Assessment of uncertainties in life prediction of fatigue crack initiation and propagation in welded rails

The risk for initiation of fatigue cracks in the rail head and web in the weld zone of a rail is studied. The interaction between the welding residual stress field and the stress field caused by service loads is simulated in a nonlinear finite element (FE) analysis where the welding residual stress distribution (shape) and magnitude, the service load magnitude and the material parameters used in the fatigue life estimation are varied. The initiation of fatigue cracks is assessed using the shear-stress-based multiaxial fatigue criterion proposed by Dang Van, and the propagation of fatigue cracks in the rail web is carried out using a Paris-type crack growth law. A discussion is presented of the interpretation of using the Dang Van criterion to assess crack initiation for stress–response load cycles with low shear stress amplitudes and high hydrostatic stress levels. In addition, the accuracy in the fatigue life assessment is evaluated by statistical uncertainty analysis where the variances according to the Gauss approximation formula are studied. The risk for fatigue crack initiation and propagation in the rail head and rail web, respectively, is enhanced due to the welding residual stress, and the uncertainty in load level dominates the uncertainty in the fatigue assessments.

[1]  J. Beynon,et al.  Engineering against fatigue , 1999 .

[2]  Uwe Zerbst,et al.  Fracture mechanics in railway applications––an overview , 2005 .

[3]  Peter Mutton,et al.  Failure modes in aluminothermic rail welds under high axle load conditions , 2004 .

[4]  Christopher P. L. Barkan,et al.  Heat transfer modelling of rail thermite welding , 2006 .

[5]  L. Susmel,et al.  The mean stress effect on the high-cycle fatigue strength from a multiaxial fatigue point of view , 2005 .

[6]  K. Dang Van,et al.  Rolling contact in railways: modelling, simulation and damage prediction , 2003 .

[7]  Luca Susmel,et al.  Multiaxial fatigue limits and material sensitivity to non‐zero mean stresses normal to the critical planes , 2008 .

[8]  Jonas W. Ringsberg,et al.  Fatigue crack growth in a welded rail under the influence of residual stresses , 2005 .

[9]  Jonas W. Ringsberg,et al.  Influence of railway wheel flat impact on crack growth in rails , 2005 .

[10]  Stefano Beretta,et al.  Mechanisms of mixed mode fatigue crack propagation at rail butt-welds , 2006 .

[11]  S. Beretta,et al.  On the application of Dang Van criterion to rolling contact fatigue , 2006 .

[12]  Jonas W. Ringsberg,et al.  Rolling contact fatigue of rails—finite element modelling of residual stresses, strains and crack initiation , 2000 .

[13]  Horst-Hannes Cerjak,et al.  Mathematical Modelling of Weld Phenomena 7 , 2002 .

[14]  B. L. Josefson,et al.  Finite element analyses of rolling contact fatigue crack initiation in railheads , 2001 .

[15]  J. Ringsberg,et al.  Investigation of the rolling contact fatigue resistance of laser cladded twin-disc specimens: FE simulation of laser cladding, grinding and a twin-disc test , 2005 .