Micro-Raman analysis of residual stresses and phase transformations in crystalline silicon under microindentation

Vickers microindentations obtained with loads between 0.05 N and 2 N were performed on crystalline (100) silicon. The residual stress field and the different structural states induced by loading were studied by mapping the indented zones by their micro-Raman response. A Raman signature of amorphous silicon is found in the center of the impression. The energy of the Γ_25 zone center phonon is found to vary from 522 cm^−1 when probing the silicon at a distance of 80 µ m from the center of the indentation up to 527 cm^−1 when probing the pileup region of the impression. When probing cracked zones in the vicinity of the pileup region, wave numbers as high as 536 cm^−1 are measured. The stress components induced by a point indentation (1 N) have been calculated from analytical expressions given in the literature. For an average conversion factor of 3.2 cm^−1/GPa, the residual local stresses after unloading are found of the same order of magnitude or even larger than the calculated stresses that are generated during loading. A tentative explanation is proposed. Finally a systematic laser-induced thermal treatment of the central area and of the pileup region of indentations was performed. It is shown that the amorphous silicon in the center can partly recrystallize but that the residual stress state in the pileup region cannot be completely relaxed by local laser heating.

[1]  Shefford P. Baker,et al.  Thin films: Stresses and mechanical properties VI , 1997 .

[2]  Michael V. Swain,et al.  Observation, analysis, and simulation of the hysteresis of silicon using ultra-micro-indentation with spherical indenters , 1993 .

[3]  David R. Clarke,et al.  Electrical resistance of metallic contacts on silicon and germanium during indentation , 1992 .

[4]  M. C. Lee,et al.  Optical and Raman correlation of laser recrystallised and quenched amorphous silicon film: a microprobe study , 1990 .

[5]  R. Cook,et al.  Direct Observation and Analysis of Indentation Cracking in Glasses and Ceramics , 1990 .

[6]  G. Pharr,et al.  Hysteresis and discontinuity in the indentation load-displacement behavior of silicon , 1989 .

[7]  Irving P. Herman,et al.  The importance of thermal stresses and strains induced in laser processing with focused Gaussian beams , 1988 .

[8]  Kroll,et al.  Amorphization and conductivity of silicon and germanium induced by indentation. , 1988, Physical review letters.

[9]  É. Bustarret,et al.  Experimental determination of the nanocrystalline volume fraction in silicon thin films from Raman spectroscopy , 1988 .

[10]  E. Anastassakis,et al.  Laser‐induced thermal strains in isotropic media: Polycrystalline Si , 1988 .

[11]  Evangelos Anastassakis,et al.  Polycrystalline Si under strain: Elastic and lattice‐dynamical considerations , 1987 .

[12]  González,et al.  Electrical properties of semimetallic silicon III and semiconductive silicon IV at ambient pressure. , 1987, Physical review letters.

[13]  Spain,et al.  Crystal data for high-pressure phases of silicon. , 1986, Physical review. B, Condensed matter.

[14]  E. Liarokapis,et al.  Temperature rise induced by a cw laser beam revisited , 1985 .

[15]  Ian L. Spain,et al.  Phases of silicon at high pressure , 1984 .

[16]  H. Olijnyk,et al.  Structural phase transitions in Si and Ge under pressures up to 50 GPa , 1984 .

[17]  Gerald Earle Jellison,et al.  Optical absorption of silicon between 1.6 and 4.7 eV at elevated temperatures , 1982 .

[18]  Mool C. Gupta,et al.  Static compression of silicon in the [100] and in the [111] directions , 1980 .

[19]  D. Tabor,et al.  Indentation hardness and semiconductor–metal transition of germanium and silicon , 1978, Nature.

[20]  O. Shimomura,et al.  Pressure-induced semiconductor-metal transitions in amorphous Si and Ge , 1974 .

[21]  V. I. Trefilov,et al.  Phase transition in diamond‐structure crystals during hardness measurements , 1972 .

[22]  V. G. Eremenko,et al.  Electron Microscope Investigation of the Microplastic Deformation Mechanisms of Silicon by Indentation , 1972, November 16.

[23]  T. R. Hart,et al.  Temperature Dependence of Raman Scattering in Silicon , 1970 .

[24]  M. Oron,et al.  Ferrimagnetic garnet thin films: Growth, structure and some magnetic properties , 1969 .

[25]  R. H. Wentorf,et al.  Two New Forms of Silicon , 1963, Science.

[26]  G. Lucazeau,et al.  Raman spectroscopy in solid state physics and material science. Theory, techniques and applications , 1995 .

[27]  E. Anastassakis,et al.  Effect of temperature gradients on the first‐order Raman spectrum of Si , 1984 .

[28]  Michael V. Swain,et al.  Microfracture beneath point indentations in brittle solids , 1975 .