Comparison of Neutron Diffraction Measurements of Residual Stress of Steel Butt Welds With Current Fitness-for-Purpose Assessments

In this research, the neutron diffraction technique was used to investigate the residual stress distributions in constrained carbon steel welds. Two full penetration welds were studied using (a) the stringer bead and (b) the temper bead weld techniques in 25 mm thick plate. The welds were not post-weld heat treated. The focus of the measurements is on the values of the subsurface and through-thickness strain/stress variation near the middle of the weld and the toe. The experimental results showed that both processes had high residual stresses particularly through the thickness. The measurements were compared with current fitness-for-purpose approaches, such as BS7910 and R6. It was found that the residual stress distribution in the temper bead welded specimen was not as favorable as suspected and post-weld heat treatment should be recommended to reduce residual tensile stresses in this type of steel welds.

[1]  J. I. Ghojel,et al.  Eliminating post-weld heat treatment in repair welding by temper bead technique: role bead sequence in metallurgical changes , 2004 .

[2]  Pingsha Dong,et al.  Residual Stress Analyses of a Multi-Pass Girth Weld: 3-D Special Shell Versus Axisymmetric Models , 2001 .

[3]  C. Windsor,et al.  Study of residual stress in a ferritic steel electron beam test weldment using neutron diffraction , 1995 .

[4]  Y. Zhu,et al.  An Overview of Some Current Research on Welding Residual Stresses and Distortion in the U.S. Navy , 1997 .

[5]  M. J. Jirinec,et al.  Experimental determination of the residual stresses in a spiral weld overlay tube , 1997 .

[6]  Robert A. Ainsworth,et al.  Assessment of the integrity of structures containing defects , 1987 .

[7]  Philip J. Withers,et al.  The Appropriateness of Residual Stress Length Scales in Structural Integrity , 2004 .

[8]  L. Edwards,et al.  Measurement of the residual stresses near a short 20° repair in a 19 mm thick stainless steel pipe girth weld , 2001 .

[9]  Youtsos Anastasius.  International Technical Specification for Non Destructive Testing-Standards Test Method for Determining Residual Stresses by Neutron Diffraction-CEN ISO/TS 21432:2005 , 2005 .

[10]  Philip J. Withers,et al.  Neutron and synchrotron measurements of residual strain in TIG welded aluminium alloy 2024 , 2003 .

[11]  John W. H. Price,et al.  Potential guidelines for design and fitness for purpose for carbon steel components subject to repeated thermal shock , 2004 .

[12]  P. Withers,et al.  Residual stress relief in MAG welded joints of dissimilar steels , 2003 .

[13]  A. Steuwer,et al.  Investigation of reference samples for residual strain measurements in a welded specimen by neutron and synchrotron X-ray diffraction , 2006 .

[14]  P. J. Webster,et al.  Neutron strain scanning of a small welded austenitic stainless steel plate , 1995 .

[15]  David Gandy,et al.  Weld Repair of Steam Turbine Casings and Piping—An Industry Survey , 2001 .

[16]  P. Withers,et al.  Residual stress. Part 1 – Measurement techniques , 2001 .

[17]  Michael E. Fitzpatrick,et al.  Direct measurement of the residual stresses near a ‘boat-shaped’ repair in a 20 mm thick stainless steel tube butt weld , 2005 .

[18]  D. Kwon,et al.  Assessing welding residual stress in A335 P12 steel welds before and after stress-relaxation annealing through instrumented indentation technique , 2003 .

[19]  W. Reimers,et al.  Comparative neutron and X-ray residual stress measurements on Al-2219 welded plate , 1997 .

[20]  Marc Duquennoy,et al.  Ultrasonic characterization of residual stresses in steel rods using a laser line source and piezoelectric transducers , 2001 .

[21]  J. Price,et al.  Neutron Diffraction Evaluation of Residual Stress for Several Welding Arrangements and Comparison With Fitness-for-Purpose Assessments , 2008 .

[22]  D. Smith,et al.  Residual Stress Distributions in Welded Ferritic Steel T-plate Joints , 2003 .

[23]  Xiaohua H. Cheng,et al.  Residual stress modification by post-weld treatment and its beneficial effect on fatigue strength of welded structures , 2003 .

[24]  H. Bhadeshia,et al.  Residual stress. Part 2 – Nature and origins , 2001 .

[25]  H. Bhadeshia,et al.  The Effects of Filler Metal Transformation Temperature on Residual Stresses in a High Strength Steel Weld , 2009 .

[26]  John W. H. Price,et al.  Comparison of experimental and theoretical residual stresses in welds: The issue of gauge volume , 2008 .