The Effect of NCO-Polyol on the Properties of Low-Density Polyethylene/Water Hyacinth Fiber (Eichhornia crassiper) Composites

Low density polyethylene (LDPE)/modified water hyacinth fiber (WHF) composites have been prepared by melt blending. All the composites were characterized by tensile test, differential scanning calorimetry (DSC), water absorption behaviour, thermogravimetric analysis (TGA) and scanning electron microscopy (SEM). The results indicated that LDPE/WHF composites with NCO-polyol as a coupling agent show higher values of tensile strength, Young's modulus and water absorption resistance but lower elongation at break than LDPE/WHF composites without NCO-polyol. The micrographs of SEM showed that the WHF were more widely dispersed in the LDPE matrix with the addition of the NCO-polyol as a coupling agent. It was also found that the modified WHF offers better thermal stability in the LDPE/WHF composites than unmodified WHF.

[1]  S. Pang,et al.  Dimensional stability and mechanical behaviour of wood–plastic composites based on recycled and virgin high-density polyethylene (HDPE) , 2008 .

[2]  R. Scaffaro,et al.  Effect of adding wood flour to the physical properties of a biodegradable polymer , 2008 .

[3]  M. Yoshida,et al.  Morphological and thermal analyses of flexible polyurethane foams containing commercial calcium carbonate , 2008 .

[4]  Hsu-Chiang Kuan,et al.  Mechanical, thermal and morphological properties of water-crosslinked wood flour reinforced linear low-density polyethylene composites , 2006 .

[5]  Adriaan S. Luyt,et al.  Thermal, mechanical and electrical properties of copper powder filled low-density and linear low-density polyethylene composites , 2006 .

[6]  P. Herrera-Franco,et al.  A study of the mechanical properties of short natural-fiber reinforced composites , 2005 .

[7]  L. Matuana,et al.  Properties of wood plastic composites made of recycled HDPE and wood flour from CCA-treated wood removed from service , 2004 .

[8]  H. Ismail,et al.  Bamboo fibre filled natural rubber composites: the effects of filler loading and bonding agent , 2002 .

[9]  Hanafi Ismail,et al.  The effects of a silane coupling agent on curing characteristics and mechanical properties of bamboo fibre filled natural rubber composites , 2002 .

[10]  Sabu Thomas,et al.  Effects of environment on the properties of low-density polyethylene composites reinforced with pineapple-leaf fibre , 1998 .

[11]  H. Ismail,et al.  Curing characteristics and mechanical properties of short oil palm fibre reinforced rubber composites , 1997 .

[12]  P. Flodin,et al.  Surface modification of cellulose fibers. III: Durability of cellulose-polyester composites under environmental aging , 1986 .