Evaluation Method and Mitigation Strategies for Shrinkage Cracking of Modern Concrete

Abstract The complex compositions and large shrinkage of concrete, as well as the strong constraints of the structures, often lead to prominent shrinkage cracking problems in modern concrete structures. This paper first introduces a multi-field (hydro–thermo–hygro–constraint) coupling model with the hydration degree of cementitious materials as the basic state parameter to estimate the shrinkage cracking risk of hardening concrete under coupling effects. Second, three new key technologies are illustrated: temperature rise inhibition, full-stage shrinkage compensation, and shrinkage reduction technologies. These technologies can efficiently reduce the thermal, autogenous, and drying shrinkages of concrete. Thereafter, a design process based on the theoretical model and key technologies is proposed to control the cracking risk index below the threshold value. Finally, two engineering application examples are provided that demonstrate that concrete shrinkage cracking can be significantly mitigated by adopting the proposed methods and technologies.

[1]  Zdenek P. Bazant,et al.  Solidification theory for concrete creep. I: formulation , 1989 .

[2]  Pietro Lura,et al.  On the mechanism of plastic shrinkage cracking in fresh cementitious materials , 2019, Cement and Concrete Research.

[3]  Edward J. Garboczi,et al.  Modelling drying shrinkage in reconstructed porous materials: application to porous Vycor glass , 1998 .

[4]  Jun Zhang,et al.  Micromechanical modeling on autogenous and drying shrinkages of concrete , 2012 .

[5]  Yu Yan,et al.  Effect of a novel starch-based temperature rise inhibitor on cement hydration and microstructure development , 2020 .

[6]  Surendra P. Shah,et al.  Permeability study of cracked concrete , 1997 .

[7]  M. Wyrzykowski,et al.  Effect of relative humidity decrease due to self-desiccation on the hydration kinetics of cement , 2016 .

[8]  Lutz Franke,et al.  Influence of the age and drying process on pore structure and sorption isotherms of hardened cement paste , 2006 .

[9]  Jiaping Liu,et al.  Impact of Temperature Rising Inhibitor on hydration kinetics of cement paste and its mechanism , 2018, Cement and Concrete Composites.

[10]  Karen L. Scrivener,et al.  The origin of early age expansions induced in cementitious materials containing shrinkage reducing admixtures , 2011 .

[11]  P. K. Mehta,et al.  Concrete Technology at the Crossroads--Problems and Opportunities , 1994, "SP-144: Concrete Technology: Past, Present, and Future".

[12]  Bernhard A. Schrefler,et al.  Hygro‐thermo‐chemo‐mechanical modelling of concrete at early ages and beyond. Part II: shrinkage and creep of concrete , 2006 .

[13]  M. Wyrzykowski,et al.  A poromechanics model for plastic shrinkage of fresh cementitious materials , 2018, Cement and Concrete Research.

[14]  Robert Otto Rasmussen,et al.  CONCRETE TEMPERATURE MODELING AND STRENGTH PREDICTION USING MATURITY CONCEPTS IN THE FHWA HIPERPAV SOFTWARE , 2001 .

[15]  Farid Benboudjema,et al.  Modeling basic creep in concrete at early-age under compressive and tensile loading , 2014 .

[16]  Jiaping Liu,et al.  Deformation and cracking modeling for early-age sidewall concrete based on the multi-field coupling mechanism , 2015 .

[17]  Miguel Cervera,et al.  THERMO-CHEMO-MECHANICAL MODEL FOR CONCRETE. I: HYDRATION AND AGING , 1999 .

[18]  G. Sant.  Examining time-zero and early age expansion in pastes containing shrinkage reducing admixtures (SRAs) , 2006 .

[19]  D. Bentz,et al.  Standard Test Method for Autogenous Strain of Cement Paste and Mortar , 2007 .

[20]  Zhangli Hu,et al.  Visco-elastic behavior of blended cement pastes at early ages , 2020 .

[21]  Anton K. Schindler,et al.  Effect of Temperature on Hydration of Cementitious Materials , 2004 .

[22]  Jiaping Liu,et al.  Starch-Assisted Synthesis and Characterization of Layered Calcium Hydroxide Particles , 2018, Journal of Inorganic and Organometallic Polymers and Materials.

[23]  Walter L. Smith.  Probability and Statistics , 1959, Nature.

[24]  Bei Huang,et al.  Combined effects of biochar and MgO expansive additive on the autogenous shrinkage, internal relative humidity and compressive strength of cement pastes , 2019 .

[25]  Gaurav Sant,et al.  Interactions between shrinkage reducing admixtures (SRA) and cement paste's pore solution , 2008 .

[26]  J.,et al.  Nonlinear water diffusion In nonsaturated concrete , 2022 .

[27]  Luc Taerwe,et al.  Degree of hydration-based description of mechanical properties of early age concrete , 1996 .

[28]  M. Wyrzykowski,et al.  Evaluation of the ultimate drying shrinkage of cement-based mortars with poroelastic models , 2016, Materials and Structures.

[29]  R. W. Burrows,et al.  Building Durable Structures in the 21st Century , 2001 .

[30]  Jiaping Liu,et al.  Temperature sensitivity of MgO expansive agent and its application in temperature crack mitigation in shiplock mass concrete , 2018 .

[31]  P. Lura,et al.  Properties of early-age concrete relevant to cracking in massive concrete , 2019, Cement and Concrete Research.

[32]  Bernhard A. Schrefler,et al.  Hygro‐thermo‐chemo‐mechanical modelling of concrete at early ages and beyond. Part I: hydration and hygro‐thermal phenomena , 2006 .

[33]  Pan Feng,et al.  Effects of novel polymer-type shrinkage-reducing admixture on early age autogenous deformation of cement pastes , 2017 .

[34]  Hyo-Gyoung Kwak,et al.  Experimental and Numerical Quantification of Plastic Settlement in Fresh Cementitious Systems , 2010 .

[35]  Modelling Moisture Transport Processes in Cement Paste Systems , 2004 .

[36]  P. Lura,et al.  Shrinkage and creep of SCC – The influence of paste volume and binder composition , 2011 .

[37]  Han-seung Lee,et al.  Heat of hydration models of cementitious materials , 2012 .

[38]  G. D. Schutter.  Degree of hydration based Kelvin model for the basic creep of early age concrete , 1999 .

[39]  K. Breugel,et al.  Autogenous shrinkage in high-performance cement paste: An evaluation of basic mechanisms , 2003 .