Energy deposition at front and rear surfaces during picosecond laser interaction with fused silica

The difference between front-surface and rear-surface energy deposition of a 35 ps laser pulse (λ=1064 nm) in fused silica was investigated using shadowgraphic and laser-deflection techniques. Shock waves were observed in the glass and in air. Shock waves generated in air at the front surface are stronger than at the rear surface. Less than 35% of the energy incident on the surface drives the air shock waves at the rear surface. Up to 90% of the incident energy drives the air shock waves at the front surface. Laser-plasma interaction is responsible for this difference and for limiting the amount of energy deposited inside the sample during front-surface ablation. Energy deposition at the rear surface is mostly limited by self-focusing inside the material.

[1]  Alberto Salleo,et al.  Machining of transparent materials using an IR and UV nanosecond pulsed laser , 2000 .

[2]  D. R. Ermer,et al.  Laser induced electron and sodium ion emission from single crystal NaNO3 at 1064 nm , 2000 .

[3]  Dynamics of an air breakdown plasma on a solid surface during picosecond laser ablation , 2000 .

[4]  B. Hopp,et al.  Time-resolved shock-wave photography above 193-nm excimer laser-ablated graphite surface , 1999 .

[5]  Francois Y. Genin,et al.  Crack propagation in fused silica during UV and IR nanosecond-laser illumination , 1999, Laser Damage.

[6]  R. Haglund,et al.  Planar and spherical shock wave generation during infrared laser ablation of calcium carbonate , 1998 .

[7]  Shock-wave generation during rear- and front-side ablation of calcite , 1997 .

[8]  Ernst-Wolfgang Kreutz,et al.  The applicability of the Sedov - Taylor scaling during material removal of metals and oxide layers with pulsed and excimer laser radiation , 1997 .

[9]  S. C. Langford,et al.  The role of defects in the rear side laser ablation of MgO at 308 nm , 1996 .

[10]  S. C. Langford,et al.  The role of defects in laser induced positive ion emission from ionic crystals , 1996 .

[11]  Peter Berger,et al.  Time-resolved observation of gas-dynamic discontinuities arising during excimer laser ablation and their interpretation , 1995 .

[12]  Perry,et al.  Laser-induced damage in dielectrics with nanosecond to subpicosecond pulses. , 1995, Physical review letters.

[13]  C. E. Otis,et al.  On the debris phenomenon with laser-sputtered polymers , 1992 .

[14]  P. Simon,et al.  Nanosecond and femtosecond excimer laser ablation of fused silica , 1992 .

[15]  M. Allmen,et al.  Laser-beam interactions with materials : physical principles and applications , 1987 .

[16]  S. P. Gill,et al.  Physics of Shock Waves and High-Temperature Hydrodynamic Phenomena , 2002 .

[17]  J. Cole,et al.  Similarity and Dimensional Methods in Mechanics , 1960 .