Mechanical properties of in situ demineralised human enamel measured by AFM nanoindentation

Abstract Diet-induced demineralisation is one of the key factors in surface changes of tooth enamel, with soft drinks being a significant etiological agent. The first step in this dissolution process is characterised by a change in the mechanical properties of the enamel and a roughening of the surface. The objective of this pilot study was to measure early stages of in situ induced hardness changes of polished human enamel surfaces with high accuracy using a nanoindenter attached to an atomic force microscope (AFM). Human unerupted third molars were cleaned, sterilised with sodium hypochlorite, sectioned and embedded in epoxy resin. The outer enamel surface was polished and the samples partly covered with a tape, allowing a 2-mm-wide zone to be exposed to the oral environment. Samples were fitted in an intra-oral appliance, which was worn from 9 a.m. to 5 p.m. for one day. During this time the volunteer sipped 250 ml of a drink over 10 min periods at 9.00, 11.00, 13.00 and 15.00 h. Three different drinks, mineral water, orange juice and the prototype of a blackcurrant drink with low demineralisation potential were used in this study. At the end of the experiment the samples were detached from the appliance, the tape removed and the surfaces chemically cleaned. The surface hardness and reduced Young's modulus of the exposed and unexposed areas of each sample were determined. In addition, high resolution topographical AFM images were obtained. This study shows that by determining the hardness and reduced Young's modulus, the difference in demineralisation caused by the drinks can be detected and quantified before statistically significant changes in surface topography could be observed with the AFM. The maximum decrease in surface hardness and Young's modulus occurred in the samples exposed to orange juice, followed by those exposed to the blackcurrant drink, while exposure to water led to the same values as unexposed areas. A one-way ANOVA showed a statistically significant difference between the changes in hardness for the drinks at a 95% confidence level (p=0.0000), while a Kruskal–Wallis test proved a statistically significant difference between the changes in the reduced Young's modulus at a 95% confidence level (p=0.0000). Thus, it was possible to detect differences in demineralisation potential in an in situ study at a very early stage. Further investigations with greater subject numbers and a larger quantity of samples are necessary to fully evaluate the potential of this method.

[1]  V. Castaño,et al.  In vitro Quantitative Assessment of Enamel Microhardness after Exposure to Eroding Immersion in a Cola Drink , 1998, Caries Research.

[2]  Bharat Bhushan,et al.  Nano/picoindentation measurements on single-crystal aluminum using modified atomic force microscopy , 1996 .

[3]  G. Willems,et al.  Hardness and Young's modulus determined by nanoindentation technique of filler particles of dental restorative materials compared with human enamel. , 1993, Journal of biomedical materials research.

[4]  J. M. ten Cate,et al.  Dental erosion, summary. , 1996, European journal of oral sciences.

[5]  B. Bhushan,et al.  Nanoscale mechanical property measurements using modified atomic force microscopy , 1996 .

[6]  R. Newcombe,et al.  Development and evaluation of a low erosive blackcurrant juice drink in vitro and in situ. 1. Comparison with orange juice. , 1999, Journal of dentistry.

[7]  A Lussi,et al.  A comparison of the erosive potential of different beverages in primary and permanent teeth using an in vitro model. , 2000, European journal of oral sciences.

[8]  Jandt,et al.  The Early Stages of Native Enamel Dissolution Studied with Atomic Force Microscopy. , 2000, Journal of colloid and interface science.

[9]  Bharat Bhushan,et al.  Micro/nanotribology using atomic force microscopy/friction force microscopy: State of the art , 1998 .

[10]  G. Pharr,et al.  An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments , 1992 .

[11]  J. Christoffersen,et al.  Some new aspects of surface nucleation applied to the growth and dissolution of fluorapatite and hydroxyapatite , 1996 .

[12]  J. T. ten Cate,et al.  Pathogenesis and modifying factors of dental erosion. , 1996, European journal of oral sciences.

[13]  J. M. Cate,et al.  TOOTH ENAMEL REMINERALIZATION , 1981 .

[14]  P. Gorostiza,et al.  In situ study of the recovery of nanoindentation deformation of the (100) face of MgO crystals by atomic force microscopy , 1999 .

[15]  D. Coomans,et al.  Load dependency and reliability of microhardness measurements on acid-etched enamel surfaces. , 1992, Dental materials : official publication of the Academy of Dental Materials.

[16]  J. Christoffersen,et al.  Kinetics of growth and dissolution of fluorapatite , 1996 .

[17]  N X West,et al.  A method to measure clinical erosion: the effect of orange juice consumption on erosion of enamel. , 1998, Journal of dentistry.

[18]  T. Attin,et al.  Correlation of microhardness and wear in differently eroded bovine dental enamel. , 1997, Archives of oral biology.

[19]  A. Slomiany,et al.  Tooth surface-pellicle lipids and their role in the protection of dental enamel against lactic-acid diffusion in man. , 1986, Archives of oral biology.

[20]  J. Olsson,et al.  Composition of Pellicles Formed in vivo on Tooth Surfaces in Different Parts of the Dentition, and in vitro on Hydroxyapatite , 1998, Caries Research.

[21]  M. Fitzgerald A Colour Atlas and Textbook of Oral Anatomy, Histology and Embryology , 1992 .

[22]  K. Jandt,et al.  Ultrasonication as a Method to Study Enamel Demineralisation during Acid Erosion , 2000, Caries Research.

[23]  G W Marshall,et al.  Viscoelastic properties of demineralized human dentin measured in water with atomic force microscope (AFM)-based indentation. , 1998, Journal of biomedical materials research.

[24]  B. Bhushan Handbook of micro/nano tribology , 1995 .

[25]  Zhuang,et al.  Metastable Equilibrium Solubility Distribution of Carbonated Apatite as a Function of Solution Composition. , 1999, Journal of colloid and interface science.

[26]  G. Maupomé,et al.  In vitro Quantitative Microhardness Assessment of Enamel with Early Salivary Pellicles after Exposure to an Eroding Cola Drink , 1999, Caries Research.

[27]  C. Rey,et al.  MicroRaman Spectral Study of the PO4 and CO3 Vibrational Modes in Synthetic and Biological Apatites , 1998, Calcified Tissue International.

[28]  P. Gorostiza,et al.  Atomic force microscopy study of nanoindentation creep on the (100) face of MgO single crystals , 2000 .

[29]  J. Voegel,et al.  Quantitative Model for the Dissolution of Calcium Hydroxyapatite with a Permselective Ionic Interface , 1993 .

[30]  R. Newcombe,et al.  Development and evaluation of a low erosive blackcurrant juice drink. 3. Final drink and concentrate, formulae comparisons in situ and overview of the concept. , 1999, Journal of dentistry.

[31]  J. Nunn,et al.  Prevalence of dental erosion and the implications for oral health. , 1996, European journal of oral sciences.

[32]  G. Marshall,et al.  Atomic force microscope measurements of the hardness and elasticity of peritubular and intertubular human dentin. , 1996, Journal of biomechanical engineering.