论文信息 - Preparation and Magnetic Properties of Nanocrystal Bulk SmCo7 Magnets

Preparation and Magnetic Properties of Nanocrystal Bulk SmCo7 Magnets

Two kinds of 2:17R Sm-Co alloys, Sm2(Fe,Cu,Zr,Co)17 and pure binary Sm2Co17 were prepared, and the amorphous powder was prepared by high-energy ball milling Sm-Co alloys. The bulk nanocrystalline SmCo7 was prepared by hot-pressing the amorphous powder, and the magnetic properties and phase composition were studied. Initial Sm2(Fe,Cu,Zr,Co)17 showed a large value of coercivity while the pure Sm2Co17 almost showed no coercivity. However, after ball milling the grain size of alloys decreased dramatically until completely amorphous. Two kinds of alloys showed the different phase composition and magnetic properties after hot-pressing. It was found that the pure Sm2Co17 bulk magnet showed a high coercivity Hc and had the 1:7H phase. On the other hand, the Sm2(Fe,Cu,Zr,Co)17 showed high saturation magnetization Ms and very low Hc since the Fe-Co and Sm2Co3 phase were precipitated from the alloy.

Q. Shen | Yilong Ma | Jun Dong | Dengming Chen

[1] Nianduan Lu,et al. Abnormal crystal structure stability of nanocrystalline Sm2Co17 permanent magnet , 2009 .

[2] Huaiwu Zhang,et al. Rare earth permanent magnets Sm2(Co, Fe, Cu, Zr)17 for high temperature applications , 2008 .

[3] Jiang Shen,et al. Atomistic simulation for disordered rare-earth compounds SmCo7 and Sm(Co,Ti)7 , 2006 .

[4] L. Schultz,et al. Stability of magnetic properties of Sm/sub 2/Co/sub 17/-type magnets at operating temperatures higher than 400/spl deg/C , 2003 .

[5] Werner Scholz,et al. TEM-analysis of Sm(Co,Fe,Cu,Zr)z magnets for high-temperature applications , 2002 .

[6] Ralph Skomski,et al. Sm–Co–Cu–Ti high-temperature permanent magnets , 2000 .

[7] G. Hadjipanayis,et al. Magnetic properties and microstructure of mechanically milled Sm2(Co,M)17-based powders with M=Zr, Hf, Nb, V, Ti, Cr, Cu and Fe , 2000 .

[8] D. Dimitrov,et al. Microstructure and high temperature magnetic properties of Sm(Co, Cu, Fe, Zr)z (z=6.7–9.1) permanent magnets , 1999 .

[9] Y. Kimura,et al. Phase transformation at high temperature and coercivity of Sm(Co,Cu,Fe,Zr)7-9 magnet alloys , 1987 .

[10] R. K. Mishra,et al. Microstructure and properties of step aged rare earth alloy magnets , 1981 .

[11] Teruhiko Ojima,et al. Magnetic properties of a new type of rare-earth cobalt magnets Sm 2 (Co, Cu, Fe, M) 17 , 1977 .

[12] T. Ojima,et al. New Type Rare Earth Cobalt Magnets with an Energy Product of 30 MG·Oe , 1977 .