Chemical analysis of heat treated softwoods

Heat treatment of wood has been found an effective method to improve dimensional stability and durability against biodegradation. A two-stage heat treatment of wood at relatively mild conditions (<200 °C) was investigated by using different chemical analysing methods, such as a wood chemical component analysis, CHNO-elemental analysis, UV-spectroscopy, and analysis of the acetyl and free hydroxyl group content. The results of this study contribute to a better understanding of the typical reaction mechanisms occurring and of the effect of heat treatment on the properties of wood, as described in previous 13C-NMR and FTIR studies of heat treated wood.ZusammenfassungDie Wärmebehandlung von Holz hat sich als ein wirksames Verfahren zur Verbesserung der Dimensionsstabilität und Fäuleresistenz erwiesen. In dieser Studie wurde eine zweistufige Wärmebehandlung von Holz unter relativ milden Bedingungen (<200 °C) untersucht. Dabei wurden verschiedene chemische Analyseverfahren, wie zum Beispiel chemische Analyse der Holzbestandteile, CHNO-Elementaranalyse, UV-Spektroskopiesowie Analyse des Acetylgehalts und der freien Hydroxylgruppen angewandt. Die Ergebnisse dieser Studie tragen zu einem besseren Verständnis der auftretenden Reaktionsmechanismen sowie der Wirkung einer Wärmebehandlung auf die Eigenschaften von Holz bei, die bereits in früheren 13C-NMR und FTIR Studien über wärmebehandeltes Holz beschrieben wurden.

[1]  E. Giebeler.  Dimensionsstabilisierung von Holz durch eine Feuchte/Wärme/Druck-Behandlung , 1983, Holz als Roh- und Werkstoff.

[2]  W. E. Hillis,et al.  High temperature and chemical effects on wood stability , 2004, Wood Science and Technology.

[3]  A. Spurr.  A low-viscosity epoxy resin embedding medium for electron microscopy. , 1969, Journal of ultrastructure research.

[4]  O. Faix,et al.  The influence of particle size and concentration in transmission and diffuse reflectance spectroscopy of wood , 1992, Holz als Roh- und Werkstoff.

[5]  H. Militz,et al.  Modification of solid wood: research and practical potential , 1997 .

[6]  A. Burmester.  Einfluß einer Wärme-Druck-Behandlung halbtrockenen Holzes auf seine Formbeständigkeit , 1973, Holz als Roh- und Werkstoff.

[7]  Kyosti V. Sarkanen,et al.  Lignins : occurrence, formation, structure and reactions , 1971 .

[8]  Nicolas Abatzoglou,et al.  Phenomenological kinetics of complex systems: mechanistic considerations in the solubilization of hemicelluloses following aqueous/steam treatments , 1991 .

[9]  A. Burmester.  Zur Dimensionsstabilisierung von Holz , 1975, Holz als Roh- und Werkstoff.

[10]  A. Pizzi,et al.  Chemical Modification of Norway Spruce and Scots Pine. A 13 C NMR CP-MAS Study of the Reactivity and Reactions of Polymeric Wood Components with Acetic Anhydride , 1996 .

[11]  Stephen Y. Lin,et al.  Methods in Lignin Chemistry , 1992, Springer Series in Wood Science.

[12]  J. Bourgois,et al.  Characterization and analysis of torrefied wood , 1988, Wood Science and Technology.

[13]  Harold Tarkow,et al.  Effect of Heat Upon the Dimensional Stabilization of Wood , 1953 .

[14]  D. Hon,et al.  Wood and Cellulosic Chemistry , 1990 .

[15]  B. L. Browning,et al.  Methods of wood chemistry , 1967 .

[16]  Alfred J. Stamm,et al.  Wood and Cellulose Science , 1964 .

[17]  Y. J. Tejwani,et al.  A new concept , 1984 .

[18]  R. Young.  The chemistry of solid wood , 1985, Wood Science and Technology.

[19]  G. T. Pott.  Natural Fibers with Low Moisture Sensitivity , 2004 .

[20]  D. Fengel,et al.  Wood: Chemistry, Ultrastructure, Reactions , 1983 .

[21]  E. Koukios,et al.  Dilute acid hydrolysis of lignocellulosics: An application to medium consistency suspensions of hardwoods using a plug flow reactor , 1990 .

[22]  W. Astbury,et al.  Structure of Cellulose , 1944, Nature.

[23]  A. Pizzi,et al.  A New Concept on the Chemical Modification of Wood by Organic Anhydrides , 1994 .

[24]  F. Kollmann,et al.  Änderungen der chemischen Zusammensetzung von Holz durch thermische Behandlung , 1965, Holz als Roh- und Werkstoff.

[25]  David Aaron,et al.  A New Concept , 1974 .

[26]  R. Overend,et al.  Conversion and solubilization profiles of a prototype hardwood (Populus tremuloides) following aqueous thermomechanical pre-treatment , 1986 .

[27]  R. Rowell,et al.  Acetyl Distribution in Acetylated Whole Wood and Reactivity of Isolated Wood Cell-Wall Components to Acetic Anhydride , 2007 .

[28]  H. Binder,et al.  Dynamischer hydrothermaler Abbau von Holz , 1980 .

[29]  F. Kollmann,et al.  Über das Sorptionsverhalten wärmebehandelter Hölzer , 1963, Holz als Roh- und Werkstoff.

[30]  H. Militz,et al.  Chemical changes in hydrothermal treated wood: FTIR analysis of combined hydrothermal and dry heat-treated wood , 2005, Holz als Roh- und Werkstoff.

[31]  J. Agterdenbos,et al.  Part 1. General Considerations , 1979 .

[32]  F. E. Bbauns.  Chemistry of lignin. , 1952 .

[33]  G. O. Aspinall.  Chemistry of Cell Wall Polysaccharides , 1980 .

[34]  L. E. Wise,et al.  A CHLORITE HOLOCELLULOSE, ITS FRACTIONATION AND BEARING ON SUMMATIVE WOOD ANALYSIS AND STUDIES ON THE HEMICELLULOSES , 1946 .