Development of Thin Film Amorphous Silicon Tandem Junction Based Photocathodes Providing High Open-Circuit Voltages for Hydrogen Production

Hydrogenated amorphous silicon thin film tandem solar cells (a-Si:H/a-Si:H) have been developed with focus on high open-circuit voltages for the direct application as photocathodes in photoelectrochemical water splitting devices. By temperature variation during deposition of the intrinsic a-Si:H absorber layers the band gap energy of a-Si:H absorber layers, correlating with the hydrogen content of the material, can be adjusted and combined in a way that a-Si:H/a-Si:H tandem solar cells provide open-circuit voltages up to 1.87 V. The applicability of the tandem solar cells as photocathodes was investigated in a photoelectrochemical cell (PEC) measurement set-up. With platinum as a catalyst, the a-Si:H/a-Si:H based photocathodes exhibit a high photocurrent onset potential of 1.76 V versus the reversible hydrogen electrode (RHE) and a photocurrent of 5.3 mA/cm2 at 0 V versus RHE (under halogen lamp illumination). Our results provide evidence that a direct application of thin film silicon based photocathodes fulfills the main thermodynamic requirements to generate hydrogen. Furthermore, the presented approach may provide an efficient and low-cost route to solar hydrogen production.

[1]  D. Nocera,et al.  Wireless Solar Water Splitting Using Silicon-Based Semiconductors and Earth-Abundant Catalysts , 2011, Science.

[2]  Nathan S. Lewis,et al.  Evaluation of Pt, Ni, and Ni–Mo electrocatalysts for hydrogen evolution on crystalline Si electrodes , 2011 .

[3]  William E. McMahon,et al.  Fill factor as a probe of current‐matching for GaInP2/GaAs tandem cells in a concentrator system during outdoor operation , 2008 .

[4]  Igor Levin,et al.  H2 evolution at Si-based metal-insulator-semiconductor photoelectrodes enhanced by inversion channel charge collection and H spillover. , 2013, Nature materials.

[5]  W. Beyer,et al.  The role of hydrogen in a-Si:H — results of evolution and annealing studies , 1983 .

[6]  S. Sugahara,et al.  Photoelectrochemical hydrogen evolution using amorphous silicon electrodes having p-i-n or p-i-n-p-i-n junctions , 1986 .

[7]  S. Sugahara,et al.  Photoelectrochemical water splitting by tandem type and heterojunction amorphous silicon electrodes , 1988 .

[8]  Arvind Shah,et al.  Thin-Film Silicon Solar Cells , 2010 .

[9]  S. Tsuda,et al.  High absorption-coefficient and stable a-Si for high-efficiency solar cells , 1990, IEEE Conference on Photovoltaic Specialists.

[10]  Arthur J. Nozik,et al.  Photoelectrochemistry: Applications to Solar Energy Conversion , 1978 .

[11]  B. Rech,et al.  Potential of amorphous silicon for solar cells , 1999 .

[12]  Subhendu Guha,et al.  Enhancement of open circuit voltage in high efficiency amorphous silicon alloy solar cells , 1986 .

[13]  Jae Sung Lee,et al.  Single-crystalline, wormlike hematite photoanodes for efficient solar water splitting , 2013, Scientific Reports.

[14]  W. Jaegermann,et al.  Preparation and Characterization of GaP Semiconductor Electrodes for Photoelectrochemical Water Splitting , 2012 .

[15]  V. Smirnov,et al.  Variation in Absorber Layer Defect Density in Amorphous and Microcrystalline Silicon Thin Film Solar Cells with 2 MeV Electron Bombardment , 2012 .

[16]  Vincent Laporte,et al.  Highly active oxide photocathode for photoelectrochemical water reduction. , 2011, Nature materials.

[17]  M. Vaněček,et al.  How to reach more precise interpretation of subgap absorption spectra in terms of deep defect density in a-Si:H , 1991 .

[18]  Ahm Arno Smets,et al.  Relation of the Si-H stretching frequency to the nanostructural Si-H bulk environment , 2007 .

[19]  N. Lewis,et al.  Powering the planet: Chemical challenges in solar energy utilization , 2006, Proceedings of the National Academy of Sciences.

[20]  Michael Grätzel,et al.  Photoelectrochemical Hydrogen Production , 2012 .

[21]  Christophe Ballif,et al.  Amorphous Si thin film based photocathodes with high photovoltage for efficient hydrogen production. , 2013, Nano letters.

[22]  D. Staebler,et al.  Reversible conductivity changes in discharge‐produced amorphous Si , 1977 .

[23]  L. Ley.  Photoemission and optical properties , 1984 .

[24]  Miro Zeman,et al.  Efficient solar water splitting by enhanced charge separation in a bismuth vanadate-silicon tandem photoelectrode , 2013, Nature Communications.

[25]  James R. Bolton,et al.  Limiting and realizable efficiencies of solar photolysis of water , 1985, Nature.

[26]  A. Matsuda,et al.  Importance of surface processes in defect formation in a-Si:H , 1993 .

[27]  Eric L. Miller,et al.  A hybrid multijunction photoelectrode for hydrogen production fabricated with amorphous silicon/germanium and iron oxide thin films , 2004 .

[28]  B. Hong,et al.  N-doped monolayer graphene catalyst on silicon photocathode for hydrogen production , 2013 .

[29]  J. Holdren,et al.  Energy and Sustainability , 2007, Science.

[30]  M. Zeman,et al.  Optimization of amorphous silicon double junction solar cells for an efficient photoelectrochemical water splitting device based on a bismuth vanadate photoanode. , 2014, Physical chemistry chemical physics : PCCP.

[31]  Turner,et al.  A monolithic photovoltaic-photoelectrochemical device for hydrogen production via water splitting , 1998, Science.

[32]  G. Hodes.  Photoelectrochemical Cell Measurements: Getting the Basics Right. , 2012, The journal of physical chemistry letters.

[33]  Adam Heller,et al.  Efficient Solar to Chemical Conversion: 12% Efficient Photoassisted Electrolysis in the [ p -type InP(Ru)]/HCl-KCl/Pt(Rh) Cell , 1981 .

[34]  M. F. Weber,et al.  Splitting water with semiconducting photoelectrodes—Efficiency considerations , 1986 .

[35]  D. Carlson,et al.  AMORPHOUS SILICON SOLAR CELL , 1976 .

[36]  Etienne Goovaerts,et al.  Conference Record of the Twenty-Eighth IEEE Photovoltaic Specialists Conference, 2000 , 2000 .

[37]  Ahm Arno Smets,et al.  Vacancies and voids in hydrogenated amorphous silicon , 2003 .

[38]  V. Smirnov,et al.  Performance of p- and n-side illuminated microcrystalline silicon solar cells following 2 MeV electron bombardment , 2012 .

[39]  James R. McKone,et al.  Solar water splitting cells. , 2010, Chemical reviews.

[40]  J. Turner,et al.  III-V nitride epilayers for photoelectrochemical water splitting: GaPN and GaAsPN. , 2006, The journal of physical chemistry. B.

[41]  V. Smirnov,et al.  p- and n-type microcrystalline silicon oxide (μc-SiOx:H) for applications in thin film silicon tandem solar cells1 , 2014 .