and nuclear reactors: an overview , 2004 .

[2]  Aaas News,et al.  Book Reviews , 1893, Buffalo Medical and Surgical Journal.

[3]  M. Allendorf,et al.  The adsorption of hydrogen chloride on polycrystalline β-silicon carbide , 1995 .

[4]  T. S. Moss,et al.  Depletion Effects of Silicon Carbide Deposition from Methyltrichlorosilane , 1992 .

[5]  Lai-fei Cheng,et al.  Numerical Simulation of Effect of Methyltrichlorosilane Flux on Isothermal Chemical Vapor Infiltration Process of C/SiC Composites , 2006 .

[6]  K. J. Hüttinger,et al.  CVD of SiC from Methyltrichlorosilane. Part II: Composition of the Gas Phase and the Deposit , 2001 .

[7]  A. Kohyama,et al.  Development of SiC/SiC composites by PIP in combination with RS , 2001 .

[8]  T. Morse,et al.  Minimizing Infiltration Times during Isothermal Chemical Vapor Infiltration with Methyltrichlorosilane , 2005 .

[9]  Jim Euchner Design , 2014, Catalysis from A to Z.

[10]  Neil Genzlinger A. and Q , 2006 .

[11]  A. Kohyama,et al.  High-temperature tensile strength of near-stoichiometric SiC/SiC composites , 2002 .

[12]  Lai-fei Cheng,et al.  Kinetics of chemical vapor deposition of SiC from methyltrichlorosilane and hydrogen , 2009 .

[13]  Y. Katoh,et al.  Handbook of SiC properties for fuel performance modeling , 2007 .

[14]  Y. Katoh,et al.  Stability of SiC and its composites at high neutron fluence , 2011 .

[15]  Akira Kohyama,et al.  Microstructural optimization of high-temperature SiC/SiC composites by NITE process , 2009 .

[16]  G. G. Stokes "J." , 1890, The New Yale Book of Quotations.

[17]  B. Sammuli,et al.  Fabrication of SiC–SiC composites for fuel cladding in advanced reactor designs , 2012 .

[18]  Analysis of the isothermal forced flow chemical vapour infiltration process. Part I: Theoretical aspects , 1995 .