SEMICONDUCTOR TECHNOLOGY Texturization of mono-crystalline silicon solar cells in TMAH without the addition of surfactant

Etching was performed on (100) silicon wafers using silicon-dissolved tetramethylammonium hydroxide (TMAH) solutions without the addition of surfactant. Experiments were carried out in different TMAH concentrations at different temperatures for different etching times. The surface phenomena, etching rates, surface morphology and surface reflectance were analyzed. Experimental results show that the resulting surface covered with uniform pyramids can be realized with a small change in etching rates during the etching process. The etching mechanism is explained based on the experimental results and the theoretical considerations. It is suggested that all the components in the TMAH solutions play important roles in the etching process. Moreover, TMA+ ions may increase the wettability of the textured surface. A good textured surface can be obtained in conditions where the absorption of OH-/H2O is in equilibrium with that of TMA+/SiO2 (OH)22-.

[1]  Osamu Tabata.  pH-controlled TMAH etchants for silicon micromachining , 1996 .

[2]  Irena Zubel,et al.  The effect of isopropyl alcohol on etching rate and roughness of (1 0 0) Si surface etched in KOH and TMAH solutions , 2001 .

[3]  Martin A. Green,et al.  Silicon solar cells , 1996 .

[4]  Rita Rizzoli,et al.  An optimized texturing process for silicon solar cell substrates using TMAH , 2005 .

[5]  Chao-Kuei Lee,et al.  A simple and cost-effective approach for fabricating pyramids on crystalline silicon wafers , 2009 .

[6]  Jose Rodriguez.  Random pyramidal texture modelling , 1997 .

[7]  James Jungho Pak,et al.  Experiments on anisotropic etching of Si in TMAH , 2001 .

[8]  M. Green,et al.  Light trapping properties of pyramidally textured surfaces , 1987 .

[9]  Junsin Yi,et al.  Low-cost texturization of large-area crystalline silicon solar cells using hydrazine mono-hydrate for industrial use , 2006 .

[10]  Arun Vijayakumar,et al.  Smooth etching of silicon using TMAH and isopropyl alcohol for MEMS applications , 2005 .

[11]  Hiranmay Saha,et al.  Novel low-cost approach for removal of surface contamination before texturization of commercial monocrystalline silicon solar cells , 2007 .

[12]  Hiranmay Saha,et al.  Role of hydrazine monohydrate during texturization of large-area crystalline silicon solar cell fabrication , 2006 .

[13]  Soonwoo Kwon,et al.  Effects of textured morphology on the short circuit current of single crystalline silicon solar cells: Evaluation of alkaline wet-texture processes , 2009 .

[14]  Martin A. Green,et al.  21.5% Efficient thin silicon solar cell , 1996 .

[15]  Alain Fave,et al.  Pyramidal texturing of silicon solar cell with TMAH chemical anisotropic etching , 2006 .