Crack growth analysis at adhesive–adherent interface in bonded joints under mixed mode I/II

The propagation of an interface crack subjected to mixed mode I/II was investigated for two 2024-T351 aluminum thin layers joined by means of DP760 epoxy adhesive produced by 3M©. On the basis of beam theory, an analytical expression for computing the energy release rate is presented for the mixed-mode end loaded split (MMELS) test. The analytical strain energy release rate was compared by finite element (FE) analysis using the virtual crack closure technique (VCCT). Several fatigue crack growth tests were carried out in a plane bending machine to compare the experimental energy release rates to those of the analytical and FE solutions. Experimental results showed the relationship between the delamination modality and initial crack length rather than the applied load. The crack growth behavior showed stable crack growth followed by rapid propagation at the interface with the adhesive layer.

[1]  T. K. Hellen.  On the method of virtual crack extensions , 1975 .

[2]  Jan K. Spelt,et al.  Mixed-mode fracture characterization of adhesive joints , 1994 .

[3]  M. Crisfield,et al.  Analytical derivation of load/displacement relationship for the DCB and MMB and proof of the FEA formulation , 1996 .

[4]  Anthony J. Kinloch,et al.  The analysis of interlaminar fracture in uniaxial fibre-polymer composites , 1990, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[5]  N. Blanco,et al.  Analysis of the mixed-mode end load split delamination test , 2006 .

[6]  A. Pasta,et al.  An analysis of interface delamination mechanisms in orthotropic and hybrid fiber-metal composite laminates , 2007 .

[7]  M. Kanninen,et al.  A finite element calculation of stress intensity factors by a modified crack closure integral , 1977 .

[8]  J. G. Williams,et al.  The mixed-mode delamination of fibre composite materials , 1993 .

[9]  Zhigang Suo,et al.  The role of material orthotropy in fracture specimens for composites , 1992 .

[10]  Z. Suo,et al.  Mixed mode cracking in layered materials , 1991 .

[11]  Gianni Nicoletto,et al.  Mixed Mode I/II fatigue crack growth in adhesive joints , 2006 .

[12]  Ronald Krueger,et al.  The Virtual Crack Closure Technique : History , Approach and Applications , 2002 .

[13]  Amar C. Garg,et al.  Delamination—a damage mode in composite structures , 1988 .

[14]  D. Broek.  The practical use of fracture mechanics , 1988 .

[15]  J. G. Williams,et al.  On the calculation of energy release rates for cracked laminates , 1988 .