Annealing effects on CoFeB-MgO magnetic tunnel junctions with perpendicular anisotropy

We studied annealing effects on perpendicular anisotropy in CoFeB-MgO magnetic tunnel junctions. The results show that annealing is an effective method to improve the perpendicular anisotropy of a CoFeB-MgO system. It is found that a thicker CoFeB layer requires a higher annealing temperature to buildup its perpendicular anisotropy. However, perpendicular anisotropy could be seriously degraded if the annealing temperature is more than 350 °C. Our study suggests that CoFeB thickness should be optimized so that the required annealing temperature window for perpendicular anisotropy could match the annealing temperature for high magnetoresistance. In this work, the perpendicular anisotropy energy density of 2.5 × 106 erg/cm3 was achieved with tunnel magnetoresistive value exceeding 70%. The use of CoFeB films will enable the development of high density nonvolatile memory with size down to 30 nm.

[1]  J. L. Costa-Krämer,et al.  Large magnetoresistance in Fe/MgO/FeCo(001) epitaxial tunnel junctions on GaAs(001) , 2001 .

[2]  J. C. Sankey,et al.  Spin-torque ferromagnetic resonance measurements of damping in nanomagnets , 2007 .

[3]  H. Ohno,et al.  Current-Driven Magnetization Switching in CoFeB/MgO/CoFeB Magnetic Tunnel Junctions , 2005, INTERMAG 2006 - IEEE International Magnetics Conference.

[4]  Reduction in critical current for spin transfer switching in perpendicular anisotropy spin valves using an in-plane spin polarizer , 2009 .

[5]  Dmytro Apalkov,et al.  Spin-transfer switching in MgO-based magnetic tunnel junctions , 2006 .

[6]  B. Diény,et al.  Sizable room-temperature magnetoresistance in cobalt based magnetic tunnel junctions with out-of-plane anisotropy , 2008 .

[7]  H. Meng,et al.  Reduction of switching current by spin transfer torque effect in perpendicular anisotropy magnetoresistive devices (invited) , 2011 .

[8]  S. Lee,et al.  Magnetic Dead Layer in Amorphous CoFeB Layers with Various Top and Bottom Structures , 2010 .

[9]  S. Yuasa,et al.  Giant room-temperature magnetoresistance in single-crystal Fe/MgO/Fe magnetic tunnel junctions , 2004, Nature materials.

[10]  T. Chong,et al.  Effects of Ta seed layer and annealing on magnetoresistance in CoFe/Pd-based pseudo-spin-valves with perpendicular anisotropy , 2007 .

[11]  S. Horng,et al.  Giant anisotropy of carrier mobility in electroluminescent conjugated polymer , 2006 .

[12]  A. Panchula,et al.  Giant tunnelling magnetoresistance at room temperature with MgO (100) tunnel barriers , 2004, Nature materials.

[13]  Y. Huai,et al.  Observation of spin-transfer switching in deep submicron-sized and low-resistance magnetic tunnel junctions , 2004, cond-mat/0504486.

[14]  Tadahiko Hirai,et al.  Magnetic tunnel junction device with perpendicular magnetization films for high-density magnetic random access memory , 2002 .

[15]  S. Yuasa,et al.  Ultrathin Co/Pt and Co/Pd superlattice films for MgO-based perpendicular magnetic tunnel junctions , 2010 .

[16]  Ilya Krivorotov,et al.  Switching current reduction using perpendicular anisotropy in CoFeB-MgO magnetic tunnel junctions , 2011 .

[17]  F. Zeng,et al.  Hysteretic giant magnetoresistance curves induced by interlayer magnetostatic coupling in [Pd/Co]/Cu/Co/Cu/[Co/Pd] dual spin valves , 2010 .

[18]  J. Zhu,et al.  Spin Torque and Field-Driven Perpendicular MRAM Designs Scalable to Multi-Gb/Chip Capacity , 2006, IEEE Transactions on Magnetics.

[19]  C. Graham,et al.  Introduction to Magnetic Materials , 1972 .

[20]  M. Hosomi,et al.  Magnetoresistive random access memory operation error by thermally activated reversal (invited) , 2005 .

[21]  O. Hellwig,et al.  Tunable magnonic frequency and damping in [Co/Pd]8 multilayers with variable Co layer thickness , 2011, 1106.4491.

[22]  R. O'handley.  Modern magnetic materials , 1999 .

[23]  H. Ohno,et al.  Tunnel magnetoresistance of 604% at 300K by suppression of Ta diffusion in CoFeB∕MgO∕CoFeB pseudo-spin-valves annealed at high temperature , 2008 .

[24]  J. Katine,et al.  Current-induced magnetization reversal in nanopillars with perpendicular anisotropy , 2006 .

[25]  Jian-Ping Wang,et al.  Low resistance spin-dependent magnetic tunnel junction with high breakdown voltage for current-induced-magnetization-switching devices , 2005 .

[26]  T. Ito,et al.  Electric field effects on magnetocrystalline anisotropy in ferromagnetic Fe monolayers , 2010 .

[27]  M. Nakayama,et al.  Spin transfer switching in TbCoFe∕CoFeB∕MgO∕CoFeB∕TbCoFe magnetic tunnel junctions with perpendicular magnetic anisotropy , 2008 .

[28]  Y. K. Kim,et al.  Switching characteristics of submicrometer magnetic tunnel junction devices with perpendicular anisotropy , 2005 .

[29]  H. Ohno,et al.  A perpendicular-anisotropy CoFeB-MgO magnetic tunnel junction. , 2010, Nature materials.