Micro-structural, electron-spectroscopic and field-emission studies of carbon nitride nanotubes grown from cage-like and linear carbon sources

Abstract Using conventional chemical vapor deposition at 800 °C at atmospheric pressure, N-doped carbon nanotubes (CNTs) were grown from two precursors: (i) from a cage-like carbon source: camphor, using dimethylformamide (DMF) as a nitrogen source; and (ii) from a linear-chain aminohydrocarbon: octadecylamine, as a dual source of carbon and nitrogen. The study suggests that the molecular structure of the precursor plays an important role in governing the structural properties of the resulting nanotubes. Although the nanotubes have bamboo-like structure in either case, electron-microscopy reveals remarkable differences in their microstructure. While camphor–DMF-grown carbon nanotubes (CD-CNTs) have corrugated outer walls and rounded tips, the octadecylamine-grown ones (OD-CNTs) are straight and have tapered tips. Quantitative as well as qualitative determination of nitrogen level is done based on XPS and EELS analyses, assigning different nitrogen moieties (pyridinic, pyrrolinic and graphitic-substitute) in the CNT-body and tip regions. Relative to CD-CNTs, the OD-CNTs have higher crystallinity, higher thermal stability and higher specific surface area, as determined by micro-Raman, TGA and BET analyses, respectively. The field emission properties of CD-CNTs are typically good, while those of OD-CNTs are better. These behavioral differences are explained in terms of the growth chemistry as well as the role of different nitrogen moieties in the CNT matrix.

[1]  C N R Rao,et al.  Nitrogen- and boron-doped double-walled carbon nanotubes. , 2007, ACS nano.

[2]  Mukul Kumar,et al.  Gigas Growth of Carbon Nanotubes , 2008 .

[3]  Y. Bando,et al.  Structure and nitrogen incorporation of carbon nanotubes synthesized by catalytic pyrolysis of dimethylformamide , 2004 .

[4]  Yoshinori Ando,et al.  Pentagons, heptagons and negative curvature in graphite microtubule growth , 1992, Nature.

[5]  L. Forró,et al.  Field emission from carbon nanotubes: perspectives for applications and clues to the emission mechanism , 1999 .

[6]  T. Ichihashi,et al.  Distribution of pentagons and shapes in carbon nano-tubes and nano-particles , 1993 .

[7]  C. Jin,et al.  Quantitative analysis of electron field-emission characteristics of individual carbon nanotubes: the importance of the tip structure. , 2006, The journal of physical chemistry. B.

[8]  Quan-hong Yang,et al.  Dual Raman features of double coaxial carbon nanotubes with N-doped and B-doped multiwalls. , 2005, Nano letters.

[9]  Tadashi Sato,et al.  Pyrolysis of organic compounds—II , 1967 .

[10]  Jeunghee Park,et al.  Experimental and theoretical studies on the structure of N-doped carbon nanotubes: Possibility of intercalated molecular N2 , 2004 .

[11]  Identification of electron donor states in N-doped carbon nanotubes , 2000, cond-mat/0011318.

[12]  S. Hong,et al.  Tailored field-emission property of patterned carbon nitride nanotubes by a selective doping of substitutional N(sN) and pyridine-like N(pN) atoms , 2007 .

[13]  Guohua Wu,et al.  Evidence for the existence of nitrogen-substituted graphite structure by polarization dependence of near-edge x-ray-absorption fine structure , 2000 .

[14]  Jeunghee Park,et al.  Investigation of field emission and photoemission properties of high-purity single-walled carbon nanotubes synthesized by hydrogen arc discharge. , 2006, The journal of physical chemistry. B.

[15]  Jeunghee Park,et al.  Release of N(2) from the carbon nanotubes via high-temperature annealing. , 2005, The journal of physical chemistry. B.

[16]  F. Illas,et al.  Origin of the Large N 1s Binding Energy in X-ray Photoelectron Spectra of Calcined Carbonaceous Materials , 1996 .

[17]  Mukul Kumar,et al.  The use of camphor-grown carbon nanotube array as an efficient field emitter , 2007 .

[18]  Daoben Zhu,et al.  Controllable Growth, Structure, and Low Field Emission of Well-Aligned CNx Nanotubes , 2002 .

[19]  T. Pichler,et al.  Tailoring N-Doped Single and Double Wall Carbon Nanotubes from a Nondiluted Carbon/Nitrogen Feedstock , 2007 .

[20]  Gang Zhang,et al.  Effect of substitutional atoms in the tip on field-emission properties of capped carbon nanotubes , 2002 .

[21]  R. Czerw,et al.  N-doping and coalescence of carbon nanotubes: synthesis and electronic properties , 2002 .

[22]  Yoshinori Ando,et al.  Field emission from camphor–pyrolyzed carbon nanotubes , 2004 .

[23]  P. Sánchez,et al.  Growth of Carbon Nanofibers from Ni/Y Zeolite Based Catalysts: Effects of Ni Introduction Method, Reaction Temperature, and Reaction Gas Composition , 2005 .

[24]  Y. Bando,et al.  Synthesis and field emission of carbon nanotubular fibers doped with high nitrogen content. , 2003, Chemical communications.

[25]  Quan-hong Yang,et al.  The template synthesis of double coaxial carbon nanotubes with nitrogen-doped and boron-doped multiwalls. , 2005, Journal of the American Chemical Society.

[26]  R. McCreery,et al.  Raman Spectroscopy of Carbon Materials: Structural Basis of Observed Spectra , 1990 .

[27]  K. Jiang,et al.  Vacuum-Breakdown-Induced Needle-Shaped Ends of Multiwalled Carbon Nanotube Yarns and Their Field Emission Applications , 2007 .

[28]  B. Sumpter,et al.  Nitrogen-mediated carbon nanotube growth: diameter reduction, metallicity, bundle dispersability, and bamboo-like structure formation. , 2007, ACS nano.

[29]  A. Govindaraj,et al.  Field emission properties of boron and nitrogen doped carbon nanotubes , 2006 .

[30]  Chang Liu,et al.  Synthesis and characterization of double-walled carbon nanotubes from multi-walled carbon nanotubes by hydrogen-arc discharge , 2005 .

[31]  P. Bernier,et al.  Synthesis of N-doped SWNT using the arc-discharge procedure , 2004 .

[32]  Quan-hong Yang,et al.  Adsorption and capillarity of nitrogen in aggregated multi-walled carbon nanotubes , 2001 .

[33]  Ajayan,et al.  Curvature-induced bonding changes in carbon nanotubes investigated by electron energy-loss spectrometry. , 1996, Physical review. B, Condensed matter.

[34]  Vikram Kumar,et al.  Enhanced field emission characteristics of nitrogen-doped carbon nanotube films grown by microwave plasma enhanced chemical vapor deposition process , 2006 .

[35]  M. Kaiser,et al.  Electron emission from individual nitrogen-doped multi-walled carbon nanotubes , 2004 .

[36]  C. Park,et al.  Fabrication of flexible carbon nanotube field emitter arrays by direct microwave irradiation on organic polymer substrate. , 2005, Journal of the American Chemical Society.

[37]  Daoben Zhu,et al.  Bamboo-like carbon nanotubes produced by pyrolysis of iron(II) phthalocyanine , 2001 .

[38]  X. Bai,et al.  Multiwall boron carbonitride/carbon nanotube junction and its rectification behavior. , 2007, Journal of the American Chemical Society.

[39]  Yoshinori Ando,et al.  Single-wall and multi-wall carbon nanotubes from camphor—a botanical hydrocarbon , 2003 .

[40]  R. Kaltofen,et al.  Influence of the Catalyst Hydrogen Pretreatment on the Growth of Vertically Aligned Nitrogen-Doped Carbon Nanotubes , 2007 .